Transition metal selenides have attracted intensive interest as cost-effective electrocatalysts for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) because of the continuous thrust in sustainable energy conversion. In this article a Mn-based bifunctional electrocatalyst, MnSe, has been identified which shows efficient OER and ORR activity in alkaline medium. The catalytic activity could be further enhanced by using multiwalled carbon nanotubes (MWCNTs) which increases the charge transfer and electronic conductivity of the catalyst composite. This MnSe@MWCNT catalyst composite exhibits a very low overpotential of 290 mV at 10 mA cm −2 , which outperforms state-of-the-art RuO 2 as well as other oxide based electrocatalysts. Furthermore, the composite's facile OER kinetics was evidenced by its small Tafel slope of 54.76 mV dec −1 and low charge transfer resistance, indicating quick transport of the reactant species at the electrode interface. The MnSe@MWCNT also exhibited efficient electrocatalytic activity for ORR with an E onset of 0.94 V, which is among the best reported to date for chalcogenide based ORR electrocatalysts. More importantly, this MnSe-based ORR electrocatalyst exhibits high degree of methanol tolerance, showing no degradation of catalyst performance in the presence of copious quantities of methanol, thereby out-performing the state-of-the-art Pt electrocatalyst. The catalyst composite also exhibited exceptional functional and compositional stability for OER and ORR after a prolonged period of continuous operation in alkaline medium. The surface Raman analysis after OER revealed the retention of manganese selenide surface with evidence of oxo coordination, confirming the formation of an (oxy)selenide as the active surface for OER. Such efficient bifunctional OER and ORR activity makes this MnSe based catalyst attractive for overall electrolysis in regenerative as well as direct methanol fuel cells.
more »
« less
This content will become publicly available on October 19, 2024
Unraveling the Cooperative Activity of Hydrophilicity, Conductivity, and Interfacial Active Sites in Alginate‐CNT‐Cuo Self‐Standing Electrodes with Benchmark‐Close Activity for Alkaline Water Splitting
Designing electrocatalysts that excel in hydrogen and oxygen electrochemistry is crucial for sustainable hydrogen generation through electrochemical water splitting. This study presents a novel tricomponent catalyst composed of an alginate hydrogel (AL) infused with single‐walled carbon nanotubes (CNTs) and copper oxide (CuO) nanoparticles. The catalyst exhibits benchmark‐close bifunctional activity toward hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) under alkaline conditions. The aerophobic nature of the AL‐gel facilitates superior bubble release from the electrode, while the inclusion of CNTs mitigates charge transfer resistance. Moreover, heterojunctions of CuO and CNTs create unique interfacial active sites, culminating in high electrocatalytic water‐splitting activity. The structural rigidity of the composite permits its use as self‐standing electrodes (SSE) without using substrates or binders, enabling a direct evaluation of its activity. The composite electrode demonstrates exceptional electrocatalytic HER activity in an alkaline solution, with onset potentials of 93 mV and moderate OER activity with an onset of 155 mV. Moreover, a water electrolysis cell featuring the bifunctional SSE exhibits an open circuit voltage of 1.85 V at 100 mA.cm−2, and only 8% efficiency loss after 100 h marking this a significant stride in developing self‐standing nonprecious electrocatalysts with impressive catalytic performance.
