This work investigates the effects of doping on both the thermodynamics and kinetics of sintering in aluminum‐doped yttrium oxide nanoparticles (Al‐doped Y2O3), with the objective of delineating their interdependent effects at different stages of the process. Direct measurements of surface and grain boundary energies using differential scanning calorimetry showed that Al‐doping decreases both interfacial energies, leading to an increase in dihedral angle (from 152.7 ± 5.6° to 165.8 ± 5.5°) and, therefore, sintering stress. Densification and grain growth analyses showed that despite this increase in sintering stress, the onset of sintering is delayed for the Al‐doped samples, demonstrating that a large dihedral angle is a necessary but not sufficient condition for densification. The measurements of activation energies for densification and grain growth point out that Al suppresses grain boundary mobility by increasing the activation energy from 400 to 448 kJ/mol, hindering densification at the intermediate stages of sintering. At temperatures above 1150℃, grain growth is activated in the Al‐doped samples, which rapidly releases the accumulated sintering stress and exhibits a higher densification rate than in undoped Y2O3. This study demonstrates a complex interconnectivity between the thermodynamics and kinetics at different temperature ranges of sintering and reinforces the need for a comprehensive description for proper design of sintering aids.
Surface energy (
- NSF-PAR ID:
- 10456893
- Publisher / Repository:
- Wiley-Blackwell
- Date Published:
- Journal Name:
- Journal of the American Ceramic Society
- Volume:
- 103
- Issue:
- 9
- ISSN:
- 0002-7820
- Page Range / eLocation ID:
- p. 4903-4912
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract This work describes the role of manganese (Mn) as a sintering aid for magnesium aluminate (MgAl2O4) nanoparticles. Mn‐doped MgAl2O4nanoparticles, synthesized by coprecipitation method, showed increased surface area when contrasted to undoped MgAl2O4. Fast firing of compacted‐doped nanoparticles achieved high degree of densification at temperatures as low as 1100°C with very moderate grain growth, resulting in average sizes at the nanoscale (~60 nm). Differential scanning calorimetry was used to quantify the exothermic heat effects of sintering, which combined with quantitative microstructural evolution analysis enabled calculation of both surface and grain boundary energies. The results revealed that Mn effectively reduces the surface and grain boundary energies which led to dihedral angle broadening and consequently increased sintering stress. Experimental data also revealed a concomitant decrease in the activation energy of sintering with Mn doping which dropped from 644 kJ/mol for undoped MgAl2O4to 285 kJ/mol, informing Mn acts as a sintering aid in a thermokinetic manner.
-
more » « less
Abstract The properties of technical ceramics are highly dependent on their microstructure, which evolves during sintering. Sintering is the process by which ceramic parts are subjected to high temperatures to activate chemical diffusion and the consumption of porosity. During the initial stage of sintering, interparticle necks between neighboring particles form and subsequently increase in size, consuming porosity as the particle centers move closer together. To experimentally determine how this process depends on particle surface composition, particle atomic layer deposition (ALD) was used to deposit a thin film of amorphous aluminum oxide (Al2O3) onto yttria‐stabilized tetragonal zirconia (3YSZ) particles, producing core‐shell structured powders. The uniformity of the Al2O3film was confirmed with transmission electron microscopy and energy dispersive spectroscopy. Scanning electron microscopy was used to observe microstructural evolution during sintering, and the dihedral angles of Al2O3and 3YSZ grains were measured to determine the ratio of interfacial energies between the 3YSZ|3YSZ, 3YSZ|Al2O3, and Al2O3|Al2O3interfaces. Analysis of the densification kinetics revealed that the initial stage of densification is dependent on the material at the surface of the particles (ie, the Al2O3film) and is controlled by the diffusion of Al3+cations through Al2O3. Once the Al2O3film has coalesced, the sintering behavior is controlled by the densification of the core material (3YSZ). Thus, core‐shell powders fabricated by particle ALD sinter by a two‐step process where the kinetics are dependent on the material present at interparticle contacts.
-
more » « less
Abstract A knowledge-based understanding of the plasma-surface-interaction with the aim to precisely control (reactive) sputtering processes for the deposition of thin films with tailored and reproducible properties is highly desired for industrial applications. In order to understand the effect of plasma parameter variations on the film properties, a single plasma parameter needs to be varied, while all other process and plasma parameters should remain constant. In this work, we use the Electrical Asymmetry Effect in a multi-frequency capacitively coupled plasma to control the ion energy at the substrate without affecting the ion-to-growth flux ratio by adjusting the relative phase between two consecutive driving harmonics and their voltage amplitudes. Measurements of the ion energy distribution function and ion flux at the substrate by a retarding field energy analyzer combined with the determined deposition rate
R dfor a reactive Ar/N2(8:1) plasma at 0.5 Pa show a possible variation of the mean ion energy at the substrateE migwithin a range of 38 and 81 eV that allows the modification of the film characteristics at the grounded electrode, when changing the relative phase shiftθ between the applied voltage frequencies, while the ion-to-growth flux ratio Γig/Γgrcan be kept constant. AlN thin films are deposited and exhibit an increase in compressive film stress from −5.8 to −8.4 GPa as well as an increase in elastic modulus from 175 to 224 GPa as a function of the mean ion energy. Moreover, a transition from the preferential orientation (002) at low ion energies to the (100), (101) and (110) orientations at higher ion energies is observed. In this way, the effects of the ion energy on the growing film are identified, while other process relevant parameters remain unchanged. -
more » « less
Abstract Sintering additives are generally considered to be important for improving densification in fabrication of transparent ceramics. However, the sintering aids as impurities doped in the laser materials would decrease the laser output power and produce additional heat during laser operation. In this work, Yb:YAG ceramics were vacuum‐sintered without additives at different temperatures for various soaking time through using ball‐milled powders synthesized by co‐precipitation route. The densification behavior and grain growth kinetics of Yb:YAG ceramics were systematically investigated through densification curves and microstructural characterizations. It was determined that the densification in the 1500°C‐1600°C temperature range was controlled by a grain‐boundary diffusion. It is revealed that the volume diffusion is the main mechanism controlling the grain growth between 1600°C and 1750°C. Although SiO2additives can promote densification during low‐temperature sintering, the optical transmittance of Yb:YAG ceramic with no additives, sintered at 1800°C for 15 hours, reaches a maximum of 83.4% at 1064 nm, very close to the measured transmittance value of Yb:YAG single crystal. The optical attenuation loss was measured at 1064 nm in Yb:YAG transparent ceramic, to be 0.0035 cm−1, a value close to that observed for single crystals.