Abstract Boron nitride nanotubes (BNNT) uniformly dispersed in stretchable materials, such as poly(dimethylsiloxane) (PDMS), could create the next generation of composites with augmented mechanical, thermal, and piezoelectric characteristics. This work reports tunable piezoelectricity of multifunctional BNNT/PDMS stretchable composites prepared via co‐solvent blending with tetrahydrofuran (THF) to disperse BNNTs in PDMS while avoiding sonication or functionalization. The resultant stretchable BNNT/PDMS composites demonstrate augmented Young's modulus (200% increase at 9 wt% BNNT) and thermal conductivity (120% increase at 9 wt% BNNT) without losing stretchability. Furthermore, BNNT/PDMS composites demonstrate piezoelectric responses that are linearly proportional to BNNT wt%, achieving a piezoelectric constant (|d33|) of 18 pmV−1at 9 wt% BNNT without poling, which is competitive with commercial piezoelectric polymers. Uniquely, BNNT/PDMS accommodates tensile strains up to 60% without plastic deformation by aligning BNNTs, which enhances the composites’ piezoelectric response approximately five times. Finally, the combined stretchable and piezoelectric nature of the composite was exploited to produce a vibration sensor sensitive to low‐frequency (≈1 kHz) excitation. This is the first demonstration of multifunctional, stretchable BNNT/PDMS composites with enhanced mechanical strength and thermal conductivity and furthermore tunable piezoelectric response by varying BNNT wt% and applied strain, permitting applications in soft actuators and vibration sensors.
more »
« less
Using a conductive sphere as a probe to characterize the sensitivity of soft piezoresistive films
Abstract Flexible piezoresistive films, such as, carbon black/polydimethylsiloxane (C‐PDMS) composites, are often used as skin analogs and integrated into complex array sensors for tactile sensing. The uniformity of the sensor characteristics heavily depends on the homogeneity of the composite. Therefore, the ability to locally characterize a film that will be integrated into a complex force sensor could be critical. Here, a method to characterize the local sensitivity of flexible piezoresistive films is presented. Using a conductive sphere, which was chosen over a flat probe to eliminate misalignment issues, the surface of a thin film composite is indented to characterize the change in resistivity in terms of average strain. Experiments were performed with 15 and 18 wt% carbon black C‐PDMS films of varying thickness. The contact radius of the probe with the piezoresistive film was estimated using the Johnson‐Roberts‐Kendall contact theory. Theoretical contact area estimates were found to agree with contact radius measurements carried out using optically transparent PDMS films observed through an optical microscope. Results show that C‐PDMS with 15 wt% carbon black exhibit a higher rate if change of resistivity and gauge factor than films of same thickness with 18 wt% carbon black. On the other hand, thicker films exhibit higher gauge factors for the two tested carbon black contents. Tests carried out at multiple locations yielded consistent sensitivity values, making these types of composites suitable for array type force sensors.
more »
« less
- Award ID(s):
- 1810402
- PAR ID:
- 10453588
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Journal of Applied Polymer Science
- Volume:
- 138
- Issue:
- 18
- ISSN:
- 0021-8995
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Despite the growing interest in flexible electronics and wearable sensors, research in piezoresistive polymer nanocomposites has stagnated in consideration of the polymer matrices, particularly in additive manufacturing (AM) applications. This research focuses on using a low‐molecular isoprene rubber (IR) as a matrix filled with carbonaceous nanoparticles conductive carbon black (CCB) and carbon nanotubes (CNT) to create piezoresistive sensors printed via direct ink writing (DIW). Using IR as a matrix not only provides an avenue for an alternate sensor matrix, but also offers a distinct advantage for retrofit sensor applications to other diene rubber substrates due to both the feedstock and substrate possessing the same vulcanization mechanism. Thereby, the rheological, mechanical, and piezoresistive properties of the IR nanocomposites are fully investigated, with emphasis on non‐ambient conditions (temperature and durability). In this work it is shown that while CCB exhibits a lower gauge factor (between 1.5 and 8) across all strain rates, strain ranges, and temperatures when compared to CNT compounds (gauge factors between 1.5 and 260), CCB compounds possess better linearity, less temperature deviation, and overall better performance under cyclic loading conditions. This is followed by demonstrations for real‐world applications, including the direct‐to‐product printing of a CCB strain gauge on a chloroprene rubber substrate. HighlightsAM via DIW of piezoresistive isoprene sensors filled with conductive CB and multi‐wall carbon nanotubes.Printed samples capable of achieving tensile strength >3.5 MPa.CB sensors showed less sensitivity, but better durability and repeatability compared to carbon nanotube filled sensors.Piezoresistive isoprene strain gauge printed on chloroprene substrate with direct adhesion.more » « less
