Mixed metal oxyhalides are an exciting class of photocatalysts, capable of the sustainable generation of fuels and remediation of pollutants with solar energy. Bismuth oxyhalides of the types Bi4MO8X (M = Nb and Ta; X = Cl and Br) and Bi2AO4X (A = most lanthanides; X = Cl, Br, and I) have an electronic structure that imparts photostability, as their valence band maxima (VBM) are composed of O 2p orbitals rather than X np orbitals that typify many other bismuth oxyhalides. Here, flux-based synthesis of intergrowth Bi4NbO8Cl–Bi2GdO4Cl is reported, testing the hypothesis that both intergrowth stoichiometry and M identity serve as levers toward tunable optoelectronic properties. X-ray scattering and atomically resolved electron microscopy verify intergrowth formation. Facile manipulation of the Bi4NbO8Cl-to-Bi2GdO4Cl ratio is achieved with the specific ratio influencing both the crystal and electronic structures of the intergrowths. This compositional flexibility and crystal structure engineering can be leveraged for photocatalytic applications, with comparisons to the previously reported Bi4TaO8Cl–Bi2GdO4Cl intergrowth revealing how subtle structural and compositional features can impact photocatalytic materials.
more »
« less
Electronic and nanoscale structures of metal oxyhalide intergrowth photocatalysts
Multimetal oxyhalide intergrowths show promise for photocatalytic water splitting. However, the relationships between intergrowth stoichiometry and their electronic and nanoscale structures are yet to be identified. This study investigates Bi4TaO8Cl–Bi2GdO4Cl intergrowths and demonstrates that stoichiometry controls the tilting of [TaO6] octahedra, influencing the bandgap of the photocatalyst and its valence and conduction band positions. To determine how the [TaO6] octahedral tilting in the intergrowths manifests as a function of intergrowth stoichiometry, we investigated changes in crystal symmetry by analyzing features arising at the higher order Laue zone (HOLZ) of convergent-beam electron diffraction patterns. Higher Ta content intergrowths displayed a more intense outer HOLZ ring compared to lower Ta content intergrowths, indicating transformation from P21cn (orthorhombic) to P4/mmm (tetragonal). This finding suggests that more distortion occurs along the ⟨001⟩ directions of the crystal than the ⟨100⟩ and ⟨010⟩ directions. This variation directly impacts the electronic structure, affecting both conduction and valence band energy levels. By combining ultraviolet photoelectron spectroscopy, UV-visible diffuse reflectance spectroscopy, and electron energy loss spectroscopy, the absolute band positions of the intergrowths were determined. Agreement between the bandgaps obtained via ensemble and nanoscale measurements indicates nanoscale homogeneity of the electronic structure. Overall, the integrated approach establishes that the bandgap energy increases with increasing Ta content, which is correlated with the crystal symmetry and [TaO6] octahedral tilting. Broadly, the modular nature of intergrowths provides building block layers to tune octahedral tilting within perovskite layers for manipulation of optoelectronic properties.
