Sulfur cements have drawn significant attention as binders because sulfur is a byproduct of fossil fuel refining. Sulfur cements that can be formed by the vulcanization of elemental sulfur and plant-derived olefins such as terpenoids are particularly promising from a sustainability standpoint. A range of terpenoid–sulfur cements have shown compressional and flexural properties exceeding those of some commercial structural mineral cements. Pozzolans such as fly ash (FA), silica fume (SF), and ground granulated blast furnace slag (GGBFS) and abundant clay resources such as metakaolin (MK) are attractive fines for addition to binders. Herein, we report 10 composites prepared by a combination of sulfur, terpenoids (geraniol or citronellol), and these pozzolans. This study reveals the extent to which the addition of the pozzolan fines to the sulfur–terpenoid cements influences their mechanical properties and chemical resistance. The sulfur–terpenoid composites CitS and GerS were prepared by the reaction of 90 wt% sulfur and 10 wt% citronellol or geraniol oil, respectively. The density of the composites fell within the range of 1800–1900 kg/m3 and after 24 h submersion in water at room temperature, none of the materials absorbed more than 0.7 wt% water. The compressional strength of the as-prepared materials ranged from 9.1–23.2 MPa, and the percentage of compressional strength retained after acid challenge (submersion in 0.1 M H2SO4 for 24 h) ranged from 80–100%. Incorporating pozzolan fines into the already strong CitS (18.8 MPa) had negligible effects on its compressional strength within the statistical error of the measurement. CitS-SF and CitS-MK had slightly higher compressive strengths of 20.4 MPa and 23.2 MPa, respectively. CitS-GGBFS and CitS-FA resulted in slightly lower compressive strengths of 17.0 MPa and 15.8 MPa, respectively. In contrast, the compressional strength of initially softer GerS (11.7 MPa) benefited greatly after incorporating hard mineral fines. All GerS derivatives had higher compressive strengths than GerS, with GerS-MK having the highest compressive strength of 19.8 MPa. The compressional strengths of several of the composites compare favorably to those required by traditional mineral cements for residential building foundations (17 MPa), whereas such mineral products disintegrate upon similar acid challenge.
more »
« less
Upcycling mixed-material waste with elemental sulfur: applications to plant oil, unseparated biomass, and raw post-consumer food waste
Herein we report the preparation of high sulfur-content materials (HSMs) using food waste and elemental sulfur.
more »
« less
- Award ID(s):
- 2203669
- PAR ID:
- 10525346
- Publisher / Repository:
- Royal Society of Chemistry
- Date Published:
- Journal Name:
- RSC Sustainability
- Volume:
- 2
- Issue:
- 6
- ISSN:
- 2753-8125
- Page Range / eLocation ID:
- 1819 to 1827
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)A simple approach to a high sulfur-content material from biomass-derived guaiacol and waste sulfur is introduced. This direct reaction of elemental sulfur with an anisole derivative lacking olefins or halogen leaving groups expands the monomer scope beyond existing routes to high sulfur-content materials.more » « less
-
Lignin is the second-most abundant biopolymer in nature and remains a severely underutilized waste product of agriculture and paper production. Sulfur is the most underutilized byproduct of petroleum and natural gas processing industries. On their own, both sulfur and lignin exhibit very poor mechanical properties. In the current work, a strategy for preparing more durable composites of sulfur and lignin, LSx , is described. Composites LSx were prepared by reaction of allyl lignin with elemental sulfur, whereby some of the sulfur forms polysulfide crosslinks with lignin to yield a three-dimensional network. Even relatively small quantities (<5 wt%) of the polysulfide-crosslinked lignin network provides up to a 3.4-fold increase in mechanical reinforcement over sulfur alone, as measured by the storage moduli and flexural strength determined from dynamic mechanical analysis (temperature dependence and stress–strain analysis). Notably, LSx composites could be repeatedly remelted and recast after pulverization without loss of mechanical strength. These initial studies suggest potential practical applications of lignin and sulfur waste streams in the ongoing quest towards more sustainable, recyclable structural materials.more » « less
-
Abstract Poly(methyl methacrylate) (PMMA) is an important commodity polymer having a wide range of applications. Currently, only about 10% of PMMA is recycled. Herein, a simple two‐stage process for the chemical upcycling of PMMA is discussed. In this method PMMA is modified by transesterification with a bio‐derived, olefin‐bearing terpenoid, geraniol. In the second stage, olefin‐derivatized PMMA is reacted with sulfur to form a network composite by an inverse vulcanization mechanism. Inverse vulcanization of PGMA with elemental sulfur (90 wt.%) yielded the durable compositePGMA‐S. This composite was characterized by NMR spectrometry, IR spectroscopy, elemental analysis, thermogravimetric analysis, and differential scanning calorimetry. Composite water uptake, compressional strength analysis, flexural strength analysis, tensile strength analysis, and thermal recyclability are presented with comparison to current commercial structural materials.PGMA‐Sexhibits a similar compressive strength (17.5 MPa) to that of Portland cement.PGMA‐Sdemonstrates an impressive flexural strength of 4.76 MPa which exceeds the flexural strength (>3 MPa) of many commercial ordinary Portland cements. This study provides a way to upcycle waste PMMA through combination with a naturally‐occurring olefin and industrial waste sulfur to yield composites having mechanical properties competitive with ecologically detrimental legacy building materials.more » « less
-
ABSTRACT Sulfur and oleic acid, two components of industrial waste/byproducts, were combined in an effort to prepare more sustainable polymeric materials. Zinc oxide was employed to serve the dual role of compatibilizing immiscible sulfur and oleic acid as well as to suppress evolution of toxic H2S gas during reaction at high temperature. The reaction of sulfur, oleic acid, and zinc oxide led to a series of composites,ZOSx(x= wt % sulfur, wherexis 8–99). TheZOSxmaterials ranged from sticky tars to hard solids at room temperature. TheZOSxcompositions were assessed by1H NMR spectrometry, FTIR spectroscopy, and elemental microanalysis. CopolymersZOS59‐99, were further analyzed for thermal and mechanical properties by thermogravimetric analysis, differential scanning calorimetry, and dynamic mechanical analysis. Remarkably, evenZOS99, comprising only 1 wt % of zinc oxide/oleic acid (99 wt % S) exhibits at least an eightfold increase in storage modulus compared to sulfur alone. The four solid samples (59–99 wt % S) were thermally healable and readily remeltable with full retention of mechanical durability. These materials represent a valuable proof‐of‐concept for sustainably sourced, recyclable materials from unsaturated fatty acid waste products. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 1704–1710more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/D4SU00104D