Abstract Carrier mobility in doped conjugated polymers is limited by Coulomb interactions with dopant counterions. This complicates studying the effect of the dopant's oxidation potential on carrier generation because different dopants have different Coulomb interactions with polarons on the polymer backbone. Here, dodecaborane (DDB)‐based dopants are used, which electrostatically shield counterions from carriers and have tunable redox potentials at constant size and shape. DDB dopants produce mobile carriers due to spatial separation of the counterion, and those with greater energetic offsets produce more carriers. Neutron reflectometry indicates that dopant infiltration into conjugated polymer films is redox‐potential‐driven. Remarkably, X‐ray scattering shows that despite their large 2‐nm size, DDBs intercalate into the crystalline polymer lamellae like small molecules, indicating that this is the preferred location for dopants of any size. These findings elucidate why doping conjugated polymers usually produces integer, rather than partial charge transfer: dopant counterions effectively intercalate into the lamellae, far from the polarons on the polymer backbone. Finally, it is shown that the IR spectrum provides a simple way to determine polaron mobility. Overall, higher oxidation potentials lead to higher doping efficiencies, with values reaching 100% for driving forces sufficient to dope poorly crystalline regions of the film.
more »
« less
Photoexcited Polaron Relaxation as a Structurally Sensitive Reporter of Charge Trapping in a Conducting Polymer
Abstract Conjugated polymers (CPs) play a central role in electronic applications due to their easily tuned electronic and ionic conductivities via chemical or electrochemical doping. Although doping improves charge conduction by introducing high densities of carriers into the CP, the accompanying structural changes and their impact on carrier mobility remain elusive. Methods capable of probing carrier distributions and their dependence on polymer morphology are needed to better understand how to improve conductivity. Here, a transient absorption (TA) spectroscopy approach is demonstrated, capable of directly probing mobile and trapped carriers in doped CPs and that is also sensitive to polymer nanostructure by using a model polythiophene system with tuned crystallinity. Exciting polarons in the polymer films produces distinct photoinduced absorption signals in the near‐infrared spectrum that decay during the picosecond timescale in the form of biphasic, stretched exponential kinetics, which reflect a distribution of mobile (free) and trapped polarons. The kinetic analysis provides evidence for mobile polarons irrespective of polymer film crystallinity, whereas polarons located in impure amorphous phases with reduced chain ordering exist within a deeper distribution of trap states. Altogether, these observations suggest a stronger correlation of carrier trapping with local chain ordering (planarity or aggregation) rather than polymer crystallinity.
more »
« less
- Award ID(s):
- 2018794
- PAR ID:
- 10513548
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 34
- Issue:
- 46
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract The relaxation of photoexcited polarons in doped conjugated polymers is studied with ultrafast transient absorption (TA) spectroscopy to examine the effect of polymer morphology and counterion size on polaron mobility. Processing conditions are first used to create F4TCNQ‐doped (2,3,5,6‐tetrafluoro‐tetracyanoquinodimethane) poly(3‐hexylthiophene‐2,5‐diyl) (P3HT) films with different morphologies and thus free and trapped polarons in different ratios. We find that less crystalline films have a higher fraction of trapped polarons, but, remarkably, that free and trapped polarons have the same relaxation times in all films. Films doped with a large dodecaborane (DDB) cluster‐based dopant are then used to show that trapping is based on Coulomb interactions between polarons and counterions; no trapped polarons are observed in TA due to the reduced Coulomb interaction between the polarons and the DDB counterion. Indeed, the relaxation of polarons in these films is an order of magnitude faster than that in F4TCNQ‐doped films, consistent with reduced trapping. Finally, the results are used to argue that counterion size has a greater effect on polaron mobility than polymer morphology and crystallinity. All of the experiments show that pump/probe spectroscopy provides a straightforward way to determine the local mobilities and degree of carrier trapping in doped conjugated polymer films.more » « less
-