more »
« less
- Award ID(s):
- 2113536
- PAR ID:
- 10512680
- Publisher / Repository:
- AIP Publishing
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 123
- Issue:
- 15
- ISSN:
- 0003-6951
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
In this work, the local structures of durable, high-activity Bi 4 TaO 8 Cl–Bi 2 GdO 4 Cl intergrowth photocatalysts that were prepared in a molten flux are determined by pair distribution function analysis of X-ray total scattering data and correlated to their photocatalytic performance. This system gives understanding to how the local structure of photocatalysts can be manipulated controllably through incorporation of rigid and flexible layers via intergrowth formation to achieve high activity. This analysis revealed that the local symmetry and distortion of the [TaO 6 ] octahedra introduced through intergrowth formation and dictated by intergrowth stoichiometry correlate with their photocatalytic activity. That is, the greater the Ta–O–Ta bond angles, the higher the photocatalytic activity of a given intergrowth for the oxygen evolution reaction. Moreover, greater tilting of the [TaO 6 ] octahedra is associated with a larger band gap. This analysis was coupled with a structure mining approach to model the intergrowth structure by building supercells for refinement of the X-ray diffraction data. This analysis found that Ta- and Gd-domains are separated within the intergrowths, with large Gd-domains separated by small Ta-domains at high Gd% and the opposite for high Ta%. Taken together with Williamson–Hall analysis, our results highlight that the local structure of layered materials can be modulated through strain engineering enabled by the selection of rigid and flexible intergrowth layers, providing a new design pathway to high performance photocatalysts.more » « less
-
There is increasing interest in α-polytype Ga2O3 for power device applications, but there are few published reports on dielectrics for this material. Finding a dielectric with large band offsets for both valence and conduction bands is especially challenging given its large bandgap of 5.1 eV. One option is HfSiO4 deposited by atomic layer deposition (ALD), which provides conformal, low damage deposition and has a bandgap of 7 eV. The valence band offset of the HfSiO4/Ga2O3 heterointerface was measured using x-ray photoelectron spectroscopy. The single-crystal α-Ga2O3 was grown by halide vapor phase epitaxy on sapphire substrates. The valence band offset was 0.82 ± 0.20 eV (staggered gap, type-II alignment) for ALD HfSiO4 on α-Ga0.2O3. The corresponding conduction band offset was −2.72 ± 0.45 eV, providing no barrier to electrons moving into Ga2O3.more » « less
-
The prospect of creating ferroelectric or high permittivity nanomaterials provides motivation for investigating complex transition metal oxides of the form Ba(Ti, MV)O3, where M = Nb or Ta. Solid state processing typically produces mixtures of crystalline phases, rarely beyond minimally doped Nb/Ta. Using a modified sol-gel method, we prepared single phase nanocrystals of Ba(Ti, M)O3. Compositional and elemental analysis puts the empirical formulas close to BaTi0.5Nb0.5O3−δ and BaTi0.5Ta0.5O3−δ. For both materials, a reversible temperature dependent phase transition (non-centrosymmetric to symmetric) is observed in the Raman spectrum in the region 533–583 K (260–310 °C); for Ba(Ti, Nb)O3, the onset is at 543 K (270 °C); and for Ba(Ti, Ta)O3, the onset is at 533 K (260 °C), which are comparable with 390–393 K (117–120 °C) for bulk BaTiO3. The crystal structure was resolved by examination of the powder x-ray diffraction and atomic pair distribution function (PDF) analysis of synchrotron total scattering data. It was postulated whether the structure adopted at the nanoscale was single or double perovskite. Double perovskites (A2B′B″O6) are characterized by the type and extent of cation ordering, which gives rise to higher symmetry crystal structures. PDF analysis was used to examine all likely candidate structures and to look for evidence of higher symmetry. The feasible phase space that evolves includes the ordered double perovskite structure Ba2(Ti, MV)O6 (M = Nb, Ta) Fm-3m, a disordered cubic structure, as a suitable high temperature analog, Ba(Ti, MV)O3Pm-3m, and an orthorhombic Ba(Ti, MV)O3Amm2, a room temperature structure that presents an unusually high level of lattice displacement, possibly due to octahedral tilting, and indication of a highly polarized crystal.more » « less
-
Introducing Cd into ZnO allows for bandgap engineering, potentially with particularly interesting properties to observe in compositionally graded samples. In this work, compositionally graded Zn1–xCdxO samples with 0x<0.16 were made using metal organic vapour phase epitaxy. The chemical composition was studied using scanning transmission electron microscopy, while the band structure of the samples was investigated using a combination of cathodoluminescence spectroscopy and X-ray photoelectron spectroscopy (XPS). It is found that the reduction of the bandgap in our samples is caused by changes in the conduction band. The position of the Fermi level relative to the vacuum level, i.e., the workfunction, was also found to change upon addition of Cd, giving an apparent shift in the valence band when evaluated from the XPS valence spectra.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1063/5.0159761