Abstract The combination of thinning ice, larger waves, and damage due to diurnal thermal cycling motivate the need to better understand the impact of flexing under the action of oceanic waves on the strength of thermally cracked ice. To that end, new experiments were performed on freshwater, lab‐grown ice and first‐year natural sea ice. Both materials were cracked by thermal shocking and then subsequently cyclically flexed. Initially, the thermal cracks weakened both materials. When the cracked ice of either origin was cyclically flexed under fully reversed loading, its flexural strength, initially reduced by the stress‐concentrating action of the cracks, recovered to the strength of non‐cracked, non‐flexed ice. When the cracked ice was cyclically flexed non‐reversely, its strength recovered only partially. During reversed cyclic flexing, the cracked region experienced alternately compressive and tensile stresses. We suggest compression resulted in contact of opposing crack faces followed by sintering leading to strength recovery. During non‐reversed cyclic flexing, contact and sintering were reduced and ice strength did not fully recover. The tendency for cracks to heal during cyclic flexing may lessen their threat to the structural integrity of an ice cover.
more »
« less
Behavior of saline ice under cyclic flexural loading
Abstract. New systematic experiments reveal that the flexural strength of saline S2 columnar-grained ice loaded normal to the columns can be increased upon cyclic loading by about a factor of 1.5. The experiments were conducted using reversed cyclic loading over ranges of frequencies from 0.1 to 0.6 Hz and at a temperature of −10 ∘C on saline ice of two salinities: 3.0 ± 0.9 and 5.9 ± 0.6 ‰. Acoustic emission hit rate during cycling increases with an increase in stress amplitude of cycling. Flexural strength of saline ice of 3.0 ± 0.9 ‰ salinity appears to increase linearly with increasing stress amplitude, similar to the behavior of laboratory-grown freshwater ice (Murdza et al., 2020b) and to the behavior of lake ice (Murdza et al., 2021). The flexural strength of saline ice of 5.9 ± 0.6 ‰ depends on the vertical location of the sample within the thickness of an ice puck; i.e., the strength of the upper layers, which have a lower brine content, was found to be as high as 3 times that of lower layers. The fatigue life of saline ice is erratic. Cyclic strengthening is attributed to the development of an internal back stress that opposes the applied stress and possibly originates from dislocation pileups.
more »
« less
- Award ID(s):
- 1947107
- PAR ID:
- 10494405
- Publisher / Repository:
- Copernicus
- Date Published:
- Journal Name:
- The Cryosphere
- Volume:
- 15
- Issue:
- 5
- ISSN:
- 1994-0424
- Page Range / eLocation ID:
- 2415 to 2428
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
This paper presents a summary of the element test simulations (calibration simulations) submitted by 11 numerical simulation (prediction) teams that participated in the LEAP-2017 prediction exercise. A significant number of monotonic and cyclic triaxial (Vasko, An investigation into the behavior of Ottawa sand through monotonic and cyclic shear tests. Masters Thesis, The George Washington University, 2015; Vasko et al., LEAP-GWU-2015 Laboratory Tests. DesignSafe-CI, Dataset, 2018; El Ghoraiby et al., LEAP 2017: Soil characterization and element tests for Ottawa F65 sand. The George Washington University, Washington, DC, 2017; El Ghoraiby et al., LEAP-2017 GWU Laboratory Tests. DesignSafe-CI, Dataset, 2018; El Ghoraiby et al., Physical and mechanical properties of Ottawa F65 Sand. In B. Kutter et al. (Eds.), Model tests and numerical simulations of liquefaction and lateral spreading: LEAP-UCD-2017. New York: Springer, 2019) and direct simple shear tests (Bastidas, Ottawa F-65 Sand Characterization. PhD Dissertation, University of California, Davis, 2016) are available for Ottawa F-65 sand. The focus of this element test simulation exercise is to assess the performance of the constitutive models used by participating team in simulating the results of undrained stress-controlled cyclic triaxial tests on Ottawa F-65 sand for three different void ratios (El Ghoraiby et al., LEAP 2017: Soil characterization and element tests for Ottawa F65 sand. The George Washington University, Washington, DC, 2017; El Ghoraiby et al., LEAP-2017 GWU Laboratory Tests. DesignSafe-CI, Dataset, 2018; El Ghoraiby et al., Physical and mechanical properties of Ottawa F65 Sand. In B. Kutter et al. (Eds.), Model tests and numerical simulations of liquefaction and lateral spreading: LEAP-UCD-2017. New York: Springer, 2019). The simulated stress paths, stress-strain responses, and liquefaction strength curves show that majority of the models used in this exercise are able to provide a reasonably good match to liquefaction strength curves for the highest void ratio (0.585) but the differences between the simulations and experiments become larger for the lower void ratios (0.542 and 0.515).more » « less