more » « less- NSF-PAR ID:
- 10469847
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Sustainable Systems
- Volume:
- 7
- Issue:
- 12
- ISSN:
- 2366-7486
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Designing efficient electrocatalysts has been one of the primary goals for water electrolysis, which is one of the most promising routes towards sustainable energy generation from renewable sources. In this article, we have tried to expand the family of transition metal chalcogenide based highly efficient OER electrocatalysts by investigating nickel telluride, Ni 3 Te 2 as a catalyst for the first time. Interestingly Ni 3 Te 2 electrodeposited on a GC electrode showed very low onset potential and overpotential at 10 mA cm −2 (180 mV), which is the lowest in the series of chalcogenides with similar stoichiometry, Ni 3 E 2 (E = S, Se, Te) as well as Ni-oxides. This observation falls in line with the hypothesis that increasing the covalency around the transition metal center enhances catalytic activity. Such a hypothesis has been previously validated in oxide-based electrocatalysts by creating anion vacancies. However, this is the first instance where this hypothesis has been convincingly validated in the chalcogenide series. The operational stability of the Ni 3 Te 2 electrocatalyst surface during the OER for an extended period of time in alkaline medium was confirmed through surface-sensitive analytical techniques such as XPS, as well as electrochemical methods which showed that the telluride surface did not undergo any corrosion, degradation, or compositional change. More importantly we have compared the catalyst activation step (Ni 2+ → Ni 3+ oxidation) in the chalcogenide series, through electrochemical cyclic voltammetry studies, and have shown that catalyst activation occurs at lower applied potential as the electronegativity of the anion decreases. From DFT calculations we have also shown that the hydroxyl attachment energy is more favorable on the Ni 3 Te 2 surface compared to the Ni-oxide, confirming the enhanced catalytic activity of the telluride. Ni 3 Te 2 also exhibited efficient HER catalytic activity in alkaline medium making it a very effective bifunctional catalyst for full water splitting with a cell voltage of 1.66 V at 10 mA cm −2 . It should be noted here that this is the first report of OER and HER activity in the family of Ni-tellurides.more » « less
-
more » « less
Abstract Multifunctional materials that are capable of facilitating multiple electrocatalytic processes are highly desirable. This work reports the observation of bifunctional electrocatalytic properties for water‐splitting in layered oxides, featuring 2‐dimensional layers of octahedrally coordinated transition metals separated by alkaline‐earth or rare‐earth metals. Remarkably, these materials are able to catalyze both half‐reactions of water‐splitting,
i. e ., oxygen‐evolution reaction (OER) and hydrogen‐evolution reaction (HER). Electrical charge‐transport studies of SrLaFe1‐xCoxO4‐δin a wide range of temperatures, 25 to 800 °C, indicate semiconducting behavior for all three compounds, where there is a systematic increase in electrical conductivity as a function of temperature. The end member of the series, SrLaCoO4‐δ, exhibits the highest electrical charge transport and best electrocatalytic activity toward both OER and HER. This catalyst also features the highest degree of polyhedral distortion as well as the presence of oxygen‐vacancies. In addition, the transition metals in this material have a favorable electronic configuration for enhanced electrocatalytic activity. -
null (Ed.)Electrochemical water splitting is one of the most promising approaches for sustainable energy conversion and storage toward a future hydrogen society. This demands durable and affordable electrocatalysts for the hydrogen evolution reaction (HER) and the oxygen evolution reaction (OER). In this study, we report the preparation of uniform Ni–P–O, Ni–S–O, and Ni–S–P–O electrocatalytic films on nickel foam (NF) substrates via flow cell-assisted electrodeposition. Remarkably, electrodeposition onto 12 cm 2 substrates was optimized by strategically varying critical parameters. The high quality and reproducibility of the materials is attributed to the use of a 3D-printed flow cell with a tailored design. Then, the as-fabricated electrodes were tested for overall water splitting in the same flow cell under alkaline conditions. The best-performing sample, NiSP/NF, required relatively low overpotentials of 93 mV for the HER and 259 mV for the OER to produce a current density of 10 mA cm −2 . Importantly, the electrodeposited films underwent oxidation into amorphous nickel (oxy)hydroxides and oxidized S and P species, improving both HER and OER performance. The superior electrocatalytic performance of the Ni–S–P–O films originates from the unique reconstruction process during the HER/OER. Furthermore, the overall water splitting test using the NiSP/NF couple required a low cell voltage of only 1.85 V to deliver a current density of 100 mA cm −2 . Overall, we demonstrate that high-quality electrocatalysts can be obtained using a simple and reproducible electrodeposition method in a robust 3D-printed flow cell.more » « less
-
more » « less
Abstract Electrocatalysts are required for clean energy technologies (for example, water‐splitting and metal‐air batteries). The development of a multifunctional electrocatalyst composed of nitrogen, phosphorus, and fluorine tri‐doped graphene is reported, which was obtained by thermal activation of a mixture of polyaniline‐coated graphene oxide and ammonium hexafluorophosphate (AHF). It was found that thermal decomposition of AHF provides nitrogen, phosphorus, and fluorine sources for tri‐doping with N, P, and F, and simultaneously facilitates template‐free formation of porous structures as a result of thermal gas evolution. The resultant N, P, and F tri‐doped graphene exhibited excellent electrocatalytic activities for the oxygen reduction reaction (ORR), oxygen evolution reaction (OER), and hydrogen evolution reaction (HER). The trifunctional metal‐free catalyst was further used as an OER–HER bifunctional catalyst for oxygen and hydrogen gas production in an electrochemical water‐splitting unit, which was powered by an integrated Zn–air battery based on an air electrode made from the same electrocatalyst for ORR. The integrated unit, fabricated from the newly developed N, P, and F tri‐doped graphene multifunctional metal‐free catalyst, can operate in ambient air with a high gas production rate of 0.496 and 0.254 μL s−1for hydrogen and oxygen gas, respectively, showing great potential for practical applications.