This paper studies a polymer network in which crosslinks are degradable but polymer chains are not. We show that entanglements markedly enhance the mechanical properties of the polymer network before degradation and slow down degradation. We synthesize polyacrylamide hydrogels with disulfide crosslinks. In a precursor of a low water-to-monomer molar ratio and low crosslinker-to-monomer molar ratio, the monomers are crowded and the resulting polymer chains are long, so that the entanglements greatly outnumber crosslinks. The as-synthesized hydrogels are submerged in pure water to swell to equilibrium. We show that entanglements enhance the swell resistance of the hydrogel, as well as stiffen and toughen the hydrogel. We further show that entanglements slow down degradation when the hydrogel is submerged in an aqueous solution of cysteine. This work demonstrates that entanglements substantially expand the properties space of degradable polymers.
more »
« less
Making Highly Elastic and Tough Hydrogels from Doughs
A hydrogel is often fabricated from preexisting polymer chains by covalently crosslinking them into a polymer network. The crosslinks make the hydrogel swell‐resistant but brittle. This conflict is resolved here by making a hydrogel from a dough. The dough is formed by mixing long polymer chains with a small amount of water and photoinitiator. The dough is then homogenized by kneading and annealing at elevated temperatures, during which the crowded polymer chains densely entangle. The polymer chains are then sparsely crosslinked into a polymer network under an ultraviolet lamp, and submerged in water to swell to equilibrium. The resulting hydrogel is both swell‐resistant and tough. The hydrogel also has near‐perfect elasticity, high strength, high fatigue resistance, and low friction. The method is demonstrated with two widely used polymers, poly(ethylene glycol) and cellulose. These hydrogels have never been made swell‐resistant, elastic, and tough before. The method is generally applicable to synthetic and natural polymers, and is compatible with industrial processing technologies, opening doors to the development of sustainable, high‐performance hydrogels.
more » « less- Award ID(s):
- 2011754
- NSF-PAR ID:
- 10500041
- Publisher / Repository:
- Wiley
- Date Published:
- Journal Name:
- Advanced Materials
- Volume:
- 34
- Issue:
- 50
- ISSN:
- 0935-9648
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Double-network (DN) hydrogels, consisting of two contrasting and interpenetrating polymer networks, are considered as perhaps the toughest soft-wet materials. Current knowledge of DN gels from synthesis methods to toughening mechanisms almost exclusively comes from chemically-linked DN hydrogels by experiments. Molecular modeling and simulations of inhomogeneous DN structure in hydrogels have proved to be extremely challenging. Herein, we developed a new multiscale simulation platform to computationally investigate the early fracture of physically-chemically linked agar/polyacrylamide (agar/PAM) DN hydrogels at a long timescale. A “random walk reactive polymerization” (RWRP) was developed to mimic a radical polymerization process, which enables to construct a physically-chemically linked agar/PAM DN hydrogel from monomers, while conventional and steered MD simulations were conducted to examine the structural-dependent energy dissipation and fracture behaviors at the relax and deformation states. Collective simulation results revealed that energy dissipation of agar/PAM hydrogels was attributed to a combination of the pulling out of agar chains from the DNs, the disruption of massive hydrogen bonds between and within DN structures, and the strong association of water molecules with both networks, thus explaining a different mechanical enhancement of agar/PAM hydrogels. This computational work provided atomic details of network structure, dynamics, solvation, and interactions of a hybrid DN hydrogel, and a different structural-dependent energy dissipation mode and fracture behavior of a hybrid DN hydrogel, which help to design tough hydrogels with new network structures and efficient energy dissipation modes. Additionally, the RWRP algorithm can be generally applied to construct the radical polymerization-produced hydrogels, elastomers, and polymers.
-
ynthesis-property relation is fundamental to materials science, but many aspects of the relation are not well understood for many materials. Impetus for this paper comes from our recent appreciation for the distinct roles of entanglements and crosslinks in a polymer network. Here we study the synthesis-property relation of polyacrylamide hydrogels prepared by free radical polymerization. Some of the as-prepared hydrogels are further submerged in water to swell either to equilibrium or to a certain polymer content. The synthesis parameters include the composition of a precursor, as well as the polymer content of a hydrogel. Series of hydrogels are prepared along several paths in the space of synthesis parameters. For each hydrogel, the stress-stretch curve is measured, giving four properties: modulus, strength, stretchability, and work of fracture. We interpret the experimentally measured synthesis-property relation in terms of entropic polymer networks of covalent bonds. When the precursor has a low crosslinker-to-monomer molar ratio, the resulting polymer network has on average long polymer segments. When the precursor has a low water-to-monomer molar ratio, the resulting polymer network has on average many entanglements per polymer segment. We show that crosslinks lower strength, but entanglements do not. By contrast, both crosslinks and entanglements increase modulus. A network of highly entangled long polymer segments exhibits high swell resistance, modulus, and strength.more » « less
-
more » « less
Longer and stronger; stiff but not brittle Hydrogels are highly water-swollen, cross-linked polymers. Although they can be highly deformed, they tend to be weak, and methods to strengthen or toughen them tend to reduce stretchability. Two papers now report strategies to create tough but deformable hydrogels (see the Perspective by Bosnjak and Silberstein). Wang
et al . introduced a toughening mechanism by storing releasable extra chain length in the stiff part of a double-network hydrogel. A high applied force triggered the opening of cycling strands that were only activated at high chain extension. Kimet al . synthesized acrylamide gels in which dense entanglements could be achieved by using unusually low amounts of water, cross-linker, and initiator during the synthesis. This approach improves the mechanical strength in solid form while also improving the wear resistance once swollen as a hydrogel. —MSL -
more » « less
Abstract Hydrogels, exhibiting wide applications in soft robotics, tissue engineering, implantable electronics, etc., often require sophisticately tailoring of the hydrogel mechanical properties to meet specific demands. For examples, soft robotics necessitates tough hydrogels; stem cell culturing demands various tissue‐matching modulus; and neuron probes desire dynamically tunable modulus. Herein, a strategy to broadly alter the mechanical properties of hydrogels reversibly via tuning the aggregation states of the polymer chains by ions based on the Hofmeister effect is reported. An ultratough poly(vinyl alcohol) (PVA) hydrogel as an exemplary material (toughness 150 ± 20 MJ m−3), which surpasses synthetic polymers like poly(dimethylsiloxane), synthetic rubber, and natural spider silk is fabricated. With various ions, the hydrogel's various mechanical properties are continuously and reversibly in situ modulated over a large window: tensile strength from 50 ± 9 kPa to 15 ± 1 MPa, toughness from 0.0167 ± 0.003 to 150 ± 20 MJ m−3, elongation from 300 ± 100% to 2100 ± 300%, and modulus from 24 ± 2 to 2500 ± 140 kPa. Importantly, the ions serve as gelation triggers and property modulators only, not necessarily required to remain in the gel, maintaining the high biocompatibility of PVA without excess ions. This strategy, enabling high mechanical performance and broad dynamic tunability, presents a universal platform for broad applications from biomedicine to wearable electronics.
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1002/adma.202206577