Polyurethane (PU) elastomers are among the most used rubberlike materials due to their combined merits, including high abrasion resistance, excellent mechanical properties, biocompatibility, and good processing performance. A PU elastomer exhibits pronounced hysteresis, leading to a high toughness on the order of 104 J/m2. However, toughness gained from hysteresis is ineffective to resist crack growth under cyclic load, causing a fatigue threshold below 100 J/m2. Here we report a fatigue-resistant PU fiber–matrix composite, using commercially available Spandex as the fibers and PU elastomer as the matrix. The Spandex fibers are stiff, strong, and stretchable. The matrix is soft, tough, and stretchable. We describe a pullout test to measure the adhesion toughness between the fiber and matrix. The test is highly reproducible, showing an adhesion toughness of 3170 J/m2. The composite shows a maximum stretchability of 6.0, a toughness of 16.7 kJ/m2, and a fatigue threshold of 3900 J/m2. When a composite with a precut crack is stretched, the soft matrix causes the crack tip to blunt greatly, which distributes high stress over a long segment of the Spandex fiber ahead the crack tip. This deconcentration of stress makes the composite resist the growth of cracks under monotonic and cyclic loads. The PU elastomer composites open doors for realistic applications of fatigue-resistant elastomers
more »
« less
Fiber‐Reinforced Viscoelastomers Show Extraordinary Crack Resistance That Exceeds Metals
Abstract Soft fiber‐reinforced polymers (FRPs), consisting of rubbery matrices and rigid fabrics, are widely utilized in industry because they possess high specific strength in tension while allowing flexural deformation under bending or twisting. Nevertheless, existing soft FRPs are relatively weak against crack propagation due to interfacial delamination, which substantially increases their risk of failure during use. In this work, a class of soft FRPs that possess high specific strength while simultaneously showing extraordinary crack resistance are developed. The strategy is to synthesize tough viscoelastic matrices from acrylate monomers in the presence of woven fabrics, which generates soft composites with a strong interface and interlocking structure. Such composites exhibit fracture energy,Γ, of up to 2500 kJ m−2, exceeding the toughest existing materials. Experimental elucidation shows that the fracture energy obeys a simple relation,Γ = W · lT, whereWis the volume‐weighted average of work of extension at fracture of the two components andlTis the force transfer length that scales with the square root of fiber/matrix modulus ratio. SuperiorΓis achieved through a combination of extraordinarily largelT(10–100 mm), resulting from the extremely high fiber/matrix modulus ratios (104–105), and the maximized energy dissipation density,W. The elucidated quantitative relationship provides guidance toward the design of extremely tough soft composites.
more »
« less
- Award ID(s):
- 1903308
- PAR ID:
- 10455341
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials
- Volume:
- 32
- Issue:
- 31
- ISSN:
- 0935-9648
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
In this work, we report 3D printable soft composites that are simultaneously stretchable and tough. The matrix of the composite consists of polydimethylsiloxane containing octuple hydrogen bonding sites, resulting in a material significantly tougher than conventional polydimethylsiloxane. Short glass fibers are also added to the material. Prior to solvent evaporation, the material possesses a viscoelastic yield stress making it suitable for printing via direct ink writing. We mechanically characterize the printed composite, including fracture tests. We observe robust crack deflection and delay of catastrophic failure, leading to measured toughness values up to 2 00 000 J m −2 for specimens with 5 vol% glass fibers. The printed composites exhibit an unprecedented combination of stiffness, stretchability, and toughness.more » « less
-
Abstract Shape‐persistent, conductive ionogels where both mechanical strength and ionic conductivity are enhanced are developed using multiphase materials composed of cellulose nanocrystals and hyperbranched polymeric ionic liquids (PILs) as a mechanically strong supporting network matrix for ionic liquids with an interrupted ion‐conducting pathway. The integration of needlelike nanocrystals and PIL promotes the formation of multiple hydrogen bonding and electrostatic ionic interaction capacitance, resulting in the formation of interconnected networks capable of confining a high amount of ionic liquid (≈95 wt%) without losing its self‐sustained shape. The resulting nanoporous and robust ionogels possess outstanding mechanical strength with a high compressive elastic modulus (≈5.6 MPa), comparable to that of tough, rubbery materials. Surprisingly, these rigid materials preserve the high ionic conductivity of original ionic liquids (≈7.8 mS cm−1), which are distributed within and supported by the nanocrystal network‐like rigid frame. On the one hand, such stable materials possess superior ionic conductivities in comparison to traditional solid electrolytes; on the other hand, the high compression resistance and shape‐persistence allow for easy handling in comparison to traditional fluidic electrolytes. The synergistic enhancement in ion transport and solid‐like mechanical properties afforded by these ionogel materials make them intriguing candidates for sustainable electrodeless energy storage and harvesting matrices.more » « less
-
Load-bearing soft tissues normally show J-shaped stress–strain behaviors with high compliance at low strains yet high strength at high strains. They have high water content but are still tough and durable. By contrast, naturally derived hydrogels are weak and brittle. Although hydrogels prepared from synthetic polymers can be strong and tough, they do not have the desired bioactivity for emerging biomedical applications. Here, we present a thermomechanical approach to replicate the combinational properties of soft tissues in protein-based photocrosslinkable hydrogels. As a demonstration, we create a gelatin methacryloyl fiber hydrogel with soft tissue-like mechanical properties, such as low Young’s modulus (0.1 to 0.3 MPa), high strength (1.1 ± 0.2 MPa), high toughness (9,100 ± 2,200 J/m 3 ), and high fatigue resistance (2,300 ± 500 J/m 2 ). This hydrogel also resembles the biochemical and architectural properties of native extracellular matrix, which enables a fast formation of 3D interconnected cell meshwork inside hydrogels. The fiber architecture also regulates cellular mechanoresponse and supports cell remodeling inside hydrogels. The integration of tissue-like mechanical properties and bioactivity is highly desirable for the next-generation biomaterials and could advance emerging fields such as tissue engineering and regenerative medicine.more » « less
-
null (Ed.)Fully biodegradable unidirectional green composites with excellent tensile properties were fabricated by combining one of the highest specific strength liquid crystalline cellulose (LCC) fibers as the reinforcement and microfibrillated cellulose (MFC) strengthened nonedible avocado seed starch (AVS)-based resin. MFC/AVS resin was crosslinked using 1,2,3,4-butane tetracarboxylic acid as well as plasticized using sorbitol or glycerol. Combination of alkali, mechanical and thermal treatments improved LCC fiber fracture stress from 1.5 GPa to over 1.9 GPa and Young’s modulus from 49 to 64 GPa. While the type and amount of plasticizer used changed the fracture strain of MFC/AVS resin, they also showed significant influence on the mechanical properties of the unidirectional composites. These composites prepared by hand lay-up, based on modified LCC fibers resulted in fracture stress of over 380 MPa and Young’s modulus of 19.5 GPa with less than 40% fiber content. Results suggest that there is scope to improve the properties further by using higher fiber content and automated manufacturing. These ‘green’ composites with excellent strength and stiffness may be used in many applications such as construction, automobile and others.more » « less