skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Synthesis and Characterization of Titanium Nitride–Carbon Composites and Their Use in Lithium-Ion Batteries
This work focuses on the synthesis of titanium nitride–carbon (TiN–carbon) composites by the thermal decomposition of a titanyl phthalocyanine (TiN(TD)) precursor into TiN. The synthesis of TiN was also performed using the sol-gel method (TiN(SG)) of an alkoxide/urea. The structure and morphology of the TiN–carbon and its precursors were characterized by XRD, FTIR, SEM, TEM, EDS, and XPS. The FTIR results confirmed the presence of the titanium phthalocyanine (TiOPC) complex, while the XRD data corroborated the decomposition of TiOPC into TiN. The resultant TiN exhibited a cubic structure with the FM3-M lattice, aligning with the crystal system of the synthesized TiN via the alkoxide route. The XPS results indicated that the particles synthesized from the thermal decomposition of TiOPC resulted in the formation of TiN–carbon composites. The TiN particles were present as clusters of small spherical particles within the carbon matrix, displaying a porous sponge-like morphology. The proposed thermal decomposition method resulted in the formation of metal nitride composites with high carbon content, which were used as anodes for Li-ion half cells. The TiN–carbon composite anode showed a good specific capacity after 100 cycles at a current density of 100 mAg−1.  more » « less
Award ID(s):
2011401 2122178
PAR ID:
10506819
Author(s) / Creator(s):
; ; ; ; ; ; ; ;
Publisher / Repository:
Nanomaterials
Date Published:
Journal Name:
Nanomaterials
Volume:
14
Issue:
7
ISSN:
2079-4991
Page Range / eLocation ID:
624
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; (, International Journal of Molecular Sciences)
    The present work focuses on the synthesis of a vanadium nitride (VN)/carbon nanocomposite material via the thermal decomposition of vanadyl phthalocyanine (VOPC). The morphology and chemical structure of the synthesized compounds were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), Fourier transformed infrared spectroscopy (FTIR), X-ray diffraction (XRD), and X-ray photoemission spectroscopy (XPS). The successful syntheses of the VOPC and non-metalated phthalocyanine (H2PC) precursors were confirmed using FTIR and XRD. The VN particles present a needle-like morphology in the VN synthesized by the sol-gel method. The morphology of the VN/C composite material exhibited small clusters of VN particles. The XRD analysis of the thermally decomposed VOPC indicated a mixture of amorphous carbon and VN nanoparticles (VN(TD)) with a cubic structure in the space group FM-3M consistent with that of VN. The XPS results confirmed the presence of V(III)-N bonds in the resultant material, indicating the formation of a VN/C nanocomposite. The VN/C nanocomposite synthesized through thermal decomposition exhibited a high carbon content and a cluster-like distribution of VN particles. The VN/C nanocomposite was used as an anode material in LIBs, which delivered a specific capacity of 307 mAh g−1 after 100 cycles and an excellent Coulombic efficiency of 99.8 at the 100th cycle. 
    more » « less
  2. ; ; ; ; ; ; (, Journal of Composites Science)
    Titanium nitride and vanadium nitride–carbon-based composite systems, TiN/C and VN/C, were prepared using a new synthesis method based on the thermal decomposition of titanyl tetraphenyl porphyrin (TiOTPP) and vanadyl tetraphenyl porphyrin (VOTPP), respectively. The structure of the TiN/C and VN/C composite materials, as well as their precursors, were characterized using Fourier Transformed Infrared Spectroscopy, X-Ray diffraction (XRD), X-Ray energy dispersive (EDS) and X-Ray photoelectron spectroscopy (XPS). Morphologies of the TiN/C and VN/C composites were examined by means of scanning electron (SEM) and transmission electron (TEM) microscopy. The synthesis of the non-metalated tetraphenyl porphyrin, the titanium, and vanadium tetraphenyl porphyrin complexes were confirmed using FTIR. The thermal decomposition of the titanium and vanadium tetraphenyl porphyrin complexes produced the respective metal nitride encapsulated in a carbon matrix; this was confirmed by XRD, SEM, TEM, and XPS. From the XRD patterns, it was determined that the TiN and VN were presented in cubic form with expected space group FM-3M and 1:1 (metal:N) stoichiometry. The XPS results confirmed the presence of both TiN and VN in the carbon matrix without metal carbides. The SEM and TEM results showed that both TiN and VN nanoparticles formed small clusters throughout the carbon matrix; the EDS results revealed a uniform composition. The synthesis method presented in this work is novel and serves as an effective means to produce TiN and VN NPs with good structure and morphology embedded in a carbon matrix. 
