To promote the sustainable development of eco-efficient calcium sulfoaluminate (CSA) cements through the partial replacement of the CSA clinker with supplementary cementitious waste products, the effects of coal fly ashes on the early-age and mature-age properties of a calcium sulfoaluminate (CSA)-based cement paste were investigated. The impacts of both Class C and Class F fly ashes on the rheological properties, hydration kinetics, and compressive strength development of CSA cement paste were studied. Rheology-based workability parameters, representing the rate of loss of flowability, the rate of hardening, and the placement limit, were characterized for the pastes prepared with fixed water-to-cement (w/c) and fixed water-to-binder (w/b) ratios. The results indicate a slight improvement in the workability of the CSA paste by fly ash addition at a fixed w/b ratio. The isothermal calorimetry studies show a higher heat of hydration for the Class C fly ash-modified systems compared to the Class F-modified systems. The results show that fly ash accelerates the hydration of the calcium sulfoaluminate cement pastes, chiefly due to the filler effects, rather than the pozzolanic effects. In general, ettringite is stabilized more by the addition of Class F fly ash than Class C fly ash. Both fly ashes reduced the 1-day compressive strength, but increased the 28-day strength of the CSA cement paste; meanwhile, the Class C modified pastes show a higher strength than Class F, which is attributed to the higher degree of reaction and potentially more cohesive binding C-S-H-based gels formed in the Class C fly ash modified systems. The results provide insights that support that fly ash can be employed to improve the performance of calcium sulfoaluminate cement pastes, while also enhancing cost effectiveness and sustainability.
more »
« less
This content will become publicly available on March 11, 2026
Lifecycle implications and mechanical properties of carbonated biomass ashes as carbon-storing supplementary cementitious materials
Methods to sequester and store atmospheric CO2 are critical to combat climate change. Alkaline-rich bioashes are potential carbon fixing materials. This work investigates potential co-benefits from mineralizing carbon in biomass ashes and partially replacing high embodied greenhouse gas (GHG) Portland cement (PC) in cement-based materials with these ashes. Specifically, rice hull ash (RHA), wheat straw ash (WSA), and sugarcane bagasse ash (SBA) were treated to mineralize carbon, and their experimental carbon content was compared to modeled potential carbonation. To understand changes in the cement-based storage materials, mortars made with CO2-treated WSA and RHA were experimentally compared to PC-only mortars and mortars made with ashes without prior CO2 treatment. Life cycle assessment methodology was applied to understand potential reductions in GHG emissions. The modeled carbonation was ∼18 g-CO2/kg-RHA and ∼180 g-CO2/kg-WSA. Ashes oxidized at 500 °C had the largest measured carbon content (5.4 g-carbon/kg-RHA and 35.3 g-carbon/kg-WSA). This carbon appeared to be predominantly residual from the biomass. Isothermal calorimetry showed RHA-PC pastes had similar heat of hydration to PC-pastes, while WSA-PC pastes exhibited an early (at ∼1.5 min) endothermic dip. Mortars with 5 % and 15 % RHA replacement had 1–12 % higher compressive strength at 28 days than PC-only mortars, and milled WSA mortars with 5 % replacement had 3 % higher strength. A loss in strength was noted for the milled 15 % WSA, the CO2-treated 5 %, and the 15 % WSA mortars. Modeled reductions in GHG emissions from CO2-treated ashes were, however, marginal (<1 %) relative to the untreated ashes.
