Abstract The current code provisions in ACI 440.11 are based on the flexural theory that applies to slender members and may not represent the actual structural behavior when the shear span-to-reinforcement depth ratio is less than 2.5 (i.e., deep members). The Strut-and-tie method (STM) can be a better approach to design deep members; however, this chapter is not included in the code. Research has shown that STM models used for steel-reinforced concrete (RC) give satisfactory results when applied to glass fiber-reinforced polymer-reinforced (GFRP)-RC members with a/d less than 2.5. Therefore, this study is carried out to provide insights into the use of STM for GFRP-RC deep members based on the available literature and to highlight the necessity for the inclusion of a new chapter addressing the use of STM in the ACI 440.11 Code. It includes a design example to show the implications of ACI 440.11 code provisions when applied to GFRP-RC deep members (i.e., isolated footings) and compares it when designed as per STM provided in ACI 318-19. It was observed that current code provisions in ACI 440.11 required more concrete thickness (i.e.,h = 1.12 m) leading to implementation challenges. However, the required dimensions decreased (i.e.,h = 0.91 m) when the design was carried out as per STM. Due to the novelty of GFRP reinforcement, current code provisions may limit its extensive use in RC buildings, particularly in footings given the water table issues and excavation costs. Therefore, it is necessary to adopt innovative methods such as STM to design GFRP-RC deep members if allowed by the code.
more »
« less
Effect of GFRP Stirrup Confinement on the Bond Strength of GFRP-RC Beams
Abstract The current provisions for development length in the ACI 440.11 code disregard the confinement effect provided by stirrups on the bond strength of longitudinal bars and require splice lengths that pose implementation challenges. Given the significant improvement in GFRP material properties, this study investigated the bond strength of sand-coated GFRP bars and proposed a new factor to include the effect of stirrup confinement on the bond-strength provisions. The experimental program involved 16 GFRP-reinforced concrete (RC) beams having a width of 300 mm, and depth 440 mm, consisting of two repetitions for every configuration, subjected to four-point loading. The test parameters comprised lap-splice length and stirrup spacing in the lap-spliced zone. Out of 16 GFRP-RC beams, two beams were reinforced with two M16 (No. 5) continuous bars and six with varying lap-splice lengths [i.e., 40, 60, and 80 bar diameters (db)] without confining stirrups. To evaluate the effect of confining stirrups, eight beams were reinforced with two M16 (No. 5) lap-spliced longitudinal bars (i.e., 40 and 60 db) and M13 (No. 4) stirrups spaced at 100 mm (4 in.) and 200 mm (8 in.) center-to-center. Based on experimental results, stirrup confinement clearly increased the bond strength, reduced longitudinal bar slippage, and increased splitting stress. The beams with a splice length of 60 dband stirrups on 100 mm (4 in.) centers achieved 57% higher capacity than those with the same lap-splice length but without stirrups. Further, the ACI 440.11 equation overestimated the bond strength of sand-coated GFRP bars but yielded conservative results with closely spaced stirrups. CSA S6:25 predicted bond-strength values that were close to the experimental results compared to CSA S6:19, and CSA S806:12.
