Wire arc additive manufacturing (WAAM) is an effective technique for producing medium to large-size components, due to its convenience and sustainability in fabricating large-scale parts with high deposition rates, employing low-cost and simple equipment, and attaining high material efficiency. Thus, WAAM attracts different industrial sectors and has experienced great growth, particularly over the last decade to overcome production market’s challenges. Consequently, fabricating parts in WAAM, mostly resulted in heterogeneity in microstructure of three different zones towards the buildup direction due to different cooling rates; upper zone (thin surface layer of fine grains), middle zone (undesired large columnar grains covers 90% of the produced part), and lower zone (intermediate columnar grains close to substrate material). Accordingly, producing parts consisting of different zones affects the final component's mechanical properties. Therefore, controlling the formation of these zones is a key role in improving WAAM technique. Altering torch motion and cooling rates were found to be effective methods to control the homogeneity of the final component in WAAM.
more »
« less
Preventing columnar grains growth during hybrid wire arc additive manufacturing of austenitic stainless steel 316L
Abstract Wire arc additive manufacturing (WAAM) is an efficient technique for producing medium to large‐size components, due to its accessibility and sustainability in fabricating large‐scale parts with high deposition rates, employing low‐cost and simple equipment, and achieving high material efficiency. Consequently, WAAM has garnered attention across various industrial sectors and experienced significant growth, particularly over the last decade, as it addresses and mitigates challenges within production markets. One of the primary limitations of WAAM is its thermal history during the process, which directly influences grain formation and microstructure heterogeneity in the resulting part. Understanding the thermal cycle of the WAAM process is thus crucial for process improvement. Typically, fabricating a part using WAAM results in a microstructure with three distinct zones along the build direction: an upper zone (thin surface layer) with fine grains, a middle zone dominated by undesirably long and large columnar grains covering more than 90% of the produced part, and a lower zone with smaller to intermediate columnar grains closer to the substrate material. These zones arise from variations in cooling rates, with the middle zone exhibiting the lowest cooling rate due to 2D conduction heat transfer. Consequently, producing a component with a microstructure comprising three different zones, with a high fraction of large and long columnar grains, significantly impacts the final mechanical properties. Therefore, controlling the size and formation of these grain zones plays a key role in improving WAAM. The aim of this work is to investigate the formation of undesired columnar grains in austenitic stainless steel 316L during WAAM and propose a simple hybrid technique by combining WAAM with a hot forging process (with or without interlayer cooling time). This approach targets the disruption of the solidification pattern of columnar grain growth during deposition progression and aims to enhance the microstructure of WAAM components.
more »
« less
- PAR ID:
- 10507172
- Publisher / Repository:
- Wiley
- Date Published:
- Journal Name:
- Engineering Reports
- ISSN:
- 2577-8196
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Gas metal arc additive manufacturing (GMA-AM), also known as wire arc additive manufacturing (WAAM), uses an electric arc to melt a wire electrode and deposit objects layer by layer. This study focuses on creating single-pass wall structures using a low-carbon steel wire (ER70S-6) and examining the relationship between pulse frequency and weld geometry, microstructure, and mechanical properties. Microscopic observations showed a typical columnar microstructure with three distinct regions: acicular ferrite, bainite, and allotriomorphic ferrite in the first and last layers, while the mid-region exhibited homogenous polygonal ferrite grains with some pearlite at the grain boundaries. The tensile test results demonstrated a dependency of strength on the applied pulse frequency, with the highest strength (i.e., the ultimate tensile strength of 522 MPa and yield strength of 375 MPa with ductility of ∼52%) achieved in parts processed at a frequency of 100 Hz. Vickers microhardness values revealed uniform hardness in the middle region, consistent with the microstructure observation. Analyzing thermal cycles, coupled with microstructure analysis and continuous cooling transition diagrams, provided insight into how phase and microstructure evolution occurred in low-carbon low-alloy steels processed through PGMA-AM.more » « less
-
Abstract The main research goal of this study is to decipher the intercorrelation between process-induced thermal-structure-property relationships of Stainless Steel 316L fabricated by laser powder bed fusion. The objective therein is achieved by explaining and quantifying the effect of processing parameters and part-scale thermal history on microstructure evolution and mechanical properties of these parts. Multiple previous works have correlated the effect of process parameters on flaw formation, microstructural features evolved and functional properties; however, a lack of understanding remains in the underlying effect of the thermal history on part microstructure and mechanical properties. The thermal distribution, or thermal history, of the part as it is being built layer-by-layer is influenced by the processing parameters, material properties and shape of the part. The thermal history influences the microstructure by changing the grain structure evolution, which affects the part properties. Therefore, the novelty of this paper lies in illuminating the process-thermal history-microstructure-property relationship in laser powder bed fusion. Characterization of tensile specimens processed at a variety of conditions reveal a direct influence of the choice of process parameters on the dendritic structure and the grain orientations. A high energy density leads to <100> textured columnar dendritic grains and low energy density leads to randomly oriented equiaxed grains as a result of the shifting heat influx. The tensile properties are correlated with the inherent microstructure. Through future work involving fracture surface analysis, the texture, grain size and porosity is expected to influence the inherent fracture mechanism. This work demonstrates that an understanding of thermal distribution within a printed part can inform the choice of processing conditions to generate the final microstructure as per the specified functional requirements. Thus, this paper lays the foundation for future prediction and control of microstructure and functional properties in laser powder bed fusion by identifying the root fundamental thermal phenomena that influences the microstructure evolution and part properties.more » « less
-
The 70/30 copper–nickel alloy is used mainly in critical parts with more demanding conditions in marine settings. There is a need for innovative methods that offer fast production and cost-effectiveness in order to supplement current copper–nickel alloy manufacturing processes. In this study, we employ wire arc additive manufacturing (WAAM) to fabricate the 70/30 copper–nickel alloy. The as-built microstructure is characterized by columnar grains with prominent dendrites and chemical segregation in the inter-dendritic area. The aspect ratio of the columnar grain increases with increasing travel speed (TS) at the same wire feed speed (WFS). This is in contrast with the equiaxed grain structure, with a more random orientation, of the conventional sample. The sample built with a WFS of 8 m/min, TS of 1000 mm/min, and a track distance of 3.85 mm exhibits superior corrosion properties in the 3.5 wt% NaCl solution when compared with the conventional sample, as evidenced by a higher film resistance and breakdown potential, along with a lower passive current density of the WAAM sample. The corrosion morphology reveals the critical roles played by the nickel element that is unevenly distributed between the dendrite core and inter-dendritic area.more » « less
-
We demonstrate the possibility of spatially controlling the degree of grain boundary serration in functionally graded stainless steels, by alloying powder mixtures on-the-fly during directed energy deposition additive manufacturing. Grain boundary serration is an attractive feature in polycrystalline microstructures, as it confers superior resistance to crack propagation and hot corrosion. Quantitative measurements at the microstructure scale coupled with thermodynamic calculations allow us to propose a mechanism to explain the origin of grain boundary serration. The formation of transient δ ferrite during solidification and its subsequent dissolution during cooling, governed by the Cr/Ni ratio, leads to the formation of remnant ferrite particles that hinder the growth of austenite grains in the solid state via a Smith-Zener pinning phenomenon. This finding opens new perspectives for grain boundary engineering, in-situ during additive manufacturing.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1002/eng2.12914