Abstract Additive Friction stir deposition (AFSD) has been extensively utilized for processing Al alloys. The properties of the Al depositions under as-fabricated state, including mechanical strength and corrosion resistance, are typically inferior compared to the base material, especially for heat-treatable alloys. In this research, multilayers of Al7075 composites, reinforced by ceramic particles, were processed by AFSD to evaluate the effect of using feedstock materials containing reinforcing particles on the properties of the deposition. For comparison, a bare Al7075 part was also processed by AFSD under the same conditions. The results of mechanical testing revealed a significant reduction in the microhardness, tensile strength and compression stress of the bare alloy after deposition. However, the composite deposition exhibited only a slight decrease in the properties compared to its feedstock material. Additionally, the corrosion resistance of the composite enhanced after AFSD, in contrast to the bare alloy, where the corrosion resistance deteriorated. Microstructural analysis showed a uniform distribution of the reinforcing particles in the matrix for the deposition, closely resembling that of the feedstock composite. This, along with grain refinement and minimal change in precipitates, were the reasons for the minimum changes in mechanical properties, as well as the improvement in corrosion resistance.
more »
« less
The Effects of Layer Thickness on the Mechanical Properties of Additive Friction Stir Deposition-Fabricated Aluminum Alloy 6061 Parts
Solid-state additive friction stir deposition (AFSD) is a thermomechanical-based additive manufacturing technique. For this study, AFSD was utilized to produce aluminum alloy 6061 (AA6061) blocks with varying layer thicknesses (1 mm, 2 mm, and 3 mm). The mechanical properties were assessed through uniaxial tensile tests and Vickers microhardness measurement, and statistical analysis was employed to investigate differences among data groups. The results revealed that the deposition layer thickness influences tensile properties in the building (Z) direction, while the properties in the X and Y directions showed minor differences across the three AFSD blocks. Furthermore, variations in tensile properties were observed depending on the sample orientation in the AFSD blocks and its depth-wise position in the part in the building direction. The microhardness values decreased non-linearly along the building direction, spread across the width of the part’s cross-section, and highlighted that the deposition layer thickness significantly affects this property. The 1 mm block exhibited lower average microhardness values than the 2 mm and 3 mm blocks. The temperature histories and dynamic heat treatment are influenced by the deposition layer thickness and depend on the location of the point being studied in the part, resulting in variations in the microstructure and mechanical properties along the building direction and across the part’s width.
more »
« less
- PAR ID:
- 10518719
- Publisher / Repository:
- MDPI
- Date Published:
- Journal Name:
- Metals
- Volume:
- 14
- Issue:
- 1
- ISSN:
- 2075-4701
- Page Range / eLocation ID:
- 101
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The solid-state additive friction stir deposition (AFSD) process is a layer-by-layer metal 3D-printing technology. In this study, AFSD is used to fabricate Al–Cu–Li 2050 alloy parts. The hardness values for various regions of the as-deposited built parts are measured, and the results are contrasted with those of the feedstock material. The as-fabricated Al2050 parts are found to have a unique hardness distribution due to the location-specific variations in the processing temperature profile. The XRD results indicate the presence of the secondary phases in the deposited parts, and EDS mapping confirms the formation of detectable alloying particles in the as-deposited Al2050 matrix. The AFSD thermal–mechanical process causes the unique hardness distribution and the reduced microhardness level in the AFSD components, in contrast to those of the feedstock material.more » « less
-