Abstract Semiconducting polymers are of interest due to their solution processibility and broad electronic applications. Electrochemistry allows these wide bandgap semiconductors to be converted to conducting polymers by doping such polymers at various potentials. When polymers arep‐doped to improve their conductivity via electrochemical oxidation, various positively‐charged carriers are created, including polarons (singly‐charged) and bipolarons (doubly‐charged). Carrier creation is accompanied by anion intercalation from the electrolyte for charge balance, and this insertion requires ion mobility. In this work, poly(3‐hexylthiophene) (P3HT) with different regioregularities is used to understand the relationship between solvent swelling, which affects anion intercalation, and electrochemical doping. Cyclic voltammetry, optical absorption spectroscopy, and grazing incidence wide‐angle X‐ray scattering (GIWAXS) measurements are used to correlate the doping level with structural changes. In situ electrochemical quartz crystal microbalance (EQCM) measurements are used to quantify the swelling of the polymers dynamically during electrochemical cycling. Lastly, in situ conductivity measurements are done to measure the effect of swelling on the ionic and electronic conductivity. The results indicate that solvent swelling is required for bipolaron formation, and that swelling facilitates both the small structural changes need for polaron formation and the disordering required for bipolaron formation.more » « less
-
The electrochemical doping/dedoping kinetics, and the organic electrochemical transistor (OECT) performance of a series of polythiophene homopolymers with ethylene glycol units in their side chains using both kosmotropic and chaotropic anion solutions were studied. We compare their performance to a reference polymer, the polythiophene derivative with diethylene glycol side chains, poly(3-{[2-(2-methoxyethoxy)ethoxy]methyl}thiophene-2,5-diyl) (P3MEEMT). We find larger OECT material figure of merit, μC *, where μ is the carrier mobility and C * is the volumetric capacitance, and faster doping kinetics with more oxygen atoms on the side chains, and if the oxygen atom is farther from the polythiophene backbone. Replacing the oxygen atom close to the polythiophene backbone with an alkyl unit increases the film π-stacking crystallinity (higher electronic conductivity in the undoped film) but sacrifices the available doping sites (lower volumetric capacitance C * in OECT). We show that this variation in C * is the dominant factor in changing the μC * product for this family of polymers. With more oxygen atoms on the side chain, or with the oxygen atom farther from the polymer backbone, we observe both more passive swelling and higher C *. In addition, we show that, compared to the doping speed, the dedoping speed, as measured via spectroelectrochemistry, is both generally faster and less dependent on ion species or side chain oxygen content. Last, through OECT, electrochemical impedance spectroscopy (EIS) and spectroelectrochemistry measurements, we show that the chaotropic anion PF 6 − facilitates higher doping levels, faster doping kinetics, and lower doping thresholds compared to the kosmotropic anion Cl − , although the exact differences depend on the polymer side chains. Our results highlight the importance of balancing μ and C * when designing molecular structures for OECT active layers.more » « less
-
Abstract When an electron is removed from a conjugated polymer, such as poly(3‐hexylthiophene‐2,5‐diyl) (P3HT), the remaining hole and associated change in the polymer backbone structure from aromatic to quinoidal are referred to as a polaron. Bipolarons are created by removing the unpaired electron from an already‐oxidized polymer segment. In electrochemically‐doped P3HT films, polarons, and bipolarons are readily observed, but in chemically‐doped P3HT films, bipolarons rarely form. This is explained by studying the effects of counterion position on the formation of polarons, strongly coupled polarons, and bipolarons using both spectroscopic and X‐ray diffraction experiments and time‐dependent density functional theory calculations. The counterion positions control whether two polarons spin‐pair to form a bipolaron or whether they strongly couple without spin‐pairing are found. When two counterions lie close to the same polymer segment, bipolarons can form, with an absorption spectrum that is blueshifted from that of a single polaron. Otherwise, polarons at high concentrations do not spin‐pair, but insteadJ‐couple, leading to a redshifted absorption spectrum. The counterion location needed for bipolaron formation is accompanied by a loss of polymer crystallinity. These results explain the observed formation order of single polarons, coupled single polarons, and singlet bipolarons in electrochemically‐ and chemically‐doped conjugated polymers.more » « less