Title: One-step Aqueous Synthesis of Zn-based Quantum Dots as Potential Generators of Reactive Oxygen Species
Abstract The actual incorporation of dopant species into the ZnS Quantum Dots (QDs) host lattice will induce structural defects evidenced by a red shift in the corresponding exciton. The doping should create new intermediate energetic levels between the valence and conduction bands of the ZnS and affect the electron-hole recombination. These trap states would favour the energy transfer processes involved with the generation of cytotoxic radicals, so-called Reactive Oxygen Species, opening the possibility to apply these nanomaterials in cancer research. Any synthesis approach should consider the direct formation of the QDs in biocompatible medium. Accordingly, the present work addresses the microwave-assisted aqueous synthesis of pure and doped ZnS QDs. As-synthesized quantum dots were fully characterized on a structural, morphological and optical viewpoint. UV-Vis analyzes evidenced the excitonic peaks at approximately 310 nm, 314 nm and 315 nm for ZnS, Cu-ZnS and Mn-ZnS, respectively, Cu/Zn and Mn/Zn molar ratio was 0.05%. This indicates the actual incorporation of the dopant species into the host lattice. In addition, the Photoluminescence spectrum of non-doped ZnS nanoparticles showed a high emission peak that was red shifted when Mn 2+ or Cu 2+ were added during the synthesis process. The main emission peak of non-doped ZnS, Cu-doped ZnS and Mn-doped ZnS were observed at 438 nm, 487 nm and 521 nm, respectively. Forthcoming work will address the capacity of pure and Cu-, Mn-ZnS quantum dots to generate cytotoxic Reactive Oxygen Species for cancer treatment applications.  more » « less
Award ID(s):
1846628
NSF-PAR ID:
10094661
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
MRS Advances
Volume:
4
Issue:
07
ISSN:
2059-8521
Page Range / eLocation ID:
399 to 404
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ( , Small)
    Abstract

    Copper indium sulfide (CIS) colloidal quantum dots (QDs) are a promising candidate for commercially viable QD‐based optical applications, for example as colloidal photocatalysts or in luminescent solar concentrators (LSCs). CIS QDs with good photoluminescence quantum yields (PLQYs) and tunable emission wavelength via size and composition control are previously reported. However, developing an understanding and control over the growth of electronically passivating inorganic shells would enable further improvements of the photophysical properties of CIS QDs. To improve the optical properties of CIS QDs, the focus is on the growth of inorganic shells via the popular metal‐carboxylate/alkane thiol decomposition reaction. 1) The role of Zn‐carboxylate and Zn‐thiolate on the formation of ZnS shells on Cu‐deficient CIS (CDCIS) QDs is studied, 2) this knowledge is leveraged to yield >90% PLQY CDCIS/ZnS core/shell QDs, and 3) a mechanism for ZnS shells grown from zinc‐carboxylate/alkane thiol decomposition is proposed.

     
    more » « less
  2. ; ; ; ; ; ( , Advanced Materials)
    Abstract

    Doped heavy metal‐free III–V semiconductor nanocrystal quantum dots (QDs) are of great interest both from the fundamental aspects of doping in highly confined structures, and from the applicative side of utilizing such building blocks in the fabrication of p–n homojunction devices. InAs nanocrystals (NCs), that are of particular relevance for short‐wave IR detection and emission applications, manifest heavy n‐type character poising a challenge for their transition to p‐type behavior. The p‐type doping of InAs NCs is presented with Zn – enabling control over the charge carrier type in InAs QDs field effect transistors. The post‐synthesis doping reaction mechanism is studied for Zn precursors with varying reactivity. Successful p‐type doping is achieved by the more reactive precursor, diethylzinc. Substitutional doping by Zn2+replacing In3+is established by X‐ray absorption spectroscopy analysis. Furthermore, enhanced near infrared photoluminescence is observed due to surface passivation by Zn as indicated from elemental mapping utilizing high‐resolution electron microscopy corroborated by X‐ray photoelectron spectroscopy study. The demonstrated ability to control the carrier type, along with the improved emission characteristics, paves the way towards fabrication of optoelectronic devices active in the short‐wave infrared region utilizing heavy‐metal free nanocrystal building blocks.

     
    more » « less
  3. ; ; ; ; ; ; ; ; ; ; et al ( , Advanced Functional Materials)
    Abstract

