skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Attention:

The NSF Public Access Repository (PAR) system and access will be unavailable from 11:00 PM ET on Friday, July 11 until 2:00 AM ET on Saturday, July 12 due to maintenance. We apologize for the inconvenience.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Effect of polyacid architecture and polycation molecular weight on lateral diffusion within multilayer films
Despite the potential use of polyelectrolyte multilayers for biomedical, separation, and energy applications, their dynamic properties are not sufficiently understood. In this work, center-of-mass diffusion of a weak polyacid—poly(methacrylic acid) (PMAA) of linear and 8-arm architecture (L-PMAA and 8-PMAA, respectively) and matched molecular weight—was studied in layer-by-layer (LbL) assemblies with poly(diallyldimethylammonium) chloride (PDADMAC) of varied molecular weight. The film deposition at low-salt, acidic conditions when PMAA was only partially ionized yielded thicker, more diffused layers with shorter PDADMAC chains, and bilayer thickness decreased for multilayers constructed with longer PDADMAC. The molecular architecture of PMAA had a weak effect on film growth, with bilayer thickness being ∼20% larger for L-PMAA for the films constructed with the shortest PDADMAC (35 kDa) and identical film growth for L-PMAA and 8-PMAA with the longest PDADMAC (300 kDa). The exposure of the multilayer films to 0.2M NaCl triggered a reduction in PMAA ionization and significant lateral diffusivity of fluorescently labeled PMAA molecules (PMAA*), with diffusion coefficients D ranging from 10−13 to 10−12 cm2/s, as determined by the fluorescence recovery after photobleaching technique. For all the films, polymer mobility was higher for star polyacids as compared to their linear counterparts, and the dependence of PMAA diffusion coefficient D on PDADMAC molecular weight (D ∼ M−n) was relatively weak (n < 0.6). However, 8-PMAA demonstrated an approximately doubled power exponent compared to the L-PMAA chains, suggesting a stronger effect of the molecular connectivity of the partner polycation molecules on the diffusion of star polyelectrolytes.  more » « less
Award ID(s):
1905535
PAR ID:
10557341
Author(s) / Creator(s):
; ; ;
Publisher / Repository:
AIP
Date Published:
Journal Name:
The Journal of Chemical Physics
Volume:
160
Issue:
12
ISSN:
0021-9606
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; (, Macromolecules)
    null (Ed.)
    Polymer chain diffusion within a hydrated polyelectrolyte complex, PEC, has been measured using an ultrathin film format prepared by the layer-by-layer method. Isotopically labeled self-exchange of deuterated poly(styrene sulfonate), dPSS, with undeuterated PSS of the same narrow molecular weight distribution permitted reliable estimates of whole-molecule diffusion coefficients, D. Narrow molecular weight distribution poly(diallyldimethylammonium), PDADMA, was used as the polycation for the PEC. Extensive pretreatment of starting films was undertaken to remove residual stress, anisotropy, and layering. PSS/PDADMA “multilayers,” PEMUs, thin enough to provide substantial exchange of polyelectrolyte, even with diffusion coefficients as low as 10–16 cm2 s–1, as a function of salt concentration and temperature were measured for this PEC, which has a glass-transition temperature, Tg, close to room temperature. Two molecular weights of dPSS, about 15 and 100 kDa, presumed to be below and above the entanglement molecular weight, respectively, both diffused faster at higher temperatures with respective activation energies, Ea, of about 21 and 53 kJ mol–1, the latter about the same as Ea for the place exchange between two pairs of PSS:PDADMA. Studies of the linear viscoelastic response of macroscopic PECs showed a difference of about 8 °C in the Tg of the two lengths of PSS complexed with the same PDADMA. Increasing concentrations of NaCl influenced D of 100 kDa PSS but not 15 kDa PSS at room temperature. D was faster in the region of the film near the solution interface, again attributed to a lower Tg caused by greater water content at this interface. 
    more » « less
  2. ; ; (, Macromolecular Rapid Communications)
    Abstract The effect of molecular architecture, star versus linear, poly(ethylene oxide) (PEO) on the formation of hydrogen‐bonded complexes with linear poly(methacrylic acid) (PMAA) is investigated experimentally and rationalized theoretically. Isothermal titration calorimetry reveals that at pH 2.5 interpolymer complexes (IPCs) of PMMA with a 6‐arm star PEO (sPEO) contains ≈50% more polyacid than IPCs formed with linear PEO (lPEO). While the enthalpy of IPC formation is positive in both cases, its magnitude is ≈50% larger forsPEO/PMAA complexes that exhibit a lower dissociation constant thanlPEO/polyacid complexes. These results are rationalized based on a higher localized density of hydrogen bonds formed betweensPEO and the polyacid which prevents penetration of star molecules into PMAA coils. Accordingly, Fourier transform infrared results indicate approximately twofold excess of self‐associated >COOH units over intermolecularly bonded >COOH units insPEO‐containing complexes. The excess of PMAA chains in IPCs and the percentage of self‐associated carboxylic groups insPEO/PMAA complexes both increase with polyacid molecular weight. Other findings, including a positive entropy, hysteresis in composition at strongly acidic pH, and progressive equilibration of IPCs at increased pH are consistent with the critical role of charge and release of water molecules in the formation ofsPEO/PMAA andlPEO/PMAA complexes. 
