skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Attention:

The NSF Public Access Repository (PAR) system and access will be unavailable from 11:00 PM ET on Friday, November 14 until 2:00 AM ET on Saturday, November 15 due to maintenance. We apologize for the inconvenience.


Title: Thickness dependent electrical resistivity modulation in tensile-strained epitaxial thin films of calcium manganese oxide
We report our studies of the thickness dependence of electrical resistivity and lattice constants in strained epitaxial thin films of calcium manganese oxide. Our results indicate the potential of bi-axial lattice mismatch strain as a handle for modulating electrical resistivity. We observe thickness dependence of lattice constants consistent with what is expected for strain relaxation for films thicker than 400 Å. At lower thickness values, anomalies are observed suggestive of reduced oxygen stoichiometry. We observe a remarkable decrease in electrical resistivity with decreasing film thickness. The resistivity of our thinnest films (5–7 nm) is about three orders of magnitude lower than the resistivity of bulk CaMnO3. Resistivity increases as the film thickness increases, along with the progression of strain relaxation. It is noteworthy that the thickness dependence of resistivity we observe in CMO thin films is the opposite of what has been reported for their hole-doped rare earth manganite counterpart La0.67Ca0.33MnO3 (LCMO), where tensile lattice mismatch strain suppresses metallicity, leading to the increase in resistivity with film thickness. We believe that the enhanced conductivity in our thinnest films is related to the possible oxygen deficiency promoted by tensile strain. Recent x-ray absorption measurements have revealed reduced oxygen content and associated changes in Mn valence states in tensile-strained CMO thin films, as also predicted by density functional theory calculations. This report is the first observation of electrical transport behavior possibly indicative of strain–oxygen stoichiometry coupling.  more » « less
Award ID(s):
1709781
PAR ID:
10597410
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
American Institute of Physics
Date Published:
Journal Name:
AIP Advances
Volume:
11
Issue:
4
ISSN:
2158-3226
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract Spin‐state transitions are an important research topic in complex oxides with the diverse magnetic states involved. In particular, the low‐spin to high‐spin transition in LaCoO3thin films has drawn a wide range of attention due to the emergent ferromagnetic state. Although various mechanisms (e.g., structural distortion, oxygen‐vacancy formation, spin‐state ordering) have been proposed, an understanding of what really underlies the emergent ferromagnetism remains elusive. Here, the ferromagnetism in LaCoO3thin films is systematically modulated by varying the oxygen pressure during thin‐film growth. Although the samples show dramatic different magnetization, their cobalt valence state and perovskite crystalline structure remain almost unchanged, ruling out the scenarios of both oxygen‐vacancy and spin‐ordering. This work provides compelling evidence that the tetragonal distortion due to the tensile strain significantly modifies the orbital occupancy, leading to a low‐spin to high‐spin transition with emergent ferromagnetism, while samples grown at reduced pressure demonstrate a pronounced lattice expansion due to cation‐off‐stoichiometry, which suppresses the tetragonal distortion and the consequent magnetization. This result not only provides important insight for the understanding of exotic ferromagnetism in LaCoO3thin films, but also identifies a promising strategy to design electronic states in complex oxides through cation‐stoichiometry engineering. 
    more » « less
  2. The ability to accommodate multiple principal cations within a single crystallographic structure makes high entropy oxides (HEOs) ideal systems for exploring new composition–property relationships. In this work, the high-entropy design strategy is extended to strained single-crystal HEO-manganite (HEO-Mn) thin films. Phase-pure orthorhombic films of (Gd0.2La0.2Nd0.2Sm0.2Sr0.2)MnO3 were deposited on three different single-crystal substrates: SrTiO3 (STO) (100), NdGaO3 (110), and LaAlO3 (LAO) (100), each inducing different degrees of epitaxial strain. Fully coherent growth of the thin films is observed in all cases, despite the high degree of lattice mismatch between HEO-Mn and LAO. Magnetometry measurements reveal distinct differences in the magnetic properties between epitaxially strained HEO-Mn thin films and their bulk crystalline HEO counterparts. In particular, the bulk polycrystalline HEO-Mn shows two magnetic transitions as opposed to a single one observed in epitaxial thin films. Moreover, the HEO-Mn film deposited on LAO exhibits a significant reduction in the Curie temperature, which is attributed to the strong variation of the in-plane lattice parameter along the thickness of the film and the resulting changes in the Mn–O–Mn bond geometry. Thus, this preliminary study demonstrates the potential of combining high entropy design with strain engineering to tailor the structure and functionality of perovskite manganites. 
