Precipitates have recently been found to significantly enhance the mechanical quality factor in piezoelectric ceramics. Such a piezoelectric hardening effect was attributed to strong interactions between ferroelectric domains and precipitates. In the present work, the response of domains to applied electric fields is observed in situ via transmission electron microscopy in aged (Ba, Ca)TiO3 ceramics with precipitates to reveal the underlying mechanism of this phenomenon. Ferroelectric domains in the Ba-rich matrix grain are observed to be more concentrated near non-polar Ca-rich precipitates. With increasing applied voltage, domains separate from precipitates merge together first, while those near precipitates persist to higher voltages. During ramping down, domains nucleate from precipitates. These direct observations confirm the strong interactions between ferroelectric domains and precipitates in piezoelectric ceramics.
more »
« less
CaTiO3-rich precipitates and their impacts on ferroelectric domains during heating in (Ba,Ca)TiO3 ceramics
In this work with a model system (Ba,Ca)TiO3, we analyze the morphologies of CaTiO3-rich precipitates and their impacts on the microstructures in their surrounding BaTiO¬3-rich matrix. Also, the response of ferroelectric domains around CaTiO3-rich precipitates during heating and cooling is observed in-situ with transmission electron microscopy. Domains attached to precipitates are observed remaining unchanged up to the Curie point at which they disappear. During cooling, domains are observed to form in the vicinity of precipitates and being held in place down to room temperature. Both observations corroborate previous findings that precipitates act as domain pinning points, behaving in a similar manner to earlier experiments with electrical field biasing. Dislocations are often seen around precipitates in the matrix grain and are observed interfering with domains during heating cycles. Dislocations may provide an additional mechanism to restrict domain wall motion and offer a greater piezoelectric hardening effect.
more »
« less
- Award ID(s):
- 2110264
- PAR ID:
- 10596264
- Publisher / Repository:
- Springer
- Date Published:
- Journal Name:
- Journal of Materials Science: Materials in Electronics
- Volume:
- 35
- Issue:
- 27
- ISSN:
- 0957-4522
- Page Range / eLocation ID:
- 1808
- Subject(s) / Keyword(s):
- In-situ TEM Precipitates Dislocations Piezoelectric Hardening (Ba,Ca)TiO3
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Even though the fundamental rules governing dislocation activities have been well established in the past century, we report a phenomenon, dislocation transformation, governed by the generalized-stacking-fault energy surface mismatch (GSF mismatch for short) between two co-existing phases. By carrying out ab-initio-informed microscopic phase-field simulations, we demonstrate that the GSF mismatch between a high symmetry matrix phase and a low symmetry precipitate phase can transform an array of identical full dislocations in the matrix into an array of two different types of full dislocations when they shear through the precipitates. The precipitates serve as a passive Shockley partial source, creating new Shockley partial dislocations that are neither the ones from the dissociation of the full dislocation. This phenomenon enriches our fundamental understanding of partial dislocation nucleation and dislocation-precipitate interactions, offering additional opportunities to tailor work-hardening and twinning processes in alloys strengthened by low-symmetry precipitate phases.more » « less
-
The work clarifies several key questions in shape memory research that have eluded previous studies. The f indings show that dislocation slip emanates at austenite-martensite interfaces during unloading and aligns with the internal twin boundary interface of martensite. It was observed that the type II internal twins of the martensite become parallel dislocations in the austenite. During reloading, these dislocations act as nucleation sites for the martensitic twins, reducing the nucleation barrier and the transformation stress. The precipitates facilitate martensite nucleation but also act as an obstacle to martensite front motion, restrict detwinning, and pin the interfacial dislocations during unloading, thereby contributing to residual strains and martensite stabilization. Martensite nucleation is not suppressed by the size of the thin film, which is of the order of 85 to 105 nanometers thick, and repeated transformation occurred cycle after cycle. Single crystals deformed in the <101> LD exhibited the best recoverability of up to 5.5 % and tensile stresses of up to 1.4 GPa. It was demonstrated for the first time that, when favorably oriented, Ni 4 Ti 3 precipitates undergo a reversible phase transformation to R-phase and can accommodate up to 4 % reversible strains.more » « less
-
This work explores the effect of microstructure on the oxidation behavior of an equiatomic TaTiCr RCCA after 24 h of exposure at 800°C, 1000°C, 1200°C, and 1400°C. Two microstructural conditions, both containing a bcc matrix with C15 Laves precipitates, with one condition having coarser precipitates (∼10.9 µm diameter) and one condition having finer precipitates (∼2.9 µm diameter) were studied. At all oxidation temperatures except 800°C, the finer-scale (TaTiCr-F) condition experienced more rapid oxidation kinetics, higher mass gains, and thicker oxide scales and internal reaction zones. However, at 800°C, the microstructure containing coarser precipitates (TaTiCr-C) formed a thicker oxide scale. Continuous, protective Cr2O3 layers were only observed in the coarse precipitate condition and correlations between Cr2O3 layer thickness, subsequent formation of complex refractory oxides, and the initial Laves precipitate size are described. It is proposed that the formation of continuous Cr2O3 is highly dependent on the size and distribution of the Cr-rich Laves phase and only mildly dependent on phase fraction. Oxidation mechanisms for each condition are discussed relative to the initial microstructures, observed oxide species, and related alloy systems.more » « less
-
There is emerging recognition that crystalline defects such as grain boundaries and dislocations can host structural and chemical environments of their own, which reside in local equilibrium with the bulk material. Targeting these defect phases as objects for materials design would promise new avenues to maximize property gains. Here, we provide experimental proof of a dislocation-templated defect phase using a processing strategy designed to engender defect phase transitions in a nickel-based alloy and demonstrate dramatic effects on strengthening. Following heat treatments designed to encourage solute segregation to dislocations, regions with introduced dislocation populations show evidence of nanoscale ordered domains with a L1 structure, whereas dislocation-free regions remain as a solid solution. Site-specific spherical nanoindentation in regions hosting dislocations and their associated ordered nanodomains exhibit a 40% increase in mean pop-in load compared to similar regions prior to the segregation heat treatment. Strength estimates based on random solute atmospheres around dislocations are not sufficient to predict our measured strengths. Our mechanical measurements, in tandem with detailed electron microscopy and diffraction of the ordered domains, as well as characterization of dislocations in the vicinity of the nanodomains, establish the defect phase framework via direct observations of chemical and structural ordering near dislocations and its potential for offering favorable properties not achievable through conventional materials design.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1007/s10854-024-13530-3