    more » « less
  3. ; ; ; ; (, Journal of Polymer Science)
    Abstract We developed the dynamic assembly of the hydrogen‐bonded multilayers of (poly(N‐vinylpyrrolidone/poly(methacrylic acid)) (PVPON/PMAA)) and compared their properties to the static multilayers. We found that dynamic multilayers, wherein a planar substrate is shaken during polymer adsorption, leads to a 15‐time faster deposition of the planar coatings. The thicknesses and roughness of the dynamic coatings were found to be ⁓30% larger than those of static (no shaking) multilayer films as measured by spectroscopic ellipsometry and atomic force microscopy. We examined the film growth, mechanical properties, wettability, hydration, and pH stability of the planar static and dynamic multilayers and demonstrated that these properties were insignificantly affected by the assembly mode. Both static and dynamic coatings produced microporous films when exposed to pH = 5.9, close to the film critical dissolution pH = 6. We discovered that during the release of the multilayer films into a solution to produce free‐standing films either as planar membranes or multilayer capsule shells, the molecular chain rearrangements result in the decreased roughness for both static and dynamic multilayers and lead to a decreased thickness of the dynamic multilayers. Our findings can help develop a rapid synthesis of thicker nanostructured polymer coatings for sensing and controlled delivery applications. 
    more » « less
  4. ; ; ; ; ; ; ; ; (, Physical Chemistry Chemical Physics)
    Charge densities of cationic polymers adsorbed to lipid bilayers are estimated from second harmonic generation (SHG) spectroscopy and quartz crystal microbalance with dissipation monitoring (QCM-D) measurements. The systems surveyed included poly(vinylamine hydrochloride) (PVAm), poly(diallyldimethylammonium chloride) (PDADMAC), poly- l -lysine (PLL), and poly- l -arginine (PLR), as well as polyalcohol controls. Upon accounting for the number of positive charges associated with each polyelectrolyte, the binding constants and apparent free energies of adsorption as estimated from SHG data are comparable despite differences in molecular masses and molecular structure, with Δ G ads values of −61 ± 2, −58 ± 2, −57 ± 1, −52 ± 2, −52 ± 1 kJ mol −1 for PDADMAC 400 , PDADMAC 100 , PVAm, PLL, and PLR, respectively. Moreover, we find charge densities for polymer adlayers of approximately 0.3 C m −2 for poly(diallyldimethylammonium chloride) while those of poly(vinylamine) hydrochloride, poly- l -lysine, and poly- l -arginine are approximately 0.2 C m −2 . Time-dependent studies indicate that polycation adsorption to supported lipid bilayers is only partially reversible for most of the polymers explored. Poly(diallyldimethylammonium chloride) does not demonstrate reversible binding even over long timescales (>8 hours). 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Electronic Materials)
    Abstract Polymer semiconductors (PSCs) are essential active materials in mechanically stretchable electronic devices. However, many exhibit low fracture strain due to their rigid chain conformation and the presence of large crystalline domains. Here, a PSC/elastomer blend, poly[((2,6‐bis(thiophen‐2‐yl)‐3,7‐bis(9‐octylnonadecyl)thieno[3,2‐b]thieno[2′,3′:4,5]thieno[2,3‐d]thiophene)‐5,5′‐diyl)(2,5‐bis(8‐octyloctadecyl)‐3,6‐di(thiophen‐2‐yl)pyrrolo[3,4‐c]pyrrole‐1,4‐dione)‐5,5′‐diyl]] (P2TDPP2TFT4) and polystyrene‐block‐poly(ethylene‐ran‐butylene)‐block‐polystyrene (SEBS) are systematically investigated. Specifically, the effects of molecular weight of both SEBS and P2TDPP2TFT4 on the resulting blend morphology, mechanical, and electrical properties are explored. In addition to commonly used techniques, atomic force microscopy‐based nanomechanical images are used to provide additional insights into the blend film morphology. Opposing trends in SEBS‐induced aggregation are observed for the different P2TDPP2TFT4 molecular weights upon increasing the SEBS molecular weight from 87 to 276 kDa. Furthermore, these trends are seen in device performance trends for both molecular weights of P2TDPP2TFT4. SEBS molecular weight also has a substantial influence on the mesoscale phase separation. Strain at fracture increases dramatically upon blending, reaching a maximum value of 640% ± 20% in the blended films measured with film‐on‐water method. These results highlight the importance of molecular weight for electronic devices. In addition, this study provides valuable insights into appropriate polymer selections for stretchable semiconducting thin films that simultaneously possess excellent mechanical and electrical properties. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email