Semiconductor Zn-based nanomaterials have emerged as promising agents for the photocatalytic degradation of organic pollutants in wastewater treatment. However, achieving efficient synthesis protocols capable of rapidly producing small structures directly in aqueous environments remains challenging. Microwave-assisted synthesis presents a viable solution by enabling one-step particle generation swiftly and directly in water through increased pressure, thereby easily elevating the boiling point. This study investigates the microwave-assisted one-step synthesis of pure and iron-doped ZnS nanoparticles and assesses their efficacy in photodegrading Quinoline Yellow (QY) in aqueous suspensions. The results demonstrate a significant degradation of QY in the presence of 1% iron-doped ZnS nanoparticles, achieving approximately 66.3% degradation with 500 ppm of doped nanoparticles after 270 min. These findings highlight the considerable potential of 1% iron-doped ZnS nanoparticles as effective nanocatalysts.
more »
« less
This content will become publicly available on May 15, 2026
Degradation of cephalexin in the presence of pure and doped ZnS nanostructures.
The rapid discharge of antibiotic pollutants from pharmaceutical industries into natural water sources poses a significant threat to human health and the environment. Conventional water treatment methods often fail to effectively remove these contaminants, leading to a pressing need for eco-friendly degradation approaches. This study focused on synthesizing pure and iron-doped zinc sulfide (ZnS) nanoparticles using a microwave-assisted technique in aqueous solution to evaluate their photocatalytic efficiency in degrading the antibiotic cephalexin. High-resolution transmission electron microscopy (TEM) characterized the synthesized nanoparticles, revealing crystalline structures approximately 5 nm in size. The photocatalytic capacity was assessed using a spectrophotometric method, demonstrating that both pure and iron-doped ZnS nanostructures exhibit higher efficiency in degrading cephalexin under UV irradiation. These findings underscore the potential of ZnS nanostructures for photocatalytic applications in environmental remediation, particularly in degrading resistant antibiotic pollutants, highlighting their role in addressing organic pollution in water sources.
more »
« less
- Award ID(s):
- 2313252
- PAR ID:
- 10601325
- Publisher / Repository:
- CEIBA-UPR
- Date Published:
- Journal Name:
- Ceiba
- ISSN:
- 0885-9906
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
This study reports the synthesis, structural characterization, adsorption studies, nanoscale interaction, and photocatalytic application of pure and Fe-doped ZnS quantum dots for the degradation of the antibiotic cefalexin in aqueous solution. Nanoparticles were synthesized via the microwave-assisted method, and Fe doping was introduced at a 1% molar ratio. HRTEM images confirmed quasi-spherical morphology and high crystallinity, with particle sizes averaging 2.4 nm (pure) and 3.5 nm (doped). XRD analysis showed a consistent cubic ZnS structure. UV-vis spectra showed strong absorption at 316 nm for both samples, and PL measurements revealed emission quenching upon Fe doping. Photocatalytic tests under UV light demonstrated significantly higher degradation rates of 10 ppm cefalexin with Fe-doped ZnS, reaching near-complete removal within 90 min. Adsorption experiments revealed higher affinity and adsorption capacity of Fe-doped ZnS toward cefalexin compared to pure ZnS, as demonstrated by the Freundlich isotherm analyses, contributing significantly to enhanced photocatalytic degradation performance. High-resolution QTOF LC-MS analysis confirmed the breakdown of the β-lactam and thiazolidine rings of cefalexin and the formation of low-mass degradation products, including fragments at m/z 122.0371, 116.0937, and 318.2241. These findings provide strong evidence for the structural destruction of the antibiotic and validate the enhanced photocatalytic performance of Fe-doped ZnS.more » « less
-
