skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Highly Stretchable Polymer Composite with Strain‐Enhanced Electromagnetic Interference Shielding Effectiveness
Abstract Polymer composites with electrically conductive fillers have been developed as mechanically flexible, easily processable electromagnetic interference (EMI) shielding materials. Although there are a few elastomeric composites with nanostructured silvers and carbon nanotubes showing moderate stretchability, their EMI shielding effectiveness (SE) deteriorates consistently with stretching. Here, a highly stretchable polymer composite embedded with a three‐dimensional (3D) liquid‐metal (LM) network exhibiting substantial increases of EMI SE when stretched is reported, which matches the EMI SE of metallic plates over an exceptionally broad frequency range of 2.65–40 GHz. The electrical conductivities achieved in the 3D LM composite are among the state‐of‐the‐art in stretchable conductors under large mechanical deformations. With skin‐like elastic compliance and toughness, the material provides a route to meet the demands for emerging soft and human‐friendly electronics.  more » « less
Award ID(s):
1933398
PAR ID:
10458684
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Materials
Volume:
32
Issue:
14
ISSN:
0935-9648
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; (, Advanced Functional Materials)
    Abstract Current stretchable conductors, often composed of elastomeric composites infused with rigid conductive fillers, suffer from limited stretchability and durability, and declined conductivity with stretching. These limitations hinder their potential applications as essential components such as interconnects, sensors, and actuators in stretchable electronics and soft machines. In this context, an innovative elastomeric composite that incorporates a 3D network of liquid metal (LM), offering exceptional stretchability, durability, and conductivity, is introduced. The mechanics model elucidates how the interconnected 3DLM architecture imparts softness and stretchability to the composites, allowing them to withstand tensile strains of up to 500% without rupture. The relatively low surface‐to‐volume ratio of the 3DLM network limits the reforming of the oxide layer during cyclic stretch, thereby contributing to low permanent strain and enhanced durability. Additionally, the 3D architecture facilitates crack blunting and stress delocalization, elevating fracture resistance, while simultaneously establishing continuous conductive pathways that result in high conductivity. Notably, the conductivity of the 3DLM composite increases with strain during substantial stretching, highlighting its strain‐enhanced conductivity. In comparison to other LM‐based composites featuring 0D LM droplets, the 3DLM composite stands out with superior properties. 
    more » « less
  2. ; ; ; (, Advanced Engineering Materials)
    In this work, a composite of barium ferrite (BaM) and multiwalled carbon nanotubes (CNTs) in a polymer matrix of polydimethylsiloxane (PDMS) are reported for the purpose of suppressing electromagnetic interference (EMI). Shielding is accomplished primarily through absorption, which arises from a combination of the ferromagnetic resonance (FMR) from the BaM and conductive losses from the CNTs. The composite is fabricated by mixing commercially available BaM nanoparticles and CNTs into PDMS, screen printing the mixture into molds, then curing at 80 °C in a DC magnetic field. Characterization involves placing the composite in the cross‐section of a rectangular waveguide, then using a vector network analyzer (VNA) to measure scattering (S) parameters from 33–50 GHz. Using the measured S parameters, power reflected and absorbed can be calculated and used to characterize the composite's shielding effectiveness (SE), and the complex permittivity and permeability can be determined. The resulting 2.4 mm thick composite shows a peak absorption of 26.9 dB at the FMR frequency of 47.4 GHz. When normalized for thickness, the composite, on average, absorbs 11.3 dB mm−1and operates at a higher frequency than other shielding composites found in the literature. 
    more » « less
  3. ; ; ; ; ; ; ; ; (, Advanced Materials Technologies)
    Abstract Simulation and experimental studies are carried out on single‐layer and double‐layer embedded metal meshes (SLEMM and DLEMM) to assess their performance as transparent electromagnetic interference (EMI) shielding. The structures consist of silver meshes embedded in polyethylene terephthalate (PET). As a transparent electrode, SLEMMs exhibit a transparency of 82.7% and a sheet resistance of 0.61 Ωsq−1as well as 91.0% and 1.49 Ωsq−1. This performance corresponds to figures of merit of 3101 and 2620, respectively. The SLEMMs achieve 48.0 dB EMI shielding efficiency (SE) in the frequency range of 8–18 GHz (X‐ and Ku‐bands) with 91% visible transmission and 56.2 dB EMI SE with 82.7% visible transmission. Samples exhibit stable performance after 1000 bending cycles with a radius of curvature of 4 mm and 60 tape test cycles. DLEMMs consist of fabricating SLEMM on opposite sides of the substrate where the distance can be varied using a spacer. Simulations are performed to investigate how varying spacer distance between two layers of metal meshes influences the EMI SE. DLEMMs are fabricated and achieved an EMI SE of 77.7 dB with 81.7% visible transmission. SLEMMs and DLEMMs may have a wide variety of applications in aerospace, medical, and military applications. 
    more » « less
  4. ; ; ; ; ; ; (, Advanced Functional Materials)
    Abstract All‐solid‐state flexible asymmetric supercapacitors (ASCs) are developed by utilization of graphene nanoribbon (GNR)/Co0.85Se composites as the positive electrode, GNR/Bi2Se3composites as the negative electrode, and polymer‐grafted‐graphene oxide membranes as solid‐state electrolytes. Both GNR/Co0.85Se and GNR/Bi2Se3composite electrodes are developed by a facile one‐step hydrothermal growth method from graphene oxide nanoribbons as the nucleation framework. The GNR/Co0.85Se composite electrode exhibits a specific capacity of 76.4 mAh g−1at a current density of 1 A g−1and the GNR/Bi2Se3composite electrode exhibits a specific capacity of 100.2 mAh g−1at a current density of 0.5 A g−1. Moreover, the stretchable membrane solid‐state electrolytes exhibit superior ionic conductivity of 108.7 mS cm−1. As a result, the flexible ASCs demonstrate an operating voltage of 1.6 V, an energy density of 30.9 Wh kg−1at the power density of 559 W kg−1, and excellent cycling stability with 89% capacitance retention after 5000 cycles. All these results demonstrate that this study provides a simple, scalable, and efficient approach to fabricate high performance flexible all‐solid‐state ASCs for energy storage. 
    more » « less
  5. ; ; ; ; (, Advanced Materials)
    Abstract Electronic devices are ubiquitous in modern society, yet their poor recycling rates contribute to substantial economic losses and worsening environmental impacts from electronic waste (E‐waste) disposal. Here, recyclable and healable electronics are reported through a vitrimer‐liquid metal (LM) microdroplet composite. These electrically conductive, yet plastic‐like composites display mechanical qualities of rigid thermosets and recyclability through a dynamic covalent polymer network. The composite exhibits a high glass transition temperature, good solvent resistance, high electrical conductivity, and recyclability. The vitrimer synthesis proceeds without the need for a catalyst or a high curing temperature, which enables facile fabrication of the composite materials. The as‐synthesized vitrimer exhibits a fast relaxation time with reconfigurability and shape memory. The electrically conductive composite exhibits high electrical conductivity with LM volume loading as low as 5 vol.%. This enables the fabrication of fully vitrimer‐based circuit boards consisting of sensors and indicator LEDs integrated with LM‐vitrimer conductive wiring. Electrical self‐healing and thermally triggered material healing are further demonstrated with the composites. The vitrimer and LM‐composite provide a pathway toward fully recyclable, mechanically robust, and reconfigurable electronics, thus advancing the field of electronic materials. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email