Al-V alloys produced via high-energy ball milling have been reported to show simultaneous improvement of corrosion resistance and mechanical properties compared to traditional Al alloys. In these alloys, V content plays a crucial role in increasing or decreasing the corrosion resistance. Therefore, the effect of V and microstructure on corrosion of high-energy ball milled and subsequently spark plasma sintered Al-xV alloys (x = 2, 5, 10 at%) has been studied. Cyclic potentiodynamic polarization tests and electrochemical impedance spectroscopic analysis revealed the increment of V content up to 5 at% enhanced the corrosion resistance of the alloy. However, highly heterogeneous microstructure in Al-10 at%V resulted in significant localized corrosion over the immersion time. The electrochemical impedance spectroscopy studies over 14 days of immersion revealed underlying corrosion mechanisms.
The time-dependent corrosion behavior of pure aluminum (Al) in a chloride-containing environment was investigated using various electrochemical and characterization techniques for up to 336 h. Transmission electron microscopic and secondary ion mass spectroscopic analysis revealed the continuous dissolution of the surface film over the immersion time. In the meantime, the increasing passive oxide thickness resulted in the surface film resistance enhancement over the immersion time, as indicated by the electrochemical impedance spectroscopic analysis. The electrochemical noise measurements showed an increase in the corrosion kinetics with immersion time until 60 h because of the accelerated localized corrosion in the early stage of immersion. However, an inhibition in corrosion kinetics occurred after longer immersion times due to corrosion product deposition inside the pit.
more » « less- NSF-PAR ID:
- 10465649
- Publisher / Repository:
- The Electrochemical Society
- Date Published:
- Journal Name:
- Journal of The Electrochemical Society
- Volume:
- 170
- Issue:
- 9
- ISSN:
- 0013-4651
- Page Range / eLocation ID:
- Article No. 091505
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
more » « less
Nanocrystalline supersaturated Al-V alloys produced by high-energy ball milling have been reported to exhibit enhanced corrosion resistance and mechanical properties compared to commercial Al alloys. Corrosion of passive alloys such as Al-V alloy relies on the characteristics of the surface film, which is studied using scanning/transmission electron microscopy and time-of-flight secondary ion mass spectrometry. The effect of microstructure and composition on the surface film has been investigated after different immersion periods (30 min, 2 h, and 1 day) in 0.1 M NaCl. The surface film was complex and composed of oxidized Al and V. The heterogeneous surface film was observed due to the presence of secondary phases and initiation of localized corrosion. The void formation was observed beneath the surface film that would potentially cause pitting corrosion. The generation of nano-sized voids was dependent on grain orientation. Compared to pure Al, the chloride penetration is suppressed in Al-V alloys. The effect of composition and microstructure on surface film formation and attendant corrosion behavior is discussed herein.
-
more » « less
Abstract Catalytic interface of semiconductor photoelectrodes is critical for high-performance photoelectrochemical solar water splitting because of its multiple roles in light absorption, electrocatalysis, and corrosion protection. Nevertheless, simultaneously optimizing each of these processes represents a materials conundrum owing to conflicting requirements of materials attributes at the electrode surface. Here we show an approach that can circumvent these challenges by collaboratively exploiting corrosion-resistant surface stoichiometry and structurally-tailored reactive interface. Nanoporous, density-graded surface of ‘black’ gallium indium phosphide (GaInP2), when combined with ammonium-sulfide-based surface passivation, effectively reduces reflection and surface recombination of photogenerated carriers for high efficiency photocatalysis in the hydrogen evolution half-reaction, but also augments electrochemical durability with lifetime over 124 h via strongly suppressed kinetics of corrosion. Such synergistic control of stoichiometry and structure at the reactive interface provides a practical pathway to concurrently enhance efficiency and durability of semiconductor photoelectrodes without solely relying on the development of new protective materials.
-
more » « less
Abstract We demonstrate that the corrosion of AISI 1045 medium carbon steel and pure aluminum can be quantified by the turn-off fluorescent sensor Phen Green-SK (PGSK) in ethanol-based solutions. We first evaluate the dependence of the chelation enhanced quenching of PGSK on iron and aluminum ion concentrations. Subsequently, we apply PGSK to examine the anodic dissolution of metal corrosion. The observed time-dependent PGSK-quenching quantifies the corrosion rates of two metals over 24-hours of immersion in ethanol-based solutions. The PGSK-based quantification of corrosion is compared to scanning electron microscopy and electrochemical techniques, including open circuit potential and Tafel extrapolation. The corrosion rates calculated from PGSK-quenching and Tafel extrapolation are in agreement, and both indicate a decrease in corrosion rates over 24-hours. Our work shows PGSK can efficiently sense and quantify anodic corrosion reactions at metal interfaces, especially in organic solvents or other non-aqueous environments where the application of electrochemical techniques can be limited by the poor conductivity of the surrounding medium.
-
more » « less
Exposure testing was performed on CoCrFeMnNi equiatomic high entropy alloy (HEA) produced via directed energy deposition additive manufacturing in NaNO3-KNO3(60–40 wt%) molten salt at 500 °C for 50 h to evaluate the corrosion performance and oxide film chemistry of the HEA. Potentiodynamic electrochemical corrosion testing, scanning electron microscopy, focused ion beam milling coupled with energy dispersive spectroscopy, Raman spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and inductively coupled plasma optical emission spectroscopy were used to analyze the corrosion behavior and chemistry of the HEA/nitrate molten salt system. The CoCrFeMnNi HEA exhibited a higher passive current density during potentiodynamic polarization testing than steel alloys SS316L and 4130 and the high-Ni alloy 800 H in identical conditions. The oxide film was primarily composed of a (Mn,Co,Ni)Fe2O4spinel with a vertical plate-like morphology at the surface. Cr and Ni were found to be totally depleted at the outer surface of the oxide and dissolved in high concentrations in the molten salt. While Cr was expected to dissolve into the molten salt, the high concentration of dissolved Ni has not been observed with traditional alloys, suggesting that Ni is less stable in the spinel when Mn and Co are present.