Abstract Membrane‐based technologies are attractive for remediating oily wastewater because they are relatively energy‐efficient and are applicable to a wide range of industrial effluents. For complete treatment of oily wastewater, removing dissolved contaminants from the water phase is typically followed by adsorption onto an adsorbent, which complicates the process. Here, an in‐air superhydrophilic and underwater superoleophobic membrane‐based continuous separation of surfactant‐stabilized oil‐in‐water emulsions and in situ decontamination of water by visible‐light‐driven photocatalytic degradation of dissolved organic contaminants is reported. The membrane is fabricated by utilizing a thermally sensitized stainless steel mesh coated with visible light absorbing iron‐doped titania nanoparticles. Post annealing of the membrane can enhance the adhesion of nanoparticles to the membrane surface by formation of a bridge between them. An apparatus that enables continuous separation of surfactant‐stabilized oil‐in‐water emulsion and in situ photocatalytic degradation of dissolved organic matter in the water‐rich permeate upon irradiation of visible light on the membrane surface with greater than 99% photocatalytic degradation is developed. The membrane demonstrates the recovery of its intrinsic water‐rich permeate flux upon continuous irradiation of light after being contaminated with oil. Finally, continuous oil−water separation and in situ water decontamination is demonstrated by photocatalytically degrading model toxins in water‐rich permeate.more » « less
-
Abstract The actual incorporation of dopant species into the ZnS Quantum Dots (QDs) host lattice will induce structural defects evidenced by a red shift in the corresponding exciton. The doping should create new intermediate energetic levels between the valence and conduction bands of the ZnS and affect the electron-hole recombination. These trap states would favour the energy transfer processes involved with the generation of cytotoxic radicals, so-called Reactive Oxygen Species, opening the possibility to apply these nanomaterials in cancer research. Any synthesis approach should consider the direct formation of the QDs in biocompatible medium. Accordingly, the present work addresses the microwave-assisted aqueous synthesis of pure and doped ZnS QDs. As-synthesized quantum dots were fully characterized on a structural, morphological and optical viewpoint. UV-Vis analyzes evidenced the excitonic peaks at approximately 310 nm, 314 nm and 315 nm for ZnS, Cu-ZnS and Mn-ZnS, respectively, Cu/Zn and Mn/Zn molar ratio was 0.05%. This indicates the actual incorporation of the dopant species into the host lattice. In addition, the Photoluminescence spectrum of non-doped ZnS nanoparticles showed a high emission peak that was red shifted when Mn 2+ or Cu 2+ were added during the synthesis process. The main emission peak of non-doped ZnS, Cu-doped ZnS and Mn-doped ZnS were observed at 438 nm, 487 nm and 521 nm, respectively. Forthcoming work will address the capacity of pure and Cu-, Mn-ZnS quantum dots to generate cytotoxic Reactive Oxygen Species for cancer treatment applications.more » « less
-
Membrane-based separation technologies are the cornerstone of remediating unconventional water sources, including brackish and industrial or municipal wastewater, as they are relatively energy-efficient and versatile. However, membrane fouling by dissolved and suspended substances in the feed stream remains a primary challenge that currently prevents these membranes from being used in real practices. Thus, we directly address this challenge by applying a superhydrophilic and oleophobic coating to a commercial membrane surface which can be utilized to separate and desalinate an oil and saline water mixture, in addition to photocatalytically degrading the organic substances. We fabricated the photocatalytic membrane by coating a commercial membrane with an ultraviolet (UV) light-curable adhesive. Then, we sprayed it with a mixture of photocatalytic nitrogen-doped titania (N-TiO2) and perfluoro silane-grafted silica (F-SiO2) nanoparticles. The membrane was placed under a UV light, which resulted in a chemically heterogeneous surface with intercalating high and low surface energy regions (i.e., N-TiO2 and F-SiO2, respectively) that were securely bound to the commercial membrane surface. We demonstrated that the coated membrane could be utilized for continuous separation and desalination of an oil–saline water mixture and for simultaneous photocatalytic degradation of the organic substances adsorbed on the membrane surface upon visible light irradiation.more » « less