The effect of olefin addition to a stream of dimethyl ether on the methanol homologation reaction is investigated using iron-substituted zeolites Fe-beta and Fe-ZSM-5. The reaction was investigated using plug-flow microreactors in the temperature range of 240-400 degrees C, at a total pressure of 0.239 MPa and a WHSV of 6.12 (g DME/ gcat-hr). For Fe-beta (Si/Fe= 9.2) catalysts, isobutene co-feeding almost doubles dimethyl ether (DME) consumption rate and shifts selectivity towards larger olefins with carbon numbers from 5 to 7. Addition of isobutene above 6.3%, however, resulted in a reduction of DME consumption rates, an effect assigned to the replacement of surface methoxy groups for adsorbed olefins in the zeolite pores. Below a temperature of 340 degrees C hydride-transfer rates are negligible; reaction rates are stable for over 5.5 h and the products consist almost exclusively of olefins and a small amount of methane. Above 360 degrees C the onset of catalytic hydride transfer processes is observed leading to fast catalyst deactivation rates and an increase in the concentration of aromatic species. Iron ZSM-5 (Si/Fe = 21.4) catalysts under similar reaction conditions consumes methanol faster than Febeta at approximately three times the TOF (on a per iron basis). The Fe-ZSM-5 catalyst was selective to a distribution of products (C5 to C8) as compared to Fe-beta which was selective to primarily C5 and C7. Co-feeding larger olefins (2-methyl-2-butene, 2,3-dimethyl-2-butene, 2,3,3-trimethyl-1-butene, and 2,4,4-trimethyl-2-pentene) at a 3.9% olefin concentration over Fe-beta changed selectivity towards cracking products (C4 compounds such as isobutene). As the size of the olefin increases, a reduction of DME consumption rate is also observed. These results show that co-feeding olefins with DME over Fe-zeolites is a promising route to increase methylation rates at relatively low temperatures producing larger branched olefins and that the product distribution is highly dependent on the zeolite pore size and structure of the olefin.
more »
« less
This content will become publicly available on January 1, 2026
Effect of pretreatment conditions on Fe-ZSM-5 properties and performance for Fischer–Tropsch synthesis
Our findings provide important insight into how pretreatment conditions on Fe-ZSM-5 affect iron particle size, phase, zeolite properties, and in turn, Fischer–Tropsch synthesis (FTS), guiding the selection of pretreatment conditions for Fe-ZSM-5.
more »
« less
- Award ID(s):
- 2345734
- PAR ID:
- 10560771
- Publisher / Repository:
- RSC
- Date Published:
- Journal Name:
- Catalysis Science & Technology
- ISSN:
- 2044-4753
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Fe‐based catalysts are an active, selective, and low‐cost option for tuning Fischer‐Tropsch synthesis (FTS) selectivity toward desirable light olefins. By encapsulating Fe within ZSM‐5, the resultant core‐shell catalysts have the potential to control the product distribution via secondary reactions that occur over the acid sites of the zeolite shell. In this paper, Fe is encapsulated within ZSM‐5 via the seed‐directed growth technique and characterized with a suite of analytical techniques including Mössbauer spectroscopy and X‐ray absorption fine structure (XAFS). Characterization of the core‐shell catalysts indicates that some of the Fe‐based active phase is destabilized during seed‐directed growth, demonstrating the challenges associated with encapsulating an Fe‐based active phase within zeolites. However, comparing FTS performance of the core‐shell catalyst with the Fe‐based control synthesized via incipient wetness impregnation demonstrates improved selectivity toward the desired C2‐C4olefins and C5+hydrocarbons.more » « less
-
This review focuses on recent fundamental insights about methane dehydroaromatization (MDA) to benzene over ZSM-5-supported transition metal oxide-based catalysts (MO x /ZSM-5, where M = V, Cr, Mo, W, Re, Fe). Benzene is an important organic intermediate, used for the synthesis of chemicals like ethylbenzene, cumene, cyclohexane, nitrobenzene and alkylbenzene. Current production of benzene is primarily from crude oil processing, but due to the abundant availability of natural gas, there is much recent interest in developing direct processes to convert CH 4 to liquid chemicals. Among the various gas-to-liquid methods, the thermodynamically-limited Methane DehydroAromatization (MDA) to benzene under non-oxidative conditions appears very promising as it circumvents deep oxidation of CH 4 to CO 2 and does not require the use of a co-reactant. The findings from the MDA catalysis literature is critically analyzed with emphasis on in situ and operando spectroscopic characterization to understand the molecular level details regarding the catalytic sites before and during the MDA reaction. Specifically, this review discusses the anchoring sites of the supported MO x species on the ZSM-5 support, molecular structures of the initial dispersed surface MO x sites, nature of the active sites during MDA, reaction mechanisms, rate-determining step, kinetics and catalyst activity of the MDA reaction. Finally, suggestions are given regarding future experimental investigations to fill the information gaps currently found in the literature.more » « less
-
Roosa, Stephen A (Ed.)This experimental process demonstrates the potential of advancing the technology of lignocellulosic-based biofuels. Maximized bio-oil yields and gasoline range aromatics were obtained from the pyrolysis of switchgrass biomass in a medium-scale fixed bed reactor (48.2 L). The reaction’s final temperature was set at 520ºC while the carrier gas flow rate was varied at (50 L min-1, 75 L min-1 and 100 L min-1) both without and with the use of the ZSM-5 catalyst. Bio-oil yields of 18.2%, 26.9%, and 34.1% were generated without catalyst. Using the ZSM-5 catalyst, bio-oil yields of 20.2%, 41.5%, and 47.7% were generated. At 75 L min-1, 9.6% gasoline range organics (GROs) were detected without the catalyst and 12.4% aromatics were detected in the experiment with ZSM-5 catalyst. At 100 L min-1, 10.5%, and 13.7% of aromatics were detected without and with ZSM-5 catalyst respectively. At 75 L min-1, 14.5% of oxygen content recorded without catalyst, and 5.6% with ZSM-5 catalyst. At 100 L min-1, oxygen content was 10.4% without catalyst, and 8.6 % with ZSM-5 catalyst. The effects of carrier gas flow rate variations and a ZSM-5 catalyst on bio-oil yields and quality were experimentally demonstrated using a single-step thermochemical conversion process. This is a major development towards improving U.S energy security and achieving global CO2 emissions mitigation targets.more » « less
-
Recently, stable non-oxidative conversion of methane (NOCM) for up to 8 h with a C 2 selectivity greater than 90% has been reported over Pt–Bi/ZSM-5 at moderate temperatures (600–700 °C). In this study, we show that the structure of the bimetallic nanoparticles on Pt–Bi/ZSM-5 catalyst is similar to Pt–Bi/SiO 2 . EXAFS indicates the formation of Pt-rich bimetallic Pt–Bi nanoparticles with Pt–Bi bond distance of 2.80 Å. The XRD spectra (on SiO 2 ) are consistent with cubic, intermetallic surface Pt 3 Bi phase on a Pt core. The Pt 3 Bi structure is not known in the thermodynamic phase diagram. In all catalysts, only a small fraction of Bi alloys with Pt. At high Bi loadings, excess Bi reduces at high temperature, covering the catalytic surface leading to a loss in activity. At lower Bi loadings with little excess Bi, the Pt 3 Bi surface is effective for non-oxidative coupling of CH 4 (on ZSM-5) and propane dehydrogenation (on SiO 2 ).more » « less