    All‐inorganic CsPbI3quantum dots (QDs) have shown great potential in photovoltaic applications. However, their performance has been limited by defects and phase stability. Herein, an anion/cation synergy strategy to improve the structural stability of CsPbI3QDs and reduce the pivotal iodine vacancy (VI) defect states is proposed. The Zn‐doped CsPbI3(Zn:CsPbI3) QDs have been successfully synthesized employing ZnI2as the dopant to provide Zn2+and extra I−. Theoretical calculations and experimental results demonstrate that the Zn:CsPbI3QDs show better thermodynamic stability and higher photoluminescence quantum yield (PLQY) compared to the pristine CsPbI3QDs. The doping of Zn in CsPbI3QDs increases the formation energy and Goldschmidt tolerance factor, thereby improving the thermodynamic stability. The additional I−helps to reduce theVIdefects during the synthesis of CsPbI3QDs, resulting in the higher PLQY. More importantly, the synergistic effect of Zn2+and I−in CsPbI3QDs can prevent the iodine loss during the fabrication of CsPbI3QD film, inhibiting the formation of newVIdefect states in the construction of solar cells. Consequently, the anion/cation synergy strategy affords the CsPbI3quantum dot solar cells (QDSC) a power conversion efficiency over 16%, which is among the best efficiencies for perovskite QDSCs.

     
    more » « less
  4. ; ; ( , Journal of Materials Chemistry C)
    The utility of colloidal semiconductor quantum dots as a source of photons and charge carriers for photonic and photovoltaic applications has created a large field of research focused on tailoring and broadening their functionality beyond what an exciton can provide. One approach towards expanding the range of characteristics of photons and charge carriers from quantum dots is through doping impurity ions ( e.g. Mn 2+ , Cu + , and Yb 3+ ) in the host quantum dots. In addition to the progress in synthesis enabling fine control of the structure of the doped quantum dots, a mechanistic understanding of the underlying processes correlated with the structure has been crucial in revealing the full potential of the doped quantum dots as the source of photons and charge carriers. In this review, we discuss the recent progress made in gaining microscopic understanding of the photophysical pathways that give rise to unique dopant-related luminescence and the generation of energetic hot electrons via exciton-to-hot electron upconversion. 
    more » « less
  5. ; ; ; ; ( , Environmental Science: Nano)
    null (Ed.)
    Nutrient nitrogen (N) and phosphorus (P) recovery from wastewater is an important challenge for enhanced environmental sustainability. Herein we report the synthesis and properties of mesoporous MgO nanoparticles doped with copper (Cu), iron (Fe), and zinc (Zn) as an alternative low-solubility high-abundance magnesium (Mg) source for crystalline struvite precipitation from nutrient-laden wastewater. Undoped MgO was shown to have the fastest phosphate (PO 4 3− ) adsorption kinetics with a k 2 value of 0.9 g g −1 min −1 at room temperature. The corresponding rate constant decreased for Cu–MgO (0.175 g g −1 min −1 ), Zn–MgO (0.145 g g −1 min −1 ), and Fe–MgO (0.02 g g −1 min −1 ). Undoped MgO resulted in the highest PO 4 3− removal at 94%, while Cu–MgO, Fe–MgO, and Zn–MgO resulted in 90%, 66% and 66%, respectively, under equivalent reaction conditions. All dopants resulted in the production of struvite as the main product with the incorporation of the transition metals into the struvite crystal lattice. X-ray absorption spectroscopy (XAS) showed that the majority of the Cu, Fe, and Zn were primarily in the +2, +3, and +2 oxidation states, respectively. XAS also showed that the Cu atoms exist in elongated octahedral coordination, while Fe was shown to be in octahedral coordination. Zn was shown to be in a complex disordered environment with octahedral sites coexisting with the majority of the tetrahedral sites. Finally, X-ray photoelectron spectroscopy data suggest a two-fold struvite surface enrichment with dopant metals, with Cu exhibiting an interesting new local binding structure. The dopant concentrations utilized were consistent with those found in natural Mg minerals, suggesting that (a) utilizing natural mineral periclase as the Mg source for struvite production can result in struvite formation, albeit at the expense of the reaction kinetics and overall yields, while also (b) supplying essential micronutrients, such as Zn and Cu, necessary for balanced nutrient uptake. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email