skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Utilizing (Al, Ga)2O3/Ga2O3 superlattices to measure cation vacancy diffusion and vacancy-concentration-dependent diffusion of Al, Sn, and Fe in β -Ga2O3
Title: Utilizing (Al, Ga)2O3/Ga2O3 superlattices to measure cation vacancy diffusion and vacancy-concentration-dependent diffusion of Al, Sn, and Fe in β -Ga2O3
Diffusion of native defects such as vacancies and their interactions with impurities are fundamental to semiconductor crystal growth, device processing, and design. However, the transient equilibration of native defects is difficult to directly measure. We used (AlxGa1−x)2O3/Ga2O3 superlattices (SLs) to detect and analyze transient diffusion of cation vacancies during annealing in O2 at 1000–1100 °C. Using a novel finite difference scheme for diffusion with time- and space-varying diffusion constants, we determined diffusion constants for Al, Fe, and cation vacancies, including the vacancy concentration dependence for Al. In the case of SLs grown on Sn-doped β-Ga2O3 (010) substrates, gradients observed in the extent of Al diffusion indicate a supersaturation of vacancies in the substrates that transiently diffuse through the SLs coupled strongly to Sn and thus slowed compared to undoped cases. In the case of SLs grown on (010) Fe-doped substrates, the Al diffusion is uniform through the SLs, indicating a depth-uniform concentration of vacancies. We find no evidence for the introduction of VGa from the free surface at rates sufficient to affect Al diffusion at at. % concentrations, establishing an upper bound on surface injection. In addition, we show that unintentional impurities in Sn-doped Ga2O3 such as Fe, Ni, Mn, Cu, and Li also diffuse toward the surface and accumulate. Many of these likely have fast interstitial diffusion modes capable of destabilizing devices, thus suggesting that impurities may require further reduction. This work provides a method to measure transients in diffusion-mediating native defects otherwise hidden in common processes such as ion implantation, etching, and film growth.  more » « less
Award ID(s):
1950589
PAR ID:
10580645
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ; ;
Publisher / Repository:
AIP Publishing
Date Published:
Journal Name:
APL Materials
Volume:
12
Issue:
8
ISSN:
2166-532X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; (, SPIE 11687, Oxide-based Materials and Devices XII)
    Teherani, Ferechteh H.; Look, David C.; Rogers, David J. (Ed.)
    Gallium oxide (Ga2O3), an ultra-wide bandgap semiconductor with potential applications in power devices, may be doped with Mg to control the native n-type conductivity. The charge transitions associated with Mg in Mg-doped β-Ga2O3 crystals are studied using photoinduced electron paramagnetic resonance (photo-EPR) spectroscopy to understand the mechanisms that produce stable semi-insulating substrates. The steady state photo-EPR measurements are performed at 130 K by illuminating the samples with photon energy from 0.7 to 4.7 eV. Our results show that there are two transitions associated with Mg in the bandgap: onset of quenching of neutral Mg at 1.5 eV and excitation at 3.0 eV. The quenching threshold is consistent with several DFT predicted values for Mg-/0 level. Therefore, we suggest the quenching is due to transition of an electron from the valence band to the neutral Mg. For photoexcitation, hole capture is the only viable process due to polaronic nature of neutral Mg in Ga2O3. The measurements demonstrate that electron excitation to impurities, such as Fe and Ir, does not contribute to creation of the holes. Further, gallium vacancies must not participate since their characteristic EPR spectrum is never seen. Thus, we speculate that the defects responsible for the hole formation and consequent excitation of the neutral Mg are oxygen vacancies. 
    more » « less
  2. ; ; ; (, Applied Physics Letters)
    Obtaining uniform silicon concentration, especially with low concentrations (ranging from 1 × 1016 to 1 × 1018 cm−3) by molecular beam epitaxy, has been challenging due to oxidation of a silicon solid source in the oxide environment. In this work, Si doping of β-Ga2O3 (010) films by diluted disilane as the Si source is investigated using hybrid plasma-assisted molecular beam epitaxy. The impact of growth temperature, disilane source concentration, and disilane flow rate on Si incorporation was studied by secondary ion mass spectrometry. Uniform Si concentrations ranging from 3 × 1016 to 2 × 1019 cm−3 are demonstrated. Si-doped β-Ga2O3 films with different silicon concentrations were grown on Fe-doped β-Ga2O3 (010) substrates. The electron concentration and mobility were determined using van de Pauw Hall measurements. A high mobility of 135 cm2/V s was measured for an electron concentration of 3.4 × 1017 cm−3 at room temperature. 
