The continued development of metal additive manufacturing (AM) has expanded the engineering metallic alloys for which these processes may be applied, including beta-titanium alloys with desirable strength-to-density ratios. To understand the response of beta-titanium alloys to AM processing, solidification and microstructure evolution needs to be investigated. In particular, thermal gradients (Gs) and solidification velocities (Vs) experienced during AM are needed to link processing to microstructure development, including the columnar-to-equiaxed transition (CET). In this work, in situ synchrotron X-ray radiography of the beta-titanium alloy Ti-10V-2Fe-3Al (wt.%) (Ti-1023) during simulated laser-powder bed fusion (L-PBF) was performed at the Advanced Photon Source at Argonne National Laboratory, allowing for direct determination of Vs. Two different computational modeling tools, SYSWELD and FLOW-3D, were utilized to investigate the solidification conditions of spot and raster melt scenarios. The predicted Vs obtained from both pieces of computational software exhibited good agreement with those obtained from in situ synchrotron X-ray radiography measurements. The model that accounted for fluid flow also showed the ability to predict trends unobservable in the in situ synchrotron X-ray radiography, but are known to occur during rapid solidification. A CET model for Ti-1023 was also developed using the Kurz–Giovanola–Trivedi model, which allowed modeled Gs and Vs to be compared in the context of predicted grain morphologies. Both pieces of software were in agreement for morphology predictions of spot-melts, but drastically differed for raster predictions. The discrepancy is attributable to the difference in accounting for fluid flow, resulting in magnitude-different values of Gs for similar Vs.
more »
« less
Probing rapid solidification pathways in refractory complex concentrated alloys via multimodal synchrotron X-ray imaging and melt pool-scale simulation
Refractory complex concentrated alloys (RCCAs) show potential as the next-generation structural materials due to their superior strength in extreme environments. However, RCCAs processed by metal additive manufacturing (AM) typically suffer from process-related challenges surrounding laser material interaction defects and microstructure control. Multimodal
- PAR ID:
- 10553390
- Publisher / Repository:
- Cambridge University Press (CUP)
- Date Published:
- Journal Name:
- Journal of Materials Research
- ISSN:
- 0884-2914
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Energy efficiency is motivating the search for new high-temperature (high-T) metals. Some new body-centered-cubic (BCC) random multicomponent “high-entropy alloys (HEAs)” based on refractory elements (Cr-Mo-Nb-Ta-V-W-Hf-Ti-Zr) possess exceptional strengths at high temperatures but the physical origins of this outstanding behavior are not known. Here we show, using integrated in-situ neutron-diffraction (ND), high-resolution transmission electron microscopy (HRTEM), and recent theory, that the high strength and strength retention of a NbTaTiV alloy and a high-strength/low-density CrMoNbV alloy are attributable to edge dislocations. This finding is surprising because plastic flows in BCC elemental metals and dilute alloys are generally controlled by screw dislocations. We use the insight and theory to perform a computationally-guided search over 10 7 BCC HEAs and identify over 10 6 possible ultra-strong high-T alloy compositions for future exploration.more » « less
-
more » « less
Abstract Two advanced manufacturing processes, spark plasma sintering (SPS) and selective laser sintering (SLS), have been developed for synthesis of (Zr,Nb,Ta,Ti,W)C compositionally complex carbide (CCC) via reactive sintering of a powder mixture of constitute monocarbides. X‐ray diffraction analysis confirmed that the single‐phase CCC can be formed by both SPS and SLS. While a homogenous microstructure with uniform metal element distributions was developed during SPS, three‐layer microstructures with a thin TiC‐rich layer and two TaC‐rich layers along with a TiO2‐rich surface layer containing W nanoparticles were formed during SLS. In addition, cellular structures with W, Zr, and Ti element segregation and dislocations on cell boundaries were observed in the SLS‐CCC sample, indicating the effect of nonequilibrium conditions on microstructure formation during laser melting followed by rapid cooling and solidification process. Compared to the SPS‐CCC sample, the SLS‐CCC showed enhanced hardness and reduced thermal conductivity, which may be related to their unique cellular structures.
-
more » « less
Abstract The direct selective laser sintering (SLS) process was successfully demonstrated for additive manufacturing of high-entropy carbide ceramics (HECC), in which a Yb fiber laser was employed for ultrafast (in seconds) reactive sintering of HECC specimens from a powder mixture of constitute monocarbides. A single-phase non-equiatomic HECC was successfully formed in the 4-HECC specimen with a uniform distribution of Zr, Nb, Hf, Ta, and C. In contrast, a three-layer microstructure was formed in the 5-HECC specimen with five metal elements (Zr, Nb, Hf, Ta and Ti), consisting of a TiC-rich top layer, a Zr–Hf–C enriched intermediate layer, and a non-equiatomic Zr–Ta–Nb–Hf–C HECC layer. Vickers hardness of 4- and 5-HECC specimens were 22.2 and 21.8 GPa, respectively, on the surface. These findings have important implications on the fundamental mechanisms governing interactions between laser and monocarbide powders to form a solid solution of HECCs during SLS.
Graphical abstract -
Microstructures and Properties of the Low-Density Al15Zr40Ti28Nb12M(Cr, Mo, Si)5 High-Entropy AlloysLow-density materials show promising prospects for industrial application in engineering, and have remained a research hotspot. The ingots of Al15Zr40Ti28Nb12Cr5, Al15Zr40Ti28Nb12Mo5 and Al15Zr40Ti28Nb12Si5 high-entropy alloys were prepared using an arc melting method. With the addition of the Cr, Mo, and Si, the phase structures of these alloys changed to a dual phase. The Cr and Mo promote the formation of the B2 phase, while the Si promotes the formation of a large amount of the silicides. The compression yield strengths of these alloys are ~1.36 GPa, ~1.27 GPa, and ~1.35 GPa, respectively. The addition of Si and Cr significantly reduces the compression ductility, and the Al15Zr40Ti28Nb12SiMo5 high-entropy alloy exhibits excellent comprehensive mechanical properties. This work investigated the influence of Cr, Mo, and Si on the phase structures and properties of the low-density Al-Zr-Ti-Nb high-entropy alloys, providing theoretical and scientific support for the development of advanced low-density alloys.more » « less