Abstract Organic mixed ionic‐electronic conductors (OMIECs) have garnered significant attention due to their capacity to transport both ions and electrons, making them ideal for applications in energy storage, neuromorphics, and bioelectronics. However, charge compensation mechanisms during the polymer redox process remain poorly understood, and are often oversimplified as single‐ion injection with little attention to counterion effects. To advance understanding and design strategies toward next‐generation OMIEC systems, a series of p‐channel carboxylated mixed conductors is investigated. Varying side‐chain functionality, distinctive swelling character is uncovered during electrochemical doping/dedoping with model chao‐/kosmotropic electrolytes. Carboxylic acid functionalized polymers demonstrate strong deswelling and mass reduction during doping, indicating cation expulsion, while ethoxycarbonyl counterparts exhibit prominent mass increase, pointing to an anion‐driven doping mechanism. By employingoperandograzing incidence X‐ray fluorescence (GIXRF), it is revealed that the carboxyl functionalized polymer engages in robust cation interaction, whereas ester functionalization shifts the mechanism towards no cation involvement. It is demonstrated that cations are pivotal in mitigating swelling by counterbalancing anions, enabling efficient anion uptake without compromising performance. These findings underscore the transformative influence of functionality‐driven factors and side‐chain chemistry in governing ion dynamics and conduction, providing new frameworks for designing OMIECs with enhanced performance and reduced swelling.
more »
« less
Photoluminescence Probes Ion Insertion into Amorphous and Crystalline Regions of Organic Mixed Conductors
Abstract Organic mixed ionic‐electronic conductors (OMIECs) have emerged as promising materials for a wide range of next‐generation technologies, including bioelectronics and neuromorphic computing. The performance of these materials depends on the transport of ions through the polycrystalline polymer matrix as well as how the distribution of ions and polarons in crystalline and amorphous regions impacts electronic transport. However, it is often challenging to distinguish whether ions enter crystalline or amorphous regions. In this work, steady‐state and time‐resolved photoluminescence (PL) spectroelectrochemistry is used to probe initial ion insertion in crystalline and amorphous regions of the OMIEC material poly(3‐[2‐[2‐(2‐methoxyethoxy)ethoxy]ethyl]thiophene ‐2,5‐diyl) (P3MEEET) as a function of applied voltage. It is found that PL spectroelectrochemistry reports on the initial stages of electrochemical doping through the quenching of PL emission. By distinguishing between amorphous and crystalline contributions to the PL spectrum, ion insertion in crystalline and amorphous regions as a function of voltage is tracked. It is found that PL spectroelectrochemistry is much more sensitive to the initial injection of ions than complementary methods, highlighting its potential as a sensitive tool for interrogating ion injection in OMIECs.
more »
« less
- Award ID(s):
- 2304613
- PAR ID:
- 10509280
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 34
- Issue:
- 40
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Chalcogel represents a unique class of meso‐ to macroporous nanomaterials that offer applications in energy and environmental pursuits. Here, the synthesis of an ion‐exchangeable amorphous chalcogel using a nominal composition of K2CoMo2S10(KCMS) at room temperature is reported. Synchrotron X‐ray pair distribution function (PDF), X‐ray absorption near‐edge structure (XANES), and extended X‐ray absorption fine structure (EXAFS) reveal a plausible local structure of KCMS gel consisting of Mo5+2and Mo4+3clusters in the vicinity of di/polysulfides which are covalently linked by Co2+ions. The ionically bound K+ions remain in the percolating pores of the Co–Mo–S covalent network. XANES of Co K‐edge shows multiple electronic transitions, including quadrupole (1s→3d), shakedown (1s→4p + MLCT), and dipole allowed 1s→4p transitions. Remarkably, despite a lack of regular channels as in some crystalline solids, the amorphous KCMS gel shows ion‐exchange properties with UO22+ions. Additionally, it also presents surface sorption via [S∙∙∙∙UO22+] covalent interactions. Overall, this study underscores the synthesis of quaternary chalcogels incorporating alkali metals and their potential to advance separation science for cations and oxo‐cationic species by integrating a synergy of surface sorption and ion‐exchange.more » « less