    more » « less
  3. This report is on the nature of strain in thin films of yttrium iron garnet (YIG) on yttrium aluminum garnet (YAG) substrates due to film-substrate lattice mismatch and the resulting induced magnetic anisotropy. Films with thickness 55 nm to 380 nm were deposited on (100), (110), and (111) YAG substrates using pulsed laser deposition (PLD) techniques and characterized by structural and magnetic characterization techniques. The in-plane strain determined to be compressive using X-ray diffraction (XRD). It varied from −0.12% to −0.98% and increased in magnitude with increasing film thickness and was relatively large in films on (100) YAG. The out-of-plane strain was tensile and also increased with increasing film thickness. The estimated strain-induced magnetic anisotropy field, found from XRD data, was out of plane; its value increased with film thickness and ranged from 0.47 kOe to 3.96 kOe. Ferromagnetic resonance (FMR) measurements at 5 to 21 GHz also revealed the presence of a perpendicular magnetic anisotropy that decreased with increasing film thickness and its values were smaller than values obtained from XRD data. The PLD YIG films on YAG substrates exhibiting a perpendicular anisotropy field have the potential for use in self-biased sensors and high-frequency devices. 
    more » « less
  4. Abstract This work focuses on the nature of magnetic anisotropy in 2.5–16 micron thick films of nickel ferrite (NFO) grown by liquid phase epitaxy (LPE). The technique, ideal for rapid growth of epitaxial oxide films, was utilized for films on (100) and (110) substrates of magnesium gallate (MGO). The motivation was to investigate the dependence of the growth induced anisotropy field on film thickness since submicron films of NFO were reported to show a very high anisotropy. The films grown at 850–875 C and subsequently annealed at 1000 C were found to be epitaxial, with the out-of-plane lattice constant showing unanticipated decrease with increasing film thickness and the estimated in-plane lattice constant increasing with the film thickness. The uniaxial anisotropy field H σ , estimated from X-ray diffraction data, ranged from 2.8–7.7 kOe with the films on (100) MGO having a higher H σ value than for the films on (110) MGO. Ferromagnetic resonance (FMR) measurements for in-plane and out-of-plane static magnetic field were utilized to determine both the magnetocrystalline the anisotropy field H 4 and the uniaxial anisotropy field H a . Values of H 4 range from −0.24 to −0.86 kOe. The uniaxial anisotropy field H a was an order of magnitude smaller than H σ and it decreased with increasing film thickness for NFO films on (100) MGO, but H a increased with film thickness for films on (110) MGO substrates. These observations indicate that the origin of the induced anisotropy could be attributed to several factors including (i) strain due to mismatch in the film-substrate lattice constants, (ii) possible variations in the bond lengths and bond angles in NFO during the growth process, and (iii) the strain arising from mismatch in the thermal expansion coefficients of the film and the substrate due to the high growth and annealing temperatures involved in the LPE technique. The LPE films of NFO on MGO substrates studied in this work are of interest for use in high frequency devices. 
    more » « less
  5. Abstract Conjugated polymers consist of complex backbone structures and side‐chain moieties to meet various optoelectronic and processing requirements. Recent work on conjugated polymers has been devoted to studying the mechanical properties and developing new conjugated polymers with low modulus and high‐crack onset strain, while the thin film mechanical stability under long‐term external tensile strain is less investigated. Here we performed direct mechanical stress relaxation tests for both free‐standing and thin film floated on water surface on both high‐Tgand low‐Tgconjugated polymers, as well as a reference nonconjugated sample, polystyrene. We measured thin films with a range of film thickness from 38 to 179 nm to study the temperature and thickness effect on thin film relaxation, where an apparent enthalpy–entropy compensation effect for glassy polymer PS and PM6 thin films was observed. We also compared relaxation times across three different conjugated polymers and showed that both crystalline morphology and higher modulus reduce the relaxation rate besides higher glass transition temperature. Our work provides insights into the mechanical creep behavior of conjugated polymers, which will have an impact on the future design of stable functional organic electronics. 
    more » « less