Abstract Common adhesives for nonstructural applications are manufactured using petrochemicals and synthetic solvents. These adhesives are associated with environmental and health concerns because of their release of volatile organic compounds (VOCs). Biopolymer adhesives are an attractive alternative because of lower VOC emissions, but their strength is often insufficient. Existing mineral fillers can improve the strength of biopolymer adhesives but require the use of crosslinkers that lower process sustainability. This work introduces a novel approach to strengthen biopolymer adhesives through calcium carbonate biomineralization, which avoids the need for crosslinkers. Biomineral fillers produced by either microbially or enzymatically induced calcium carbonate precipitation (MICP and EICP, respectively) were precipitated within guar gum and soy protein biopolymers. Both, MICP and EICP, increased the strength of the biopolymer adhesives. The strength was further improved by optimizing the concentrations of bacteria, urease enzyme, and calcium. The highest strengths achieved were on par with current commercially available nonstructural adhesives. This study demonstrates the feasibility of using calcium carbonate biomineralization to improve the properties of biopolymer adhesives, which increases their potential viability as more sustainable adhesives.
more »
« less
Biotrapping Ureolytic Bacteria on Sand to Improve the Efficiency of Biocementation
Microbially induced calcium carbonate precipitation (MICP) has emerged as a novel technology with the potential to produce building materials through lower-temperature processes. The formation of calcium carbonate bridges in MICP allows the biocementation of aggregate particles to produce biobricks. Current approaches require several pulses of microbes and mineralization media to increase the quantity of calcium carbonate minerals and improve the strength of the material, thus leading to a reduction in sustainability. One potential technique to improve the efficiency of strength development involves trapping the bacteria on the aggregate surfaces using silane coupling agents such as positively charged 3-aminopropyl-methyl-diethoxysilane (APMDES). This treatment traps bacteria on sand through electrostatic interactions that attract negatively charged walls of bacteria to positively charged amine groups. The APMDES treatment promoted an abundant and immediate association of bacteria with sand, increasing the spatial density of ureolytic microbes on sand and promoting efficient initial calcium carbonate precipitation. Though microbial viability was compromised by treatment, urea hydrolysis was minimally affected. Strength was gained much more rapidly for the APMDES-treated sand than for the untreated sand. Three injections of bacteria and biomineralization media using APMDES-treated sand led to the same strength gain as seven injections using untreated sand. The higher strength with APMDES treatment was not explained by increased calcium carbonate accrual in the structure and may be influenced by additional factors such as differences in the microstructure of calcium carbonate bridges between sand particles. Overall, incorporating pretreatment methods, such as amine silane coupling agents, opens a new avenue in biomineralization research by producing materials with an improved efficiency and sustainability.
more »
« less
- Award ID(s):
- 2349256
- PAR ID:
- 10578942
- Publisher / Repository:
- ACS Publications
- Date Published:
- Journal Name:
- ACS applied materials interfaces
- ISSN:
- 1944-8244
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Viana da Fonseca, António; Ferreira, Cristiana (Ed.)Microbially induced carbonate precipitation (MICP) is a bio-mediated ground improvement technique that can increase soil stiffness and produce cohesion within granular material. Most experimental investigations on MICP-treated soils are performed on idealized granular materials. Evaluating a narrow range of particle sizes dismisses the potential influence of soil fabric on MICP treatment efficiency. Therefore, little is known regarding the influence of soil fabric on the level of improvement achievable post-MICP treatment. We investigate the influence of the coefficient of uniformity (Cu) on the level of improvement that can be obtained from MICP treatment. This study couples unconfined compression testing with microscale observations obtained from x-ray computed tomography (CT) of two sand mixtures with different Cu values. A soil column and CT specimen of each sand mixture were prepared and received the same number of MICP- injections. The shear wave velocity (Vs) of the soil columns was monitored to evaluate the increase in soil stiffness over time. After MICP treatment, the bio-cemented columns were subjected to unconfined compressive strength testing. Results indicate that for a similar mass of carbonate, the soil with a larger Cu experienced a greater increase in Vs but a lower maximum unconfined compressive strength. Through CT imaging, the soil with a smaller Cu was observed to have a more uniform distribution of carbonate within the sand matrix whereas the soil with a larger Cu has more sporadic MICP trends. This study elucidates the influence of soil fabric on the level of improvement that can be achieved through MICP treatment and assesses the reliability of x-ray CT scanning of MICP-treated sands with moderate carbonate content.more » « less