-
Fluorides are promising host materials for optical applications. This paper reports the photoluminescent (PL) and cathodoluminescent (CL) characteristics of barium hexafluorogermanate BaGeF 6 nanowires codoped with Ce 3+ , Tb 3+ and Sm 3+ rare earth ions, produced by a solvothermal route. The synthesized BaGeF 6 nanowires exhibit uniform morphology and size distribution. X-ray diffraction divulges the one-dimensional growth of crystalline BaGeF 6 structure, with the absence of any impurity phases. Visible luminescence is recorded from the nanowires in green and red regions, when the nanowires are codoped with Ce 3+ /Tb 3+ , and Ce 3+ /Tb 3+ /Sm 3+ , respectively, under a UV excitation source. The PL emission from the codoped BaGeF 6 nanowires, when excited by a 254 nm source, originates from the efficient energy transfer bridges between Ce 3+ , Tb 3+ and Sm 3+ ions. The decay time of the visible luminescent emission from the nanowires is in the order of subnanoseconds, being one of the shortest decay time records from inorganic scintillators. The CL emission from the BaGeF 6 nanowires in the tunable visible range reveals their potential use for the detection of high-energy radiation. The PL emissions are sensitive to H 2 O 2 at low concentrations, enabling their high-sensitivity detection of H 2 O 2 using BaGeF 6 nanowires. A comparison with BaSiF 6 nanowires is made in terms of decay time and its sensitivity towards H 2 O 2 .more » « less
-
Microstructural changes induced by helium implantation in materials lead to volumetric swelling and mechanical property changes. How these properties are linked and establishing direct relationships can be difficult due to the underlying material’s microstructure evolution. Some materials also experience a phase change due to irradiation damage making them even more complex to analyze. Here, single crystalline Si (100) was used to establish a relationship among these parameters. The swelling height as a function of implantation fluence can equally fit a linear relationship. Solely irradiation induced defects are observed at low fluence below 5.0 × 10 16 ions/cm 2 . An abrupt amorphous and crystalline mixed layer of ∼200 nm thick within a highly damaged polycrystalline matrix is observed when implantation fluence exceeds 5.0 × 10 16 ions/cm 2 , leading to the appearance of irradiation induced swelling and hardening behavior. As the fluence increases beyond 1.0 × 10 17 ions/cm 2 , the amorphous layer expands in size and the bubble size distribution takes the form of a Gaussian distribution with a maximum size of up to 6.4 nm, which causes a further increase in the height of swelling. Furthermore, irradiation induced softening appeared due to the enlarged bubble size and amorphization.more » « less
-
The zinc-ion battery (ZIB) has been a system of particular interest in the research community as a possible alternative to lithium-ion batteries (LIB), and much work has been devoted to finding a suitable host material. In this article, monoclinic V 2 (PO 4 ) 3 is investigated as a host material for reversible insertion of Zn 2+ . Initial chemical assessment via a facile microwave-assisted chemical insertion method indicates the possibility of Zn 2+ insertion into the host. Electrochemical assessment, however, exhibits a significant capacity fade. In-depth analysis on the average and local structure of Li 3 V 2 (PO 4 ) 3 , the empty host V 2 (PO 4 ) 3 , and the Zn-inserted V 2 (PO 4 ) 3 reveals that heavy distortion is induced upon Zn 2+ insertion into the V 2 (PO 4 ) 3 framework, which is believed to be a result of a strong host–guest interaction jeopardizing the structural integrity. This is further supported by the dissolution of most of the material during the chemical oxidation of the Zn-inserted V 2 (PO 4 ) 3 . The underlying structural inadequacy poses difficulties for monoclinic V 2 (PO 4 ) 3 to be a viable reversible host for Zn-ion batteries. This work suggests that not only the electrostatic repulsions of multivalent ions in a structure during diffusion, but also the structural stability of the host upon insertion of multivalent ions, must be considered for a better design of suitable host materials for multivalent-ion batteries.more » « less