more »
« less
- Award ID(s):
- 2033966
- PAR ID:
- 10608141
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Biomass and Bioenergy
- Volume:
- 197
- Issue:
- C
- ISSN:
- 0961-9534
- Page Range / eLocation ID:
- 107772
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Amziane, S; Merta, I; Page, J. (Ed.)Portland cement is one of the most used materials on earth. Its annual production is responsible for approximately 7% of global carbon dioxide (CO2) emissions. These emissions are primarily associated with (1) the burning of fossil fuels to heat cement kilns and (2) the release of CO2 during limestone calcination. One proposed strategy for CO2 reduction includes the use of functional limestone fillers, which reduce the amount of portland cement in concrete without compromising strength. This study investigated the effect of using renewable, CO2-storing, biogenic CaCO3 produced by E. huxleyi as limestone filler in portland limestone cements (PLCs). Biogenic CaCO3 was used to synthesize PLCs with 0, 5, 15, and 35% limestone replacement of portland cement. The results substantiate that the particle sizes of the biogenic CaCO3 were significantly smaller and the surface areas significantly larger than that of reagent grade CaCO3. X-ray diffraction indicated no differences in mineralogy between reagent-grade and biogenic CaCO3. The use of biogenic CaCO3 as a limestone filler led to (i) increased water demand at the higher replacements, which was countered by using a superplasticizer, and (ii) enhanced nucleation during cement hydration, as measured by isothermal conduction calorimetry. The 7-day compressive strengths of the PLC pastes were measured using mechanical testing. Enhanced nucleation effects were observed for PLC samples containing biogenic CaCO3. 7-day compressive strength of the PLCs produced using biogenic CaCO3 were also enhanced compared to PLCs produced using reagent-grade CaCO3 due to the nucleation effect. This study illustrates an opportunity for using CO2-storing, biogenic CaCO3 to enhance mechanical properties and CO2 storage in PLCs containing biologically architected CaCO3.more » « less
-
While a large amount of research has been performed in recent years on characterizing wildfire ashes and determining the hydrological properties of slopes post-wildfire, fewer studies have concentrated on the overall engineering behavior of ash. This study addresses this need by examining the compaction, shear strength, and hydraulic behavior of wildfire ash and ash/soil layered specimens. Unique chemical and physical characteristics of wildfire ashes were shown to influence the ash engineering behavior. Ashes in the as-received condition have a silty sand grain size distribution with higher than expected surface areas (>1 m2/g). Chemically, ashes contained silica, aluminum, calcium (in the form of carbonates) and residual organic carbon from incomplete combustion. Maximum dry unit weights ranged from 13 – 16 kN/m3 at optimum moisture contents between 20 and 30%. Hydraulic conductivity of samples varied between 10^-4 and 10^-5 cm/s. A wet deposited layer of fine-grained ash on top of compacted sand reduced the hydraulic conductivity of sand by 1 – 3 orders of magnitude. Shear strength of ash/sand layered specimens demonstrated that ash was fairly stiff, with an average friction angle of 28 degrees. Void ratios of specimens were consistently higher than expected for a silty sand fabric (usually above 1.0). Ash particles were irregular in shape with fibrous textures and had electrostatic attractive tendencies. The authors suspect that the unique chemistries present in ash (notably carbonates and organic char) contributed to the loose fabric structure and engineering properties that were atypical of a silty sand grain size distributionmore » « less
-
This paper studies the alkali-silica reaction (ASR) in rapid-strength belitic calcium sulfoaluminate (BCSA) cement systems. Theoretically, its low alkalinity and high alumina content should make BCSA less prone to ASR than portland cement (PC), but little experimental evidence has been published, and the theorized mechanisms have not been examined critically. We examine this problem using expansion tests, microstructural analysis, and pore solution analysis. Accelerated expansion tests show increased expansion in BCSA mortars with reactive aggregates, but we argue that the test conditions are unsuitable for the cement. Long-term expansion tests show a significant reduction in expansion in BCSA mortars with reactive aggregates, but later-age measurements still exceed ASTM C1778 limits and microstructural investigations indicate ASR damage. Curiously, BCSA mortars with nonreactive aggregates also expanded significantly, but no ASR damage was observed. BCSA pore solutions had ten times more aluminum than PC and one-tenth as much calcium. While the pH was sufficiently high to initiate ASR, the alkali reserves can be half or less than in PC. Overall, BCSA cement is not immune to ASR, but it is more resistant than PC. This is mostly related to the lower alkalinity of the cement and, to a lesser degree, to the abundance of alumina and shortage of soluble calcium.more » « less
-
Pervious concrete, which has recently found new applications in buildings, is both energy- and carbon-intensive to manufacture. However, similar to normal concrete, some of the initial CO2 emissions associated with pervious concrete can be sequestered through a process known as carbonation. In this work, the theoretical formulation and application of a mathematical model for estimating the carbon dioxide (CO2) sequestration potential of pervious concrete is presented. Using principles of cement and carbonation chemistry, the model related mixture proportions of pervious concretes to their theoretical in situ CO2 sequestration potential. The model was subsequently employed in a screening life cycle assessment (LCA) to quantify the percentage of recoverable CO2 emissions—namely, the ratio of in situ sequesterable CO2 to initial cradle-to-gate CO2 emissions—for common pervious concrete mixtures. Results suggest that natural carbonation can recover up to 12% of initial CO2 emissions and that CO2 sequestration potential is maximized for pervious concrete mixtures with (i) lower water-to-cement ratios, (ii) higher compressive strengths, (iii) lower porosities, and (iv) lower hydraulic conductivities. However, LCA results elucidate that mixtures with maximum CO2 sequestration potential (i.e., mixtures with high cement contents and CO2 recoverability) emit more CO2 from a net-emissions perspective, despite their enhanced in situ CO2 sequestration potential.more » « less