skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Band-engineered LaFeO3–LaNiO3 thin film interfaces for electrocatalysis of water
Iron and nickel-based perovskite oxides have proven promising for the oxygen evolution reaction (OER) in alkaline environments, as their catalytic overpotentials rival precious metal catalysts when the band alignment is tuned through substitutional doping or alloying. Here, we report the engineering of band alignment in LaFeO3/LaNiO3 (LFO/LNO) heterostructures via interfacial doping that yields greatly enhanced catalytic performance. The 0.2 eV offset (VBO) between the Fermi level in metallic LNO and the valence band in semiconducting LFO that we predict using density functional theory makes LFO a p-type semiconductor, resulting in significantly lower barriers for hole transport through LFO compared to the intrinsic material. Experimental band alignment measured with in situ x-ray photoelectron spectroscopy of epitaxial LFO/LNO heterostructures confirms these predictions, producing a measured VBO of 0.3(1) eV. Furthermore, OER catalytic measurements on these samples in the alkaline solution show an increase in catalytic current density by a factor of ∼275 compared to LFO grown on n-type Nb-doped SrTiO3. These results demonstrate the power of tuning band alignments through interfacial band engineering for improved catalytic performance of oxides.  more » « less
Award ID(s):
1848344
PAR ID:
10519477
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
AIP Publishing LLC
Date Published:
Journal Name:
Journal of Vacuum Science & Technology A
Volume:
41
Issue:
6
ISSN:
0734-2101
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; (, Journal of Materials Chemistry A)
    Transition metal oxides have long been an area of interest for water electrocatalysis through the oxygen evolution and oxygen reduction reactions. Iron oxides, such as LaFeO 3 , are particularly promising due to the favorable energy alignment of the valence and conduction bands comprised of Fe 3+ cations and the visible light band gap of such materials. In this work, we examine the role of band alignment on the electrocatalytic oxygen evolution reaction (OER) in the intrinsic semiconductor LaFeO 3 by growing epitaxial films of varying thicknesses on Nb-doped SrTiO 3 . Using cyclic voltammetry, we find that there is a strong thickness dependence on the efficiency of electrocatalysis for OER. These measurements are understood based on interfacial band alignment in the system as well as catalytically active surface defect states as confirmed by layer-resolved electron energy loss spectroscopy, electrochemical impedance spectroscopy, and Mott–Schottky measurements. Our results demonstrate the importance of band engineering for the rational design of thin film electrocatalysts for renewable energy sources. 
    more » « less
  2. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Functional Materials)
    Abstract Van der Waals (vdW) heterostructures of 2D atomically thin layered materials (2DLMs) provide a unique platform for constructing optoelectronic devices by staking 2D atomic sheets with unprecedented functionality and performance. A particular advantage of these vdW heterostructures is the energy band engineering of 2DLMs to achieve interlayer excitons through type‐II band alignment, enabling spectral range exceeding the cutoff wavelengths of the individual atomic sheets in the 2DLM. Herein, the high performance of GaTe/InSe vdW heterostructures device is reported. Unexpectedly, this GaTe/InSe vdWs p–n junction exhibits extraordinary detectivity in a new shortwave infrared (SWIR) spectrum, which is forbidden by the respective bandgap limits for the constituent GaTe (bandgap of ≈1.70 eV in both the bulk and monolayer) and InSe (bandgap of ≈1.20–1.80 eV depending on thickness reduction from bulk to monolayer). Specifically, the uncooled SWIR detectivity is up to ≈1014Jones at 1064 nm and ≈1012Jones at 1550 nm, respectively. This result indicates that the 2DLM vdW heterostructures with type‐II band alignment produce an interlayer exciton transition, and this advantage can offer a viable strategy for devising high‐performance optoelectronics in SWIR or even longer wavelengths beyond the individual limitations of the bandgaps and heteroepitaxy of the constituent atomic layers. 
    more » « less
  3. ; ; ; ; ; ; ; ; ; ; et al (, Journal of Vacuum Science & Technology A)
    There is increasing interest in the alpha polytype of Ga2O3 because of its even larger bandgap than the more studied beta polytype, but in common with the latter, there is no viable p-type doping technology. One option is to use p-type oxides to realize heterojunctions and NiO is one of the candidate oxides. The band alignment of sputtered NiO on α-Ga2O3 remains type II, staggered gap for annealing temperatures up to 600 °C, showing that this is a viable approach for hole injection in power electronic devices based on the alpha polytype of Ga2O3. The magnitude of both the conduction and valence band offsets increases with temperature up to 500 °C, but then is stable to 600 °C. For the as-deposited NiO/α-Ga2O3 heterojunction, ΔEV = −2.8 and ΔEC = 1.6 eV, while after 600 °C annealing the corresponding values are ΔEV = −4.4 and ΔEC = 3.02 eV. These values are 1−2 eV larger than for the NiO/β-Ga2O3 heterojunction. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; (, ECS Journal of Solid State Science and Technology)
    The band alignment of Atomic Layer Deposited SiO2on (InxGa1−x)2O3at varying indium concentrations is reported before and after annealing at 450 °C and 600 °C to simulate potential processing steps during device fabrication and to determine the thermal stability of MOS structures in high-temperature applications. At all indium concentrations studied, the valence band offsets (VBO) showed a nearly constant decrease as a result of 450 °C annealing. The decrease in VBO was −0.35 eV for (In0.25Ga0.75)2O3, −0.45 eV for (In0.42Ga0.58)2O3, −0.40 eV for (In0.60Ga0.40)2O3, and −0.35 eV (In0.74Ga0.26)2O3for 450 °C annealing. After annealing at 600 °C, the band alignment remained stable, with <0.1 eV changes for all structures examined, compared to the offsets after the 450 °C anneal. The band offset shifts after annealing are likely due to changes in bonding at the heterointerface. Even after annealing up to 600 °C, the band alignment remains type I (nested gap) for all indium compositions of (InxGa1−x)2O3studied. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; (, Nature Communications)
    Abstract Developing stable and efficient electrocatalysts is vital for boosting oxygen evolution reaction (OER) rates in sustainable hydrogen production. High-entropy oxides (HEOs) consist of five or more metal cations, providing opportunities to tune their catalytic properties toward high OER efficiency. This work combines theoretical and experimental studies to scrutinize the OER activity and stability for spinel-type HEOs. Density functional theory confirms that randomly mixed metal sites show thermodynamic stability, with intermediate adsorption energies displaying wider distributions due to mixing-induced equatorial strain in active metal-oxygen bonds. The rapid sol-flame method is employed to synthesize HEO, comprising five 3d-transition metal cations, which exhibits superior OER activity and durability under alkaline conditions, outperforming lower-entropy oxides, even with partial surface oxidations. The study highlights that the enhanced activity of HEO is primarily attributed to the mixing of multiple elements, leading to strain effects near the active site, as well as surface composition and coverage. 