skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Attention:

The DOI auto-population feature in the Public Access Repository (PAR) will be unavailable from 4:00 PM ET on Tuesday, July 8 until 4:00 PM ET on Wednesday, July 9 due to scheduled maintenance. We apologize for the inconvenience caused.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


This content will become publicly available on November 1, 2025

Title: Low‐Temperature Synthesis of Stable CaZn 2 P 2 Zintl Phosphide Thin Films as Candidate Top Absorbers
Abstract The development of tandem photovoltaics and photoelectrochemical solar cells requires new absorber materials with bandgaps in the range of ≈1.5–2.3 eV, for use in the top cell paired with a narrower‐gap bottom cell. An outstanding challenge is finding materials with suitable optoelectronic and defect properties, good operational stability, and synthesis conditions that preserve underlying device layers. This study demonstrates the Zintl phosphide compound CaZn2P2as a compelling candidate semiconductor for these applications. Phase‐pure, ≈500 nm‐thick CaZn2P2thin films are prepared using a scalable reactive sputter deposition process at growth temperatures as low as 100 °C, which is desirable for device integration. Ultraviolet‐visible  spectroscopy shows that CaZn2P2films exhibit an optical absorptivity of ≈104 cm−1at ≈1.95 eV direct bandgap. Room‐temperature photoluminescence (PL) measurements show near‐band‐edge optical emission, and time‐resolved microwave conductivity (TRMC) measurements indicate a photoexcited carrier lifetime of ≈30 ns. CaZn2P2is highly stable in both ambient conditions and moisture, as evidenced by PL and TRMC measurements. Experimental data are supported by first‐principles calculations, which indicate the absence of low‐formation‐energy, deep intrinsic defects. Overall, this study shall motivate future work integrating this potential top cell absorber material into tandem solar cells.  more » « less
Award ID(s):
2011967
PAR ID:
10590648
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ; ; ; ; ; ; ;
Publisher / Repository:
Wiley
Date Published:
Journal Name:
Advanced Energy Materials
Volume:
14
Issue:
44
ISSN:
1614-6832
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; (, MRS Advances)
    Abstract: Monolithic integrated thin film tandem solar cells consisting of a high bandgap perovskite top cell and a low bandgap thin film bottom cell are expected to reach higher power conversion efficiencies (PCEs) with lower manufacturing cost and environmental impacts than the market-dominant crystalline silicon photovoltaics. There have been several demonstrations of 4-terminal and 2-terminal perovskite tandem devices with CuInGaSe 2 (CIGS) or CuInSe 2 (CIS) and, similar to the other tandem structures, the optimization of this device relies on optimal choice for the perovskite bandgap and thickness. Therefore, further advancement will be enabled by tuning the perovskite absorber to maximize the photocurrent limited by the current match condition. Here, we systematically study the optical absorption and transmission of perovskite thin films with varying absorber band gap. Based on these results, we model the photocurrent generations in both perovskite and CIS subcells and estimate the performances of projected tandem devices by considering the ideally functioning perovskite and CIS device. Our results show that for perovskite layers with 500 nm thickness the optimal bandgap is around 1.6 eV. With these configurations, PCEs above 20% could be achieved by monolithically integrated perovskite/CIS tandem solar cells. Also by modelling the absorption at every layer we calculate the quantum efficiency at each subcell in addition to tracking optical losses. 
    more » « less
  2. ; ; ; ; ; ; ; (, Solar)