Abstract Additive friction stir deposition (AFSD) is a novel additive manufacturing technique that enables the fabrication of components in the solid state. Given the benefits of AFSD, understanding the behavior of various feedstock materials after undergoing the AFSD process is crucial for optimizing their performance in structural applications. This study aims to evaluate the effects of AFSD on an Al–Mg alloy, Al5086, comparing it to its initial H32 condition to assess the changes in mechanical properties, microstructure, corrosion resistance, microhardness, and electrical conductivity. Tensile testing showed a 23% reduction in yield strength for as-deposited samples, while ultimate tensile strength remained comparable to the feedstock. Ductility improved significantly, with elongation to failure increasing by 77%, attributed to grain refinement and dynamic recovery. Microhardness decreased by 16% in lower layers due to thermal exposure, but electrical conductivity remained stable, indicating minimal solute atom redistribution. The Nitric Acid Mass Loss Test (NAMLT) revealed a 245% increase in corrosion rate for the AFSD material, linked to the higher density of grain boundaries acting as pathways for corrosion. These findings highlight AFSD’s potential for improving ductility and formability. However, they underscore the need for optimization to reduce corrosion susceptibility and address mechanical strength trade-offs. Future work should focus on fine-tuning process parameters or implementing post-treatment methods to enhance corrosion and mechanical performance.more » « less
-
Abstract Fused deposition modeling (FMD) is considered one of the most common additive manufacturing methods for creating prototypes and small functional parts. Many researchers have studied Polylactic acid (PLA), Polycarbonate (PC), and Acrylonitrile butadiene styrene (ABS) as a material for fused deposition modeling printing. Among them, Polylactic Acid (PLA) is considered one of the most popular thermoplastic materials due to its low cost and biodegradable properties. In this study, silk PLA material was used. In Fused deposition modeling (FMD), the selection of printing parameters plays a pivotal role in determining the overall quality and integrity of the 3D-printed products. These parameters significantly influence the quality and strength of 3-D printed products. This study investigates the mechanical properties of silk-PLA printed specimens under different printing conditions, such as layer thickness, nozzle temperature, and print speed. All the tensile specimens were tested using ASTM D638 to characterize Young’s modulus and ultimate tensile strength. The thickness of the layers of tensile specimens was set to 0.1 mm, 0.15 mm, and 0.2 mm. The temperatures of the nozzle used during printing varied from 200°C, 210°C, and 220°C, whereas print speeds of 100 mm/s, 120 mm/s, and 140 mm/s were considered. The other printing parameters were kept consistent for all specimens. The result indicates tensile strength generally increases with increasing temperature of the nozzle, up to 220°C; however, a decline was observed in the average Young’s modulus value when the thickness of the layer increased from 0.10 mm to 0.20 mm. According to the results of the ANOVA analysis, the interaction between layer thickness, nozzle temperature, and printing speed significantly affects the tensile strength and Young’s modulus of Silk-PLA. This study reveals that nozzle temperature is the most critical parameter regarding the ultimate tensile strength and Young’s modulus, providing crucial insights for optimizing 3D printing parameters.more » « less
-
This study aims to investigate surface roughness, microstructure, and mechanical properties of overhead thin-wall structures of stainless steel(SS316L) fabricated by cold metal transfer (CMT)-based wire + arc additive manufacturing (WAAM). In the first stage, single-layer bead experiments were carried out in flat and overhead positions utilizing Box-Behnken experimental design with a range of process parameters (i.e., wire feed rate, travel speed, and weave amplitude). To study the effect of individual process parameters on the bead geometry and identify a process window, analysis of variance(ANOVA) is performed using the bead cross-section measurement data. For single layer bead experiments in flat and overhead position, out of all process parameters, the weave amplitude is the most significant parameter on bead width, whereas travel speed is most significant parameter for bead height. Based on single-layer bead experiments, process parameters for thin wall deposition were identified. In the second stage, two thin-walls were deposited with wire feed rates of 1000 and 1500 mm/min in the overhead position. The surface roughness was measured using cloud point data acquired from the coordinate measuring machine(CMM). The deposited structure with the wire feed rate of 1500 mm/min resulted in better surface quality. It was also observed that, microstructure was composed of austenite and dendritic delta ferrite. The microstructure changed as the deposition height increased. The average microhardness value was measured 183 HV and 187.4 HV for the overhead structures. Average tensile properties of the SS316L overhead structures were comparable to that of SS316L fabricated by other WAAM processes.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.3390/met14010101