Maximizing ion conduction in single-ion-conducting ionomers is essential for their application in energy-related technologies such as Li-ion batteries. Understanding the anion chemical composition impacts on ion conduction offers new perspectives to maximize ion transport, since the current approach of lowering T g has apparently reached a limit (lowest T g ∼ 190 K, highest conductivity ∼10 −5 –10 −4 S cm −1 ). Here, a series of random ionomers are synthesized by copolymerizing poly(ethylene glycol)methacrylate with either sulfonylimide lithium methacrylate (MTLi) or sulfonate lithium methacrylate (MSLi) using reversible addition–fragmentation chain transfer (RAFT) polymerization. Li-Ion conduction and self-diffusion coefficients ( D Li + ) of the ionomers are characterized with dielectric relaxation spectroscopy (DRS) and pulsed-field-gradient (PFG) NMR diffusometry, respectively. Increasing ion content decreases the Li-ion conductivity and D Li + , as expected from the increased T g . Moreover, a considerably lower ionic conductivity and D Li + are observed for MSLi compared to MTLi at constant ion content and T g / T . As revealed from X-ray scattering, strong ion aggregation in MSLi results in much lower conductivity and D Li + compared with less aggregated MTLi based on the more delocalized sulfonylimide anion. These results emphasize the detrimental and molecularly specific role of ion aggregation in Li-ion conductivity, and highlight the necessity for minimizing ion aggregation via the rational choice of anion chemical composition.
more »
« less
This content will become publicly available on May 1, 2025
Effect of background gas composition on the stoichiometry and lithium ion conductivity of pulse laser deposited epitaxial lithium lanthanum tantalate (Li3 x La1/3− x TaO3)
Lithium lanthanum tantalate (Li3xLa1/3−xTaO3, x = 0.075) thin films were grown via pulsed laser deposition using background gas atmospheres with varying partial pressures of oxygen and argon. The background gas composition was varied from 100% to 6.6% oxygen, with the pressure fixed at 150 mTorr. The maximum ion conductivity of 1.5 × 10−6 S/cm was found for the film deposited in 100% oxygen. The ion conductivity of the films was found to decrease with reduced oxygen content from 100% to 16.6% O2 in the background gas. The 6.6% oxygen background condition produced ion conductivity that approached that of the 100% oxygen condition film. The lithium transfer from the target to the film was found to decrease monotonically with decreasing oxygen content in the background gas but did not account for all changes in the ion conductivity. The activation energy of ion conduction was measured and found to correlate well with the measured ion conductivity trends. Analysis of x-ray diffraction results revealed that the films also exhibited a change in the lattice parameter that directly correlated with the ion conduction activation energy, indicating that a primary factor for determining the conductivity of these films is the changing size of the ion conduction bottleneck, which controls the activation energy of ion conduction.
more »
« less
- Award ID(s):
- 2055042
- PAR ID:
- 10502729
- Publisher / Repository:
- AIP
- Date Published:
- Journal Name:
- Journal of Vacuum Science & Technology A
- Volume:
- 42
- Issue:
- 3
- ISSN:
- 0734-2101
- Page Range / eLocation ID:
- 032705
- Subject(s) / Keyword(s):
- pulsed laser deposition atmosphere stoichiometry ion conductivity
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The (SmxGa1−x)2O3 alloy system is a potential new dielectric for compound semiconductors such as GaAs. Using molecular beam epitaxy under metal-modulated growth conditions, we grew the binary oxide, Sm2O3, at two substrate temperatures (100 and 500 °C) and optimized the structural, morphological, and electrical properties of the films. Decreasing the Sm cell temperature suppressed the formation of the monoclinic phase and promoted the growth of the cubic phase. Next, the ternary oxide, (SmxGa1−x)2O3, was deposited to investigate the effects of Ga incorporation. Optimization experiments were used to determine the effects of substrate temperature and samarium cell temperature (i.e., growth rate) on film stoichiometry, phase distribution, and microstructure in these films. Films grown at 500 °C showed significant surface roughness and the presence of multiple crystalline phases. Since all of the Sm-based oxides (i.e., samarium oxide with and without gallium) were found to have unbonded Sm metal, annealing experiments were carried out in oxygen and forming gas to determine the effects of annealing on film stoichiometry. The motivation behind annealing in forming gas was to see whether this commonly used technique for reducing interface densities could improve the film quality. GaAs metal-oxide-semiconductor diodes with (SmxGa1−x)2O3 showed breakdown fields at 1 mA/cm2 of 4.35 MV/cm, which decreased with increasing Sm unbonded metal content in the films.more » « less