    The tandem solar cell presents a potential solution to surpass the Shockley–Queisser limit observed in single-junction solar cells. However, creating a tandem device that is both cost-effective and highly efficient poses a significant challenge. In this study, we present proof of concept for a four-terminal (4T) tandem solar cell utilizing a wide bandgap (1.6–1.8 eV) perovskite top cell and a narrow bandgap (1.2 eV) antimony selenide (Sb2Se3) bottom cell. Using a one-dimensional (1D) solar cell capacitance simulator (SCAPS), our calculations indicate the feasibility of this architecture, projecting a simulated device performance of 23% for the perovskite/Sb2Se3 4T tandem device. To validate this, we fabricated two wide bandgap semitransparent perovskite cells with bandgaps of 1.6 eV and 1.77 eV, respectively. These were then mechanically stacked with a narrow bandgap antimony selenide (1.2 eV) to create a tandem structure, resulting in experimental efficiencies exceeding 15%. The obtained results demonstrate promising device performance, showcasing the potential of combining perovskite top cells with the emerging, earth-abundant antimony selenide thin film solar technology to enhance overall device efficiency. 
    more » « less
  3. ; ; ; ; (, Solar RRL)
    Air‐stable p‐type SnF2:Cs2SnI6with a bandgap of 1.6 eV has been demonstrated as a promising material for Pb‐free halide perovskite solar cells. Crystalline Cs2SnI6phase is obtained with CsI, SnI2, and SnF2salts in gamma‐butyrolactone solvent, but not with dimethyl sulfoxide andN,N‐dimethylformamide solvents. Cs2SnI6is found to be stable for at least 1000 h at 100 °C when dark annealed in nitrogen atmosphere. In this study, Cs2SnI6has been used in a superstrate n–i–p planar device structure enabled by a spin‐coated absorber thickness of ≈2 μm on a chemical bath deposited Zn(O,S) electron transport layer. The best device power conversion efficiency reported here is 5.18% withVOCof 0.81 V, 9.28 mA cm−2JSC, and 68% fill factor. The dark saturation current and diode ideality factor are estimated as 1.5 × 10−3 mA cm−2and 2.18, respectively. The devices exhibit a highVOCdeficit and low short‐circuit current density due to high bulk and interface recombination. Device efficiency can be expected to increase with improvement in material and interface quality, charge transport, and device engineering. 
    more » « less
  4. ; ; ; ; ; ; (, Conference record of the IEEE Photovoltaic Specialists Conference)
    Cadmium telluride and silicon are among the widely used absorber materials in photovoltaic industry. A tandem solar cell of these two can absorb significant portion of solar spectrum to yield high efficiency due to the added voltage of the two solar cells. On basis of low-cost production, a CdTe/Si cell has the potential to produce low-cost and high efficiency tandem PV. The CdTe top cell in a substrate configuration is essential to achieve a tandem between CdTe and Si. A functional CdS/CdTe solar cell in the substrate configuration was fabricated on a Si wafer. Current -Voltage measurements show a diode-like curve with lower J-V parameters compared to standard CdS/CdTe cells. SCAPS simulations were performed to identify possible reasons for poor performance and help improve the device performance. 
    more » « less
  5. ; ; ; ; ; ; ; ; ; ; et al (, 2018 IEEE 7th World Conference on Photovoltaic Energy Conversion (WCPEC))
    Spectroscopic ellipsometry (SE) was performed on CuIn Se 2 (CIS) thin films and solar cells with a goal toward optimizing this low bandgap absorber for tandem applications. The CIS thin films and the absorbers in devices were deposited by one-stage thermal co-evaporation on silicon and on Mo-coated soda-lime glass substrates in a deposition system that has yielded CuIn 1-x Ga x Se 2 (CIGS) cells with > 17% efficiency using standard thickness (2.0 μm)x = 0.3 absorbers and > 13% using 0.7 μm low-Ga absorbers. In this study, a mapping capability for CIS Cu stoichiometry y = [Cu]/[In] over the film area was established based on a y-dependent parametric dielectric function (ε 1 , ε 2 ) with bandgap critical point E g decreasing linearly from 1.030 eV for y = 0.7 to 1.016 eV for y = 1.1. In addition, a full set of (ε 1 , ε 2 ) spectra measured for the CIS cell components enables analysis of SE data in terms of an accurate structural model for the device. With this model, spectra in the external quantum efficiency can be predicted, and deviations from this prediction can be attributed to incomplete collection of photogenerated electrons and holes as simulated with a carrier collection profile. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email