more »
« less
- Award ID(s):
- 1916342
- PAR ID:
- 10559628
- Publisher / Repository:
- Springer Science + Business Media
- Date Published:
- Journal Name:
- International Journal of Concrete Structures and Materials
- Volume:
- 18
- Issue:
- 1
- ISSN:
- 2234-1315
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Fiber reinforced polymer (FRP) waste is becoming an environmental concern due to the widespread use and non-biodegradable nature of FRP composites. Cutting FRP waste into discrete reinforce-ments (referred to as “needles” hereafter) as coarse aggregate in concrete has been suggested as a possible solution to FRP waste recycling. It has previously been observed in small specimens that FRP needles increase the tensile strength and energy absorption capacity of concrete. This paper presents an experimental investiga-tion into the effect of GFRP needles as coarse aggregate partial replacement in concrete on shear behavior of full-scale reinforced concrete (RC) beams. A total of 10 RC beams without steel stirrups in the critical zone were tested under four-point bending. The volume replacement ratio of the coarse aggregate and the surface type of GFRP needles were chosen as the test parameters. GFRP needles, with either smooth or helically wrapped surfaces, were added to the concrete mix to replace 5% or 10% of coarse aggregate by volume, respectively. All test beams failed in shear in a brittle manner with the ductility being slightly enhanced by the partial replace-ment of coarse aggregate using GFRP needles. An enhancement of 8%-10% in the load carrying capacity was observed in beams with helically wrapped needles, while beams with smooth needles showed a reduction in the load carrying capacity.more » « less
-
Abstract Glass fiber reinforced polymer (GFRP) bars are composite materials that, in the field of civil engineering, serve as an alternative for the internal steel reinforcement of concrete structures. The study and development of these material systems in construction are relatively new, requiring targeted research and development to achieve greater adoption. In this scenario, research and standardization play crucial roles. The development and publication of new test methods, material specifications, and other standards, as well as the improvement of the existing ones, allow for quality control, validation, and acceptance. One of these improvements is the evaluation of precision statements of the different ASTM standards related to the physical-mechanical and durability characterization of GFRP bars used as internal concrete reinforcement. Precision refers to how closely test results obtained under specific conditions agree with each other. A precision statement allows potential users to assess the test method’s general suitability for their intended applications. It should provide guidance on the type of variation that can be expected between test results when the method is used in one or more competent laboratories. The present study aims to enhance the precision statements in ASTM standards pertaining to the geometric, material, mechanical, and physical properties required for GFRP bars in concrete reinforcement, including ASTM standards like ASTM D7205M-21, Standard Test Method for Tensile Properties of Fiber Reinforced Polymer Matrix Composite Bars; ASTM D7617M-11(2017), Standard Test Method for Transverse Shear Strength of Fiber-Reinforced Polymer Matrix Composite Bars; and ASTM D7913M-14(2020), Standard Test Method for Bond Strength of Fiber-Reinforced Polymer Matrix Composite Bars to Concrete by Pullout Testing, while in accordance with the statistical procedures and calculation methods outlined in ASTM Practices ASTM E177-20, Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods, and ASTM E691-22, Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method.more » « less
-
This paper reports on a combined experimental and numerical modeling investigation of cracking of concrete slabs with GFRP reinforcement. At this stage of the project, attention is given to early-age cracking driven by plastic shrinkage, preceding longer term considerations of cracking resistance over the service life of field applications. Of interest is the effectiveness of GFRP reinforcement in restricting plastic shrinkage cracking. Nine small-scale slab specimens were subjected to controlled evaporation rates. Images of crack development were acquired periodically, from which crack width estimations were made. Comparisons were made between slabs reinforced with conventional steel and those reinforced with GFRP, along with control specimens lacking reinforcement. During the period of plastic shrinkage, the time of crack initiation and subsequent crack openings do not appear to be influenced by the presence of the reinforcing bars. To understand this behavior, six early-age bond tests were conducted for both types of the bars after 1, 2, and 3 h exposure to the controlled evaporation rate. In addition, concrete strength development and time of settings were measured using penetration resistance tests on a representative mortar. The numerical modeling component of this research is based on a Voronoi cell lattice model; in this approach, the relative humidity, temperature, and displacement fields are discretized in three-dimensions, allowing for a comprehensive investigation of material behavior within the controlled environment. Based on the measured bond properties, our simulations confirm that the reinforcing bars restrict crack development, though they do not prevent it entirely.more » « less
-
null (Ed.)Adequate rebar-concrete bonding is crucial to ensure the reliable performance of reinforced concrete (RC) structures. Many factors such as the concrete properties, concrete cover depth, transverse reinforcement, and the presence of corrosion will affect the bond behavior, and consequently, the structural performance. While many prior studies have focused on the influence of the aforementioned factors on the bond strength, the impact of these factors on the bond failure mode has not been thoroughly investigated. A probabilistic bond failure mode prediction model that considers various influencing factors including loading type and corrosion is developed in this study. This study uses the bond testing results of 132 beam-end specimens subjected to monotonic and cyclic loading and adopts classification methods to develop the prediction model, which is then used to evaluate the impact of bond behavior on the reliability of a RC beam with a lap splice.more » « less