    more » « less
  3. ; ; ; ; ; (, Applied Physics Letters)
    Growing a thick high-quality epitaxial layer on the β-Ga2O3 substrate is crucial in commercializing β-Ga2O3 devices. Metal organic chemical vapor deposition (MOCVD) is also well-established for the large-scale commercial growth of β-Ga2O3 and related heterostructures. This paper presents a systematic study of the Schottky barrier diodes fabricated on two different Si-doped homoepitaxial β-Ga2O3 thin films grown on Sn-doped (001) and (010) β-Ga2O3 substrates by MOCVD. X-ray diffraction analysis of the MOCVD-grown sample, room temperature current density–voltage data for different Schottky diodes, and C–V measurements are presented. Diode characteristics, such as ideality factor, barrier height, specific on-resistance, and breakdown voltage, are studied. Temperature dependence (170–360 K) of the ideality factor, barrier height, and Poole–Frenkel reverse leakage mechanism are also analyzed from the J–V–T characteristics of the fabricated Schottky diodes. 
    more » « less
  4. ; ; (, Applied Physics Letters)
    Si-doped β-phase (010) Ga2O3 epi-films with fast growth rates were comprehensively investigated using trimethylgallium (TMGa) as the Ga precursor via metalorganic chemical vapor deposition (MOCVD). Two main challenges facing the MOCVD growth of thick (010) β-Ga2O3 films with fast growth rates include high impurity carbon (C) incorporation and rough surface morphologies due to the formation of imbedded 3D pyramid-shaped structures. In this work, two different categories of oxygen source (high-purity O2 > 99.9999% and O2* with 10 ppm of [H2O]) were used for β-Ga2O3 MOCVD growth. Our study revealed that the size and density of the 3D defects in the β-Ga2O3 epi-films were significantly reduced when the O2* was used. In addition, the use of off-axis (010) Ga2O3 substrates with 2° off-cut angle leads to further reduction of defect formation in β-Ga2O3 with fast growth rates. To suppress C incorporation in MOCVD β-Ga2O3 grown with high TMGa flow rates, our findings indicate that high O2 (or O2*) flow rates are essential. Superior room temperature electron mobilities as high as 110–190 cm2/V·s were achieved for β-Ga2O3 grown using O2* (2000 sccm) with a growth rate of 4.5 μm/h (film thickness of 6.3 μm) within the doping range of 1.3 × 1018–7 × 1015 cm−3. The C incorporation is significantly suppressed from ∼1018 cm−3 to <5 × 1016 cm−3 ([C] detection limit) for β-Ga2O3 grown using high O2 (O2*) flow rate of 2000 sccm. Results from this work will provide guidance on developing high-quality, thick β-Ga2O3 films required for high power electronic devices with vertical configurations. 
    more » « less
  5. ; ; ; ; ; ; (, Applied Physics Letters)
    This work demonstrates the advantage of carrying out silicon ion (Si+) implantation at high temperatures for forming controlled heavily doped regions in gallium oxide. Room temperature (RT, 25 °C) and high temperature (HT, 600 °C) Si implants were carried out into MBE grown (010) β-Ga2O3 films to form ∼350 nm deep Si-doped layers with average concentrations up to ∼1.2 × 1020 cm−3. For such high concentrations, the RT sample was too resistive for measurement, but the HT samples had 82.1% Si dopant activation efficiency with a high sheet electron concentration of 3.3 × 1015 cm−2 and an excellent mobility of 92.8 cm2/V·s at room temperature. X-ray diffraction measurements indicate that HT implantation prevents the formation of other Ga2O3 phases and results in reduced structural defects and lattice damage. These results are highly encouraging for achieving ultra-low resistance heavily doped Ga2O3 layers using ion implantation. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email