    more » « less
  3. ; ; ; ; ; ; ; ; (, Materials Express)
    Titanium nitride (TiN) materials have gained an interest over the past years due to their unique characteristics, such as thermal stability, extreme hardness, low production cost, and comparable optical properties to gold. In the present study, TiN nanoparticles were synthesized via a thermal benzene route to obtain black nanoparticles. Scanning electron microscopy (SEM) was carried out to examine the morphology. Further microscopic characterization was done where the final product was drop cast onto double-sided conductive carbon tape and sputter-coated with gold/palladium at a thickness of 4 nm for characterization by field emission scanning electron microscopy (FE-SEM) with energy dispersive X-Ray spectroscopy (EDS) that revealed they are spherical. ImageJ software was used to measure the average size of the particles to be 79 nm in diameter. EDS was used to determine the elements present in the sample and concluded that there were no impurities. Further characterization by Fourier Transform infrared (FTIR) spectroscopy was carried out to identify the characteristic peaks of TiN. X-ray diffraction (XRD) revealed typical peaks of cubic phase titanium nitride, and crystallite size was determined to be 14 nm using the Debye-Scherrer method. Dynamic light scattering (DLS) analysis revealed the size distribution of the TiN nanoparticles, with nanoparticles averaging at 154 nm in diameter. Zeta potential concluded the surface of the TiN nanoparticles is negatively charged. 
    more » « less
  4. ; ; ; ; ; ; (, Journal of Materials Research)
    null (Ed.)
    Nanosized, well-dispersed titania particles were synthesized via a hydrothermal method using multiwalled carbon nanotubes (MWCNTs) as structural modifiers during the nucleation process to decrease aggregation. Synthesized TiO 2 /MWCNT composites containing different amounts of MWCNTs were characterized using N 2 physisorption, XRD, spectroscopic techniques (Raman, UV-visible, and X-ray photoelectron), and electron microscopy to illuminate the morphology, crystal structure, and surface chemistry of the composites. Photocatalytic performance was evaluated by measuring the degradation of acetaldehyde in a batch reactor under UV illumination. Average rate constants decrease in the following order: TiO 2 /MWCNT-1% > TiO 2 > TiO 2 /MWCNT-5%. Addition of MWCNTs beyond the optimum loading ratio of 1:100 (MWCNT:TiO 2 ) diminishes the effectiveness of the photocatalyst and the synergistic effect between MWCNTs and TiO 2 . The primary mechanism for photocatalytic activity enhancement in TiO 2 /MWCNT-1% is thought to be due to increased porosity, hydroxyl enrichment on the surface, and high dispersion of TiO 2 particles. 
    more » « less
  5. ; ; ; ; ; ; ; ; (, New Journal of Chemistry)
    Astounding graphitic carbon nitride (g-C 3 N 4 ) nanostructures have attracted huge attention due to their unique electronic structures, suitable band gap, and thermal and chemical stability, and are insinuating as a promising candidate for photocatalytic and energy harvesting applications. The growth of a free-standing film is desirable for widespread electronic devices and electrochemical applications. Here, we present a facile approach to prepare free-standing films (15 mm × 10 mm × 0.5 mm) comprising g-C 3 N 4 nanolayers by the pyrolysis of dicyandiamide (C 2 H 4 N 4 ) utilizing the chemical vapor deposition (CVD) technique. The synthesis is done under low-pressure conditions of argon (∼3 Torr) and at a temperature of 600 °C. The as-synthesized g-C 3 N 4 films are systematically studied for their structural/microstructural characterization using X-ray diffraction (XRD), scanning and transmission electron microscopy (SEM and TEM), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR) and UV-visible spectroscopy techniques. The excitation-dependent photoluminescence (PL) spectra of the as-synthesized g-C 3 N 4 film exhibited an intense, stable and broad emission peak in the visible region at ∼459 nm. The emission spectra of free-standing g-C 3 N 4 films show a blue shift and band sharpening compared to that of the g-C 3 N 4 powder. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email