-
Abstract. The flexural strength of ice surfaces bonded by freezing, termedfreeze bond, was studied by performing four-point bending tests of bondedfreshwater S2 columnar-grained ice samples in the laboratory. The sampleswere prepared by milling the surfaces of two ice pieces, wetting two of thesurfaces with water of varying salinity, bringing these surfaces together,and then letting them freeze under a compressive stress of about 4 kPa. Thesalinity of the water used for wetting the surfaces to generate the bondvaried from 0 to 35 ppt (parts per thousand). Freezing occurred in air under temperatures varyingfrom −25 to −3 ∘C over periods that varied from 0.5 to∼ 100 h. Results show that an increase in bond salinity ortemperature leads to a decrease in bond strength. The trend for the bondstrength as a function of salinity is similar to that presented in Timco andO'Brien (1994) for saline ice. No freezing occurs at −3 ∘C oncethe salinity of the water used to generate the bond exceeds ∼ 25 ppt. The strength of the saline ice bonds levels off (i.e., saturates)within 6–12 h of freezing; bonds formed from freshwater reach strengthsthat are comparable or higher than that of the parent material in less than0.5 h.more » « less
-
Abstract Cyclic degradation in flexible electronic inks remains a key challenge while their deployment in life critical applications is ongoing. The origin of electrical degradation of a screen-printed stretchable conductive ink with silver flakes embedded in a polyurethane binder is investigated under uniaxial monotonic and cyclic stretching, using in-situ confocal microscopy and scanning electron microscopy experiments, for varying ink thickness (1, 2, and 3 layers, each layer around 8–10 μ m) and trace width (0.5, 1, and 2 mm). Cracks form under monotonic stretching, and the evolution of crack pattern (density, length and width) with applied strain is affected by ink thickness such that the 3-layer ink exhibits larger normalized resistance but slightly lower resistance than the 1-layer ink up to strains of 125%. For cyclic stretching, the crack density and length do not evolve with cycling. However, the cracks widen and deepen, leading to an increase in resistance with cycling. There exists a strong correlation between fatigue life, i.e. the number of cycles until a normalized resistance of 100 is reached, and the strain amplitude. The normalized resistance increase rate with respect to cycling is also found to scale with strain amplitude. The rate of change in resistance with cycling decreases with ink thickness and trace width. For practical applications, thicker ( ⩾ 25 μ m) and wider (⩾2 mm) inks should be used to lower resistance increases with repeated deformation.more » « less
-
In this research study, the fracture strength of flat 10 mm thick annealed glass sheets having an abrasive water-jet cut surface and bearing against a transparent interface material is experimentally investigated. The transparent interface material is necessary to provide axial-compressive force continuity in modular compression-dominant all- glass shell structures. A series of short glass columns were tested in axial compression under a variety of load cases, which included cyclic, creep, and monotonic-to-fracture loading. A target glass fracture bearing stress of 36.6 MPa is identified and represents an upper bound bearing stress for annealed glass compression members failing in a flexural buckling mode. The study concludes the transparent thermoplastic material, known as Surlyn, was able to achieve a fracture strength that exceeds the target value and that the fracture strength is not affected by cyclic or creep loading. Consequently, column-related failure limit states will occur before glass fracture is associated with interface bearing. Glass fracture occurs in Type-I mode, reflecting the presence of interface tensile stress. Furthermore, the monotonic bearing stiffness in the service range of 5 to 15 MPa is increased by 20 % and 16 % for samples subjected to cyclic and creep loading, respectively, relative to monotonic-only samples.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.5194/tc-15-2415-2021