Title: Selected Area Deposition of High Purity Gold for Functional 3D Architectures

Selected area deposition of high purity gold films onto nanoscale 3D architectures is highly desirable as gold is conductive, inert, plasmonically active, and can be functionalized with thiol chemistries, which are useful in many biological applications. Here, we show that high-purity gold coatings can be selectively grown with the Me2Au (acac) precursor onto nanoscale 3D architectures via a pulsed laser pyrolytic chemical vapor deposition process. The selected area of deposition is achieved due to the high thermal resistance of the nanoscale geometries. Focused electron beam induced deposits (FEBID) and carbon nanofibers are functionalized with gold coatings, and we demonstrate the effects that laser irradiance, pulse width, and precursor pressure have on the growth rate. Furthermore, we demonstrate selected area deposition with a feature-targeting resolutions of ~100 and 5 µm, using diode lasers coupled to a multimode (915 nm) and single mode (785 nm) fiber optic, respectively. The experimental results are rationalized via finite element thermal modeling.

more » « less
Award ID(s):
Author(s) / Creator(s):
; ;
Publisher / Repository:
Date Published:
Journal Name:
Page Range / eLocation ID:
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
    more » « less
  2. Abstract

    Applications in soft, flexible optical, and optoelectronic applications demand polymer thin film coatings that can accommodate substantial physical deformations. The preparation of high refractive index polymers (HRIPs) through the quaternization of poly(4‐vinylpyridine) (P4VP) thin films with (di)halomethanes is presented. P4VP thin films are prepared by initiated chemical vapor deposition (iCVD) and then quaternized through exposure to saturated vapors of iodomethane (CH3I), dibromomethane (CH2Br2), and diiodomethane (CH2I2), resulting in refractive indices (RI) as high as 1.67, 1.71, and 2.07, respectively (at 632.8 nm). Fourier‐transform infrared (FTIR) spectroscopy and X‐ray photoelectron spectroscopy (XPS) confirmed the quaternization of pyridine pendant groups on the polymer chain to n‐methylpyridinium with primarily an iodide or bromide counterion, though a minor fraction of polyiodides are also detected. Additionally, these films demonstrate superior thermal stability, retaining their refractive index and thickness after thermal excursions to 200 °C. The halogenated P4VP films exhibit superior mechanical flexibility relative to conventional inorganic coatings (Al2O3and Ta2O5) and do not fracture at uniaxial tensile strains as high as 10%. This new material chemistry and fabrication approach method may enable advanced optical designs and functionality in a wide range of substrates and device architectures.

    more » « less
  3. Stimuli-responsive polymers functionalized with reactive inorganic groups enable creation of macromolecular structures such as hydrogels, micelles, and coatings that demonstrate smart behavior. Prior studies using poly( N -isopropyl acrylamide- co -3-(trimethoxysilyl)propyl methacrylate) (P(NIPAM- co -TMA)) have stabilized micelles and produced functional nanoscale coatings; however, such systems show limited responsiveness over multiple thermal cycles. Here, polymer architecture and TMA content are connected to the aqueous self-assembly, optical response, and thermoreversibility of two distinct types of PNIPAM/TMA copolymers: random P(NIPAM- co -TMA), and a ‘blocky-functionalized’ copolymer where TMA is localized to one portion of the chain, P(NIPAM- b -NIPAM- co -TMA). Aqueous solution behavior characterized via cloud point testing (CPT), dynamic light scattering (DLS), and variable-temperature nuclear magnetic resonance spectroscopy (NMR) demonstrates that thermoresponsiveness and thermoreversibility over multiple cycles is a strong function of polymer configuration and TMA content. Despite low TMA content (≤2 mol%), blocky-functionalized copolymers assemble into small, well-ordered structures above the cloud point that lead to distinct transmittance behaviors and stimuli-responsiveness over multiple cycles. Conversely, random copolymers form disordered aggregates at elevated temperatures, and only exhibit thermoreversibility at negligible TMA fractions (0.5 mol%); higher TMA content leads to irreversible structure formation. This understanding of the architectural and assembly effects on the thermal cyclability of aqueous PNIPAM- co -TMA can be used to improve the scalability of responsive polymer applications requiring thermoreversible behavior, including sensing, separations, and functional coatings. 
    more » « less
  4. Abstract

    Photopolymerization is a ubiquitous, indispensable technique widely applied in applications from coatings, inks, and adhesives to thermosetting restorative materials for medical implants, and the fabrication of complex macroscale, microscale, and nanoscale 3D architectures via additive manufacturing. However, due to the brittleness inherent in the dominant acrylate‐based photopolymerized networks, a significant need exists for higher performance resin/oligomer formulations to create tough, defect‐free, mechanically ductile, thermally and chemically resistant, high modulus network polymers with rapid photocuring kinetics. This study presents densely cross‐linked triazole‐based glassy photopolymers capable of achieving preeminent toughness of ≈70 MJ m−3and 200% strain at ambient temperature, comparable to conventional tough thermoplastics. Formed either via photoinitiated copper(I)‐catalyzed cycloaddition of monomers containing azide and alkyne groups (CuAAC) or via photoinitiated thiol‐ene reactions from monomers containing triazole rings, these triazole‐containing thermosets completely recover their original dimensions and mechanical behavior after repeated deformations of 50% strain in the glassy state over multiple thermal recovery–strain cycles.

    more » « less
  5. Self-sufficient and non-contact sensors play multiple roles in lunar, planetary exploration, and Earth structures. These sensors allow engineers to accurately examine structural integrity and defects on mechanical components for optimal operations. Structural integrity allows the industry to ensure the safety and capacity of key structures. Materials like α-alumina can be employed as sensors due to the photoluminescent properties that they possess. Piezospectroscopy is a non-destructive evaluation (NDE) method capable of capturing in-situ stress using α-alumina due to the chromium ion impurities that it contains. The chromium ion impurities carry spectral characteristics, that when excited with an Nd: YAG laser (532 nm), demonstrate capabilities for structural integrity monitoring. In this work, a 3D printing method is developed to autonomously create sensors that are compatible with use in space environments. The 3D printing method intends to provide the industry flexible and adaptive solutions for structural integrity monitoring. This method includes a modified Fused Deposition Method printer by exchanging its original nozzle with a syringe base nozzle. The printing parameters such as printing speed, printing bed temperature, coating thickness, and syringe volume are determined during the testing process. Challenges include achieving uniform integration and nanoparticle dispersion as well as adhesion between the matrix and the substrates. The parameters to encounter these challenges will depend on the materials used. Experiments with three different volume fractions (VF) of α-alumina within an epoxy were performed to address the printing challenges. The sensors were applied to nine specimens, three of each VF but with varying deposition rates after the mixture process. These experiments considered the mixing and deposition method while testing the dispersion within the α-alumina and the epoxy matrix. The substrates, on which the epoxy matrix was deposited, underwent a surface treatment to ensure adhesion between the substrate and the sensor matrix. During this experiment, the epoxy matrix was deposited with a syringe onto a substrate and cured at room temperature. The specimens were tested with a tensile load using an electromechanical MTS. While the samples are tensile loaded, the sensors were characterized via photoluminescent piezo spectroscopy to determine which VF demonstrates the best stress sensing capabilities, along with the adhesion between the matrix and the substrate. The data collected allows the optimal VF to be established for future applications. 
    more » « less