In functionally graded materials (FGMs) fabricated using directed energy deposition (DED) additive manufacturing (AM), cracks may form due to interdendritic stress during solidification, the formation of deleterious phases, or the buildup of residual stresses. This study builds on our previously proposed concept of FGM feasibility diagrams to identify gradient pathways that avoid deleterious phases in FGMs by also considering hot cracking. Here, five hot cracking criteria were integrated into the feasibility diagrams, and equilibrium simulations were carried out based on Scheil results (termed hybrid Scheil-equilibrium simulation) to predict phase formation below the solidus temperature considering solidification micro-segregation. The new feasibility diagrams were applied to four previously studied FGMs, and the newly proposed approach predicted high crack susceptibility, detrimental phase formation, or interdendritic BCC phase formation in the experimentally observed cracking region. This demonstrates the utility of the proposed framework for crack prediction in the design of future FGMs gradient pathways.
more »
« less
This content will become publicly available on December 1, 2025
Circumventing cracking in grading 316L stainless steel to Monel400 through compositional modifications in directed energy deposition
In joining Fe-alloys and Cu-containing alloys to access the high strength of steels and corrosion resistance of Cu-alloy, cracking is widely observed due to the significant Cu microsegregation during the solidification process, resulting in an interdendritic Cu-rich liquid film at the end of solidification. By fabricating functionally graded materials (FGMs) that incorporate additional elements like Ni in the transition region between these terminal alloy classes, the hot cracking can be reduced. In the present work, the joining of stainless steel 316L (SS316L) and Monel400 by modifying the Ni concentration in the gradient region was studied. A new hot cracking criterion based on hybrid Scheil-equilibrium approach was developed and validated with monolithic multi-layer samples within the SS316L-Ni-Monel400 three-alloy system and a SS316L to 55/45 wt% SS316L/Ni to Monel400 FGM sample fabricated by direct energy deposition (DED). The new hot cracking criterion, based on the hybrid Scheil-equilibrium approach, is expected to help design FGM paths between other Fe-alloys and Cu-containing alloys as well.
more »
« less
- Award ID(s):
- 2050069
- PAR ID:
- 10583095
- Publisher / Repository:
- Materialia
- Date Published:
- Journal Name:
- Materialia
- Volume:
- 38
- Issue:
- C
- ISSN:
- 2589-1529
- Page Range / eLocation ID:
- 102283
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Joining of Cu-based dispersion-strengthened alloys to Ni-based superalloys has garnered increased attention for liquid rocket engine applications due to the high thermal conductivity of Cu-based alloys and high temperature tensile strength of Ni-based superalloys. However, such joints can suffer from cracking when joined via liquid state processes, leading to part failure. In this work, compositions of 15–95 wt.% GRCop42 are alloyed with Inconel 625 and characterized to better understand the root cause of cracking. Results indicate a lack of miscibility between Cu-deprived and Cu-rich liquids in compositions corresponding to 30–95 wt.% GRCop42. Two distinct morphologies are observed and explained by use of CALPHAD; Cu-deprived dendrites with Cu-rich interdendritic zones at 30–50 wt.% GRCop42 and Cu-deprived spheres surrounded by a Cu-rich matrix at 60–95 wt.% GRCop42. Phase analysis reveals brittle intermetallic phases precipitate in the 60–95 wt.% GRCop42 Cu-deprived region. Three cracking mechanisms are proposed herein that provide guidance on the avoidance of defects Ni-based superalloy to Cu-based dispersion strengthened alloy joints.more » « less
-
Nickel-based alloys, Alloys 625 and 718, are widely used in the aerospace industry due to their excellent corrosion resistance and high strength at elevated temperatures. Recently, these alloys have been utilized to manufacture rocket engine components using additive manufacturing (AM) technologies such as laser powder bed fusion (LPBF) and powder-blown laser-based directed energy deposition (DED). These technologies offer faster and more cost-effective production while enabling the fabrication of near-net-shape parts that are subsequently joined by welding. However, solidification cracking susceptibility varies significantly between AM and conventionally processed materials, and limited weldability characterization has been conducted on AM-fabricated materials. This study assesses the weld solidification cracking susceptibility of Alloys 625 and 718 produced by wrought (mill-rolled), LPBF, and DED using transverse varestraint testing, Scheil-Gulliver simulations, the Crack Susceptibility Index (CSI), and the Flow Resistance Index (FRI). Transverse varestraint testing revealed that AM parts exhibited higher susceptibility due to the presence of larger and elongated grains in the fusion zone, affecting the weld solidification cracking response. In Alloy 625, the LPBF condition exhibited the highest maximum crack distance (MCD) of 2.35 ± 0.16 mm, compared to 1.56 ± 0.06 mm for wrought and 1.72 ± 0.10 mm for DED. Similarly, in Alloy 718, the DED condition showed the highest MCD of 2.93 ± 0.41 mm, while the wrought condition had an MCD of 2.01 ± 0.12 mm, and the LPBF condition reached 3.01 ± 0.33 mm at 5 % strain, without a clearly defined saturation strain. Although wrought materials demonstrated greater resistance to solidification cracking, solidification simulations did not correlate with the experimental testing, as they do not account for microstructural and mechanical factors, relying solely on chemistry.more » « less
-
Defining heat treatments for compositionally functionally graded materials (FGMs) is challenging due to varying processing conditions in terminal alloys and gradient regions. In the present work, we studied the impact of heat treatments on phase transformations and the resulting mechanical properties along an FGM grading from stainless steel 304L (SS304L) to Inconel 625 (IN625) FGM fabricated using directed energy deposition (DED) additive manufacturing (AM). We applied heat treatments at 700 °C, 900 °C, and 1150 °C and the microstructure and hardness, as a function of layer-wise composition and applied heat treatment, were characterized. The applicability of computational methods previously developed by the team to predict experimentally observed phases by the hybrid Scheil-equilibrium approach was evaluated. This approach improves the accuracy of predicting phases formed after heat treatment compared to equilibrium thermodynamic calculations using the overall layer compositions and provides a simple pathway to assist in designing heat treatment for FGMs.more » « less
-
Designing alloys for additive manufacturing (AM) presents significant opportunities. Still, the chemical composition and processing conditions required for printability (ie., their suitability for fabrication via AM) are challenging to explore using solely experimental means. In this work, we develop a high-throughput (HTP) computational framework to guide the search for highly printable alloys and appropriate processing parameters. The framework uses material properties from stateof- the-art databases, processing parameters, and simulated melt pool profiles to predict processinduced defects, such as lack-of-fusion, keyholing, and balling. We accelerate the printability assessment using a deep learning surrogate for a thermal model, enabling a 1,000-fold acceleration in assessing the printability of a given alloy at no loss in accuracy when compared with conventional physics-based thermal models. We verify and validate the framework by constructing printability maps for the CoCrFeMnNi Cantor alloy system and comparing our predictions to an exhaustive ’in-house’ database. The framework enables the systematic investigation of the printability of a wide range of alloys in the broader Co-Cr-Fe-Mn-Ni HEA system. We identified the most promising alloys that were suitable for high-temperature applications and had the narrowest solidification ranges, and that was the least susceptible to balling, hot-cracking, and the formation of macroscopic printing defects. A new metric for the global printability of an alloy is constructed and is further used for the ranking of candidate alloys. The proposed framework is expected to be integrated into ICME approaches to accelerate the discovery and optimization of novel high-performance, printable alloys.more » « less