An official website of the United States government
Metastable phases were formed in Mn1−xCoxNiGe (x=0.05 and 0.08) by annealing at 800 °C followed by rapid cooling, i.e., quenching, at ambient pressure (P=0) and under a pressure of P=3.5 GPa, and their phase transitions and associated magnetocaloric properties were investigated. The crystal cell volumes of the metastable phases decreased, and their structural transitions significantly shifted to lower temperatures relative to those of the slow-cooled compounds, with a greater reduction observed in the samples where the rapid cooling occurred under high pressures. The magnetic and structural transitions coupled to form a magnetostructural transition in the metastable phases, resulting in large magnetic entropy changes up to −79.6 J kg−1 K−1 (x=0.08) for a 7-T field change. The experimental results demonstrate thermal quenching and high-pressure annealing as alternative methods to create magnetostructural transitions, without modifying the compositions of the materials.
more »
« less
This content will become publicly available on June 7, 2025
The effects of high-pressure annealing on magnetostructural transitions and magnetoresponsive properties in stoichiometric MnCoGe
In this study, phase transitions (structural and magnetic) and associated magnetocaloric properties of stoichiometric MnCoGe have been investigated as a function of annealing pressure. Metastable phases were generated by annealing at 800 °C followed by rapid cooling under pressures up to 6.0 GPa. The x-ray diffraction results reveal that the crystal cell volume of the metastable phases continuously decreases with increasing thermal processing pressure, leading to a decrease in the structural transition temperature. The magnetic and structural transitions merge and form a first-order magnetostructural transition between the ferromagnetic orthorhombic and paramagnetic hexagonal phases over a broad temperature range (>80 K) spanning room temperature, yielding considerable magnetic entropy changes. These findings demonstrate the utility of thermal processing under high pressure, i.e., high-pressure annealing, to control the magnetostructural transitions and associated magnetocaloric properties of MnCoGe without altering its chemical composition.
more »
« less
- Award ID(s):
- 1904636
- PAR ID:
- 10562117
- Publisher / Repository:
- AIP Publishing
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 135
- Issue:
- 21
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The effects of doping, hydrostatic pressure, and thermal quenching on the phase transitions and magnetocaloric properties of the Mn1−xCoxNiGe system have been investigated. Cobalt doping on the Mn site shifted the martensitic structural transition toward lower temperature until it was ultimately absent, leaving only a magnetic transition from a ferromagnetic (FM) to a paramagnetic (PM) state in the high-temperature hexagonal phase. Co-occurrence of the magnetic and structural transitions to form a first-order magnetostructural transition (MST) from the FM orthorhombic to the PM hexagonal phase was observed in samples with 0.05 < x < 0.20. An additional antiferromagnetic–ferromagnetic-like transition was observed in the martensite phase for 0.05 < x < 0.10, which gradually vanished with increasing Co concentration (x > 0.10) or magnetic field (H > 0.5 T). The application of external hydrostatic pressure shifted the structural transition to lower temperature until an MST was formed in samples with x = 0.03 and 0.05, inducing large magnetic entropy changes up to −80.3 J kg−1 K−1 (x = 0.03) for a 7-T field change under 10.6-kbar pressure. Similar to the effects of the application of hydrostatic pressure, an MST was formed near room temperature in the sample with x = 0.03 by annealing at high temperature (1200 °C) followed by quenching, resulting in a large magnetic entropy change of −56.2 J kg−1 K−1. These experimental results show that the application of pressure and thermal quenching, in addition to compositional variations, are effective methods to create magnetostructural transitions in the MnNiGe system, resulting in large magnetocaloric effects.more » « less
-
The MAB phases are atomically layered, ternary or quaternary transition metal (M) borides (TMBs), with the general formula (MB)2 zAx(MB2)y( z = 1–2; x = 1–2; y = 0–2), whose structures are composed of a transition M-B sublattices interleaved by A-atom (A = Al,Zn) mono- or bilayers. Most of the MAB phases were discovered before the 1990s, but recent discoveries of intriguing magnetocaloric properties, mechanical deformation behaviour, catalytic properties, and high-temperature oxidation resistance has led to their ‘re-discovery’. Herein, MAB phase synthesis is reviewed and their magnetic, electronic, thermal, and mechanical properties are summarized. Because the M-B layers in the MAB phases structurally resemble their corresponding binaries of the same M:B stoichiometry, the effects of the A-layers on properties are discussed. Inconsistencies in the literature are critically assessed to gain insights on the processing-structure-property relations, suggest fruitful avenues for future research, and identify limitations for prospective applications.more » « less
-
The magnetocaloric effect (MCE) in iron (Fe) nanoparticles incorporated within a titanium nitride (TiN) thin-film matrix grown using pulsed laser deposition (PLD) is investigated in this study. The study demonstrates the ability to control the entropy change across the magnetic phase transition by varying the size of the Fe nanoparticles. The structural characterization carried out using X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and scanning transmission electron (TEM) showed that TiN films are (111) textured, while the Fe-particles are mostly spherical in shapes, are single-crystalline, and have a coherent structure with the surrounding TiN thin-film matrix. The TiN thin-film matrix was chosen as a spacer layer since it is nonmagnetic, is highly corrosion-resistive, and can serve as an excellent conduit for extracting heat due to its high thermal conductivity (11 W/m K). The magnetic properties of Fe–TiN systems were investigated using a superconducting quantum interference device (SQUID) magnetometer. In-plane magnetic fields were applied to record magnetization versus field (M–H) and magnetization versus temperature (M–T) curves. The results showed that the Fe–TiN heterostructure system exhibits a substantial isothermal entropy change (ΔS) over a wide temperature range, encompassing room temperature to the blocking temperature of the Fe nanoparticles. Using Maxwell’s relation and analyzing magnetization–temperature data under different magnetic fields, quantitative insights into the isothermal entropy change (ΔS) and magnetocaloric effect (MCE) were obtained for the Fe–TiN heterostructure system. The study points out a considerable negative change in ΔS that reaches up to 0.2 J/kg K at 0.2 T and 300 K for the samples with a nanoparticle size on the order of 7 nm. Comparative analysis revealed that Fe nanoparticle samples demonstrate higher refrigeration capacity (RC) in comparison to Fe thin-film multilayer samples, with the RC increasing as the Fe particle size decreases. These findings provide valuable insights into the potential application of Fe–TiN heterostructures in solid-state cooling technologies, highlighting their enhanced magnetocaloric properties.more » « less
-
Abstract The phase transitions in MnNiGe compounds were explored by manipulating the heat treatment conditions and through hydrostatic pressure application. As the quenching temperature increased, both the first-order martensitic structural transition temperatures and magnetic transition temperatures decreased relative to those in the slowly-cooled samples. When the samples were quenched from 1200 ∘C, the first-order martensitic structural transition temperature lowered by more than 200 K. The structural transitions also shifted to lower temperature with the application of hydrostatic pressure during measurement. Temperature-dependent x-ray diffraction results reveal that the changes of the cell parameters resulting from the structural transitions are nearly identical for all samples regardless of the extensive variation in their structural transition temperatures. In addition, neutron scattering measurements confirm the magnetic structure transition between simple and cycloidal spiral magnetic structures.more » « less