-
Abstract Researchers have made headway against challenges of increasing cement infrastructure and low plastic recycling rates by using waste plastic in cementitious materials. Past studies indicate that microbially induced calcium carbonate precipitation (MICP) to coat plastic in calcium carbonate may improve the strength. The objective of this study was to increase the amount of clean and contaminated waste plastic that can be added to mortar and to assess whether MICP treatment enhances the strength. The performance of plastic-filled mortar was investigated at 5%, 10%, and 20% volume replacement for cement. Untreated, clean plastics at a 20% cement replacement produced compressive strengths acceptable for several applications. However, a coating of MICP on clean waste plastic did not improve the strengths. At 10% replacement, both MICP treatment and washing of contaminated plastics recovered compressive strengths by approximately 28%, relative to mortar containing oil-coated plastics. By incorporating greater volumes of waste plastics into mortar, the sustainability of cementitious composites has the potential of being improved by the dual mechanisms of reduced cement production and repurposing plastic waste.more » « less
-
Abstract Microbially-induced calcium carbonate precipitation (MICP) is a biological process in which microbially-produced urease enzymes convert urea and calcium into solid calcium carbonate (CaCO3) deposits. MICP has been demonstrated to reduce permeability in shale fractures under elevated pressures, raising the possibility of applying this technology to enhance shale reservoir storage safety. For this and other applications to become a reality, non-invasive tools are needed to determine how effectively MICP seals shale fractures at subsurface temperatures. In this study, two different MICP strategies were tested on 2.54 cm diameter and 5.08 cm long shale cores with a single fracture at 60 ℃. Flow-through, pulsed-flow MICP-treatment was repeatedly applied to Marcellus shale fractures with and without sand (“proppant”) until reaching approximately four orders of magnitude reduction in apparent permeability, while a single application of polymer-based “immersion” MICP-treatment was applied to an Eagle Ford shale fracture with proppant. Low-field nuclear magnetic resonance (LF-NMR) and X-Ray computed microtomography (micro-CT) techniques were used to assess the degree of biomineralization. With the flow-through approach, these tools revealed that while CaCO3precipitation occurred throughout the fracture, there was preferential precipitation around proppant. Without proppant, the same approach led to premature sealing at the inlet side of the core. In contrast, immersion MICP-treatment sealed off the fracture edges and showed less mineral precipitation overall. This study highlights the use of LF-NMR relaxometry in characterizing fracture sealing and can help guide NMR logging tools in subsurface remediation efforts.more » « less
-
Tang, Qiang (Ed.)As an environmentally friendly technology, microbially induced calcite precipitation (MICP) is widely used to improve the engineering properties of soil. The goal of this study was to investigate the effect of rainfall-induced erosion on the stability of sandy slopes which were treated by MICP technology. The observation of the erosion pattern of low concentration (0.25 M Ca) and high concentration (0.5 M Ca) of MICP-treated slopes, the mechanical behaviors of MICP-treated and cement-treated samples, and the effects of rainfall-induced erosion on the roughness of 0.5 M Ca MICP-treated and 10% cement-treated slope were studied through visual observation, unconfined compressive tests, and roughness tests. For the 0.25 M Ca MICP-treated sample, surface erosion was found to occur soon after the start of the rainfall erosion test, while for the 0.5 M Ca MICP-treated sample, the slope surface remained intact after exposing to the rainfall for 24 hours. Through unconfined compressive tests, it can be concluded that the 0.5 M Ca MICP treatment achieved a high strength, which was similar to 10% cement-treated sand. The roughness test results showed that the surface of 0.5 M Ca MICP-treated slope looked smoother than the uneroded surface after 24-h rainfall-induced erosion. On the contrary, the surface of the 10% cement-treated slope became rougher after 24-h rainfall-induced erosion. These results indicated that the MICP-treated sandy slope had lower resistance against rainfall-induced erosion compared to the cement-treated sandy slope.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- The DOI is not currently available.