Systematic investigations of electronic energy loss (Se) effects on pre-existing defects in crystalline silicon (Si) are crucial to provide reliance on the use of ionizing irradiation to anneal pre-existing defects, leading to successful implementation of this technology in the fabrication of Si-based devices. In this regard, the Se effects on nonequilibrium defect evolution in pre-damaged Si single crystals at 300 K has been investigated using intermediate-energy ions (12 MeV O and Si ions) that interact with the pre-damaged surface layers of Si mainly by ionization, except at the end of their range where the nuclear energy loss (Sn) is no longer negligible. Under these irradiation conditions, experimental results and molecular dynamics simulations have revealed that pre-existing disorder in Si can be almost fully annealed by subsequent irradiation with intermediate-energy incident ions with Se values as low as 1.5 - 3.0 keV/nm. Selective annealing of pre-existing defect levels in Si at room temperature can be considered as an effective strategy to mediate the transient enhanced diffusion of dopants in Si. This approach is more desirable than the regular thermal annealing, which is not compatible with the processing requirements that fall below the typical thermal budget.
more »
« less
Ion velocity effect governs damage annealing process in defective KTaO 3
Abstract Effects of electronic to nuclear energy losses (Se/Sn) ratio on damage evolution in defective KTaO3have been investigated by irradiating pre-damaged single crystal KTaO3with intermediate energy O ions (6 MeV, 8 MeV and 12 MeV) at 300 K. By exploring these processes in pre-damaged KTaO3containing a fractional disorder level of 0.35, the results demonstrate the occurrence of a precursory stage of damage production before the onset of damage annealing process in defective KTaO3that decreases with O ion energy. The observed ionization-induced annealing process by ion channeling analysis has been further mirrored by high resolution transmission electron microscopy analysis. In addition, the reduction of disorder level is accompanied by the broadening of the disorder profiles to greater depth with increasing ion fluence, and enhanced migration is observed with decreasing O ion energy. SinceSe(∼3.0 keV nm−1) is nearly constant for all 3 ion energies across the pre-damaged depth, the difference in behavior is due to the so-called ‘velocity effect’: the lower ion velocity below the Bragg peak yields a confined spread of the electron cascade and hence an increased energy deposition density. The inelastic thermal spike calculation has further confirmed the existence of a velocity effect, not previously reported in KTaO3or very scarcely reported in other materials for which the existence of ionization-induced annealing has been reported. In other words, understanding of ionization-induced annealing has been advanced by pointing out that ion velocity effect governs the healing of pre-existing defects, which may have significant implication for the creation of new functionalities in KTaO3through atomic-level control of microstructural modifications, but may not be limited to KTaO3.
more »
« less
- Award ID(s):
- 2104228
- PAR ID:
- 10544637
- Publisher / Repository:
- IOP Publishing
- Date Published:
- Journal Name:
- Journal of Physics D: Applied Physics
- Volume:
- 57
- Issue:
- 36
- ISSN:
- 0022-3727
- Format(s):
- Medium: X Size: Article No. 365303
- Size(s):
- Article No. 365303
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract 17 MeV proton irradiation at fluences from 3–7 × 1013cm−2of vertical geometry NiO/β-Ga2O3heterojunction rectifiers produced carrier removal rates in the range 120–150 cm−1in the drift region. The forward current density decreased by up to 2 orders of magnitude for the highest fluence, while the reverse leakage current increased by a factor of ∼20. Low-temperature annealing methods are of interest for mitigating radiation damage in such devices where thermal annealing is not feasible at the temperatures needed to remove defects. While thermal annealing has previously been shown to produce a limited recovery of the damage under these conditions, athermal annealing by minority carrier injection from NiO into the Ga2O3has not previously been attempted. Forward bias annealing produced an increase in forward current and a partial recovery of the proton-induced damage. Since the minority carrier diffusion length is 150–200 nm in proton irradiated Ga2O3, recombination-enhanced annealing of point defects cannot be the mechanism for this recovery, and we suggest that electron wind force annealing occurs.more » « less
-
Highly conductive Ge-doped AlN with conductivity of 0.3 (Ω cm)−1 and electron concentration of 2 × 1018 cm−3 was realized via a non-equilibrium process comprising ion implantation and annealing at a moderate thermal budget. Similar to a previously demonstrated shallow donor state in Si-implanted AlN, Ge implantation also showed a shallow donor behavior in AlN with an ionization energy ∼80 meV. Ge showed a 3× higher conductivity than its Si counterpart for a similar doping level. Photoluminescence spectroscopy indicated that higher conductivity for Ge-doped AlN was achieved primarily due to lower compensation. This is the highest n-type conductivity reported for AlN doped with Ge to date and demonstration of technologically useful conductivity in Ge-doped AlN.more » « less
-
We report the effect of extended duration electron beam exposure on the minority carrier transport properties of 10 MeV proton irradiated (fluence ∼1014cm−2) Si-dopedβ-Ga2O3Schottky rectifiers. The diffusion length (L) of minority carriers is found to decrease with temperature from 330 nm at 21 °C to 289 nm at 120 °C, with an activation energy of ∼26 meV. This energy corresponds to the presence of shallow Si trap-levels. Extended duration electron beam exposure enhancesLfrom 330 nm to 726 nm at room temperature. The rate of increase forLis lower with increased temperature, with an activation energy of 43 meV. Finally, a brief comparison of the effect of electron injection on proton irradiated, alpha-particle irradiated and a reference Si-dopedβ-Ga2O3Schottky rectifiers is presented.more » « less
-
Abstract Understanding the interplay between the inherent disorder and the correlated fluctuating-spin ground state is a key element in the search for quantum spin liquids. H3LiIr2O6is considered to be a spin liquid that is proximate to the Kitaev-limit quantum spin liquid. Its ground state shows no magnetic order or spin freezing as expected for the spin liquid state. However, hydrogen zero-point motion and stacking faults are known to be present. The resulting bond disorder has been invoked to explain the existence of unexpected low-energy spin excitations, although data interpretation remains challenging. Here, we use resonant X-ray spectroscopies to map the collective excitations in H3LiIr2O6and characterize its magnetic state. In the low-temperature correlated state, we reveal a broad bandwidth of magnetic excitations. The central energy and the high-energy tail of the continuum are consistent with expectations for dominant ferromagnetic Kitaev interactions between dynamically fluctuating spins. Furthermore, the absence of a momentum dependence to these excitations are consistent with disorder-induced broken translational invariance. Our low-energy data and the energy and width of the crystal field excitations support an interpretation of H3LiIr2O6as a disordered topological spin liquid in close proximity to bond-disordered versions of the Kitaev quantum spin liquid.more » « less