-
Sensitive and flexible pressure sensors have invoked considerable interest for a broad range of applications in tactile sensing, physiological sensing, and flexible electronics. The barrier between high sensitivity and low fabrication cost needs to be addressed to commercialize such flexible pressure sensors. A low-cost sacrificial template-assisted method for the capacitive sensor has been reported herein, utilizing a porous Polydimethylsiloxane (PDMS) polymer and a multiwalled carbon nanotube (MWCNT) composite-based dielectric layer. The sensor shows high sensitivity of 2.42 kPa−1 along with a low limit of detection of 1.46 Pa. The high sensitivity originates from adding MWCNT to PDMS, increasing the composite polymer’s dielectric constant. Besides this, the pressure sensor shows excellent stability at a cyclic loading of 9000 cycles, proving its reliability for long-lasting application in tactile and physiological sensing. The high sensitivity of the sensor is suitable for the detection of small deformations such as pulse waveforms as well as tactile pressure sensing. In addition, the paper demonstrates a simultaneous contact and non-contact sensing capability suitable for dual sensing (pressure and proximity) with a single data readout system. The dual-mode sensing capability may open opportunities for realizing compact systems in robotics, gesture control, contactless applications, and many more. The practicality of the sensor was shown in applications such as tactile sensing, Morse code generator, proximity sensing, and pulse wave sensing.more » « less
-
Abstract Periodic micro/nanoscale structures from nature have inspired the scientific community to adopt surface design for various applications, including superhydrophobic drag reduction. One primary concern of practical applications of such periodic microstructures remains the scalability of conventional microfabrication technologies. This study demonstrates a simple template‐free scalable manufacturing technique to fabricate periodic microstructures by controlling the ribbing defects in the forward roll coating. Viscoelastic composite coating materials are designed for roll‐coating using carbon nanotubes (CNT) and polydimethylsiloxane (PDMS), which helps achieve a controllable ribbing with a periodicity of 114–700 µm. Depending on the process parameters, the patterned microstructures transition from the linear alignment to a random structure. The periodic microstructure enables hydrophobicity as the water contact angles of the samples ranged from 128° to 158°. When towed in a static water pool, a model boat coated with the microstructure film shows 7%–8% faster speed than the boat with a flat PDMS film. The CNT addition shows both mechanical and electrical properties improvement. In a mechanical scratch test, the cohesive failure of the CNT‐PDMS film occurs in ≈90% higher force than bare PDMS. Moreover, the nonconductive bare PDMS shows sheet resistance of 747.84–22.66 Ω □−1with 0.5 to 2.5 wt% CNT inclusion.more » « less
-
Intense Pulsed Light Sintering (IPL) uses pulsed, large-area, broad-spectrum visible light from a xenon lamp for rapid fusion of nanomaterials into films or patterns used in flexible sensors, solar cells, displays and other applications. Past work on the IPL of silver nanoparticles has shown that a self-damping coupling between densification and optical absorption governs the evolution of the deposited nanomaterial temperature during IPL. This work examines the influence of the nanomaterial shape distribution on this coupling and on the temperature evolution in IPL of silver nanowire–nanoparticle composite films. The film thickness, resistivity, micromorphology, crystallinity and optical properties are compared for varying ratios of nanowire to nanoparticle content in the film. It is shown for the first time, that increasing the nanowire content reduces the maximum film temperature during IPL from 240 °C to 150 °C and substantially alters the temperature evolution trends over consecutive pulses, while enabling film resistivity within 4–5 times that of bulk silver in 2.5 seconds of processing time. Nanoscale electromagnetic models are used to understand optical absorption as a function of changing ratio of nanowires to nanoparticles in a model assembly that emulates the IPL experiments performed here. The coupling between densification and optical absorption is found to inherently depend on the nanomaterial shape distribution and the ability of this phenomenon to explain the experimental temperature evolution trends is discussed. The implications of these observations for controlling self-damping coupling in IPL and the optimum nanoparticle to nanowire ratios for concurrently achieving high throughput, low processing temperatures, low material costs and low resistivity in IPL of conductive metallic nanomaterials are also described.more » « less