-
GeSn films were simultaneously deposited on Si (100), Si (111), c-plane sapphire (Al2O3), and fused silica substrates to investigate the impact of the substrate on the resulting GeSn film. The electronic, structural, and optical properties of these films were characterized by temperature-dependent Hall-effect measurements, x-ray diffractometry, secondary ion mass spectrometry, and variable angle spectroscopic ellipsometry. All films were polycrystalline with varying degrees of texturing. The film on Si (100) contained only GeSn (100) grains, 40.4 nm in diameter. The film deposited on Si (111) contained primarily GeSn (111) grains, 36.4 nm in diameter. Both films deposited on silicon substrates were fully relaxed. The layer deposited on Al2O3 contained primarily GeSn (111) grains, 41.3 nm in diameter. The film deposited on fused silica was not textured, and the average grain size was 35.0 nm. All films contained ∼5.6 at. % Sn throughout the layer, except for the film deposited on Al2O3, which contained 7.5% Sn. The films deposited on Si (111), Al2O3, and fused silica exhibit p-type conduction over the entire temperature range, 10–325 K, while the layer deposited on the Si (100) substrate shows a mixed conduction transition from p-type at low temperature to n-type above 220 K. From ∼175 to 260 K, both holes and electrons contribute to conduction. Texturing of the GeSn film on Si (100) was the only characteristic that set this film apart from the other three films, suggesting that something related to GeSn (100) crystal orientation causes this transition from p- to n-type conduction.more » « less
-
Abstract All‐solid‐state rechargeable sodium (Na)‐ion batteries are promising for inexpensive and high‐energy‐density large‐scale energy storage. In this contribution, new Na solid electrolytes, Na3−yPS4−xClx, are synthesized with a strategic approach, which allows maximum substitution of Cl for S (x= 0.2) without significant compromise of structural integrity or Na deficiency. A maximum conductivity of 1.96 mS cm−1at 25 °C is achieved for Na3.0PS3.8Cl0.2, which is two orders of magnitude higher compared with that of tetragonal Na3PS4(t‐Na3PS4). The activation energy (Ea) is determined to be 0.19 eV. Ab initio molecular dynamics simulations shed light on the merit of maximizing Cl‐doping while maintaining low Na deficiency in enhanced Na‐ion conduction. Solid‐state nuclear magnetic resonance (NMR) characterizations confirm the successful substitution of Cl for S and the resulting change of P oxidation state from 5+ to 4+, which is also verified by spin moment analysis. Ion transport pathways are determined with a tracer‐exchange NMR method. The functional detects that promote Na ‐ion transport are maximized for further improvement in ionic conductivity. Full‐cell performance is demonstrated using Na/Na3.0PS3.8Cl0.2/Na3V2(PO4)3with a reversible capacity of ≈100 mAh g‐1at room temperature.more » « less
-
We present a 23Na nuclear spin dynamics model for interpreting nuclear magnetic resonance (NMR) spin-lattice relaxation and central linewidth data in the invert glass system Na4P2S7-xOx, 0 ≤ x ≤ 7. The glassy nature of this material results in variations in local Na+ cation environments that may be described by a Gaussian distribution of activation energies. A consistent difference between the mean activation energies determined by NMR and DC conductivity measurements was observed, and interpreted using a percolation theory model. From this, the Nasingle bondNa coordination number in the sodium cation sublattice was obtained. These values were consistent with jumps through tetrahedral faces of the sodium cages for the sulfur rich glasses, x < 5, consistent with proposed models of their short range order (SRO) structures. From NMR spin-echo measurements, we determined the Nasingle bondNa second moment M2 resulting from the Nasingle bondNa magnetic dipole interaction of nearest neighbors. Values of M2 obtained as a function of sodium number density N were in agreement with models for uniform sodium distribution, indicating that these invert glass systems form so as to maximize the average Nasingle bondNa distance. A simple Coulombic attraction model between Na+ cation and X (=S−, O−) anion was applied to calculate the activation energy. In the range 1.5 ≤ x ≤ 7, an increase in activation energy with increasing oxygen content x occurred, and was consistent with the decrease in average anionic radius, and the increase in Coulombic attraction. For small oxygen additions, 0 ≤ x ≤ 1.5, the suggested minimum at low oxygen concentration seen in the activation energies obtained from DC conductivity data is not evident in the model.more » « less