Title: Accelerating Discovery of Solid‐State Thin‐Film Metal Dealloying for 3D Nanoarchitecture Materials Design through Laser Thermal Gradient Treatment
Abstract Thin‐film solid‐state metal dealloying (thin‐film SSMD) is a promising method for fabricating nanostructures with controlled morphology and efficiency, offering advantages over conventional bulk materials processing methods for integration into practical applications. Although machine learning (ML) has facilitated the design of dealloying systems, the selection of key thermal treatment parameters for nanostructure formation remains largely unknown and dependent on experimental trial and error. To overcome this challenge, a workflow enabling high‐throughput characterization of thermal treatment parameters is demonstrated using a laser‐based thermal treatment to create temperature gradients on single thin‐film samples of Nb‐Al/Sc and Nb‐Al/Cu. This continuous thermal space enables observation of dealloying transitions and the resulting nanostructures of interest. Through synchrotron X‐ray multimodal and high‐throughput characterization, critical transitions and nanostructures can be rapidly captured and subsequently verified using electron microscopy. The key temperatures driving chemical reactions and morphological evolutions are clearly identified. While the oxidation may influence nanostructure formation during thin‐film treatment, the dealloying process at the dealloying front involves interactions solely between the dealloying elements, highlighting the availability and viability of the selected systems. This approach enables efficient exploration of the dealloying process and validation of ML predictions, thereby accelerating the discovery of thin‐film SSMD systems with targeted nanostructures.  more » « less
Award ID(s):
1752839
PAR ID:
10609384
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ;
Publisher / Repository:
Wiley
Date Published:
Journal Name:
Small
ISSN:
1613-6810
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract Solid‐state metal dealloying (SSMD) is a promising method for fabricating nanoscale metallic composites and nanoporous metals across a range of materials. Thin‐film SSMD is particularly attractive due to its ability to create fine features via solid‐state interfacial reactions within a thin‐film geometry, which can be integrated into devices for various applications. This work examines a new dealloying couple, namely the Nb–Al alloy with the dealloying agent Sc, as previously predicted in the machine‐learning (ML) models. Prior ML predictions aimed to guide the design of nanoarchitectured materials through dealloying, relying on intuition‐driven discovery within a large parameter space. However, this work reveals that at the nanoscale, the involvement of oxygen in thin film processing may instead drive the dealloying process, resulting in the formation of bicontinuous nanostructures similar to those formed by metal‐agent dealloying. The phase evolution, as well as chemical and morphological changes, are closely analyzed using a combination of X‐ray absorption spectroscopy, diffraction, and scanning transmission electron microscopy to understand the mechanisms behind nanostructure formation. The findings suggest a potential pathway for utilizing oxygen to drive the formation of bicontinuous metal–metal oxide nanocomposites, paving the way for further development of functional nanoporous materials in diverse fields. 
    more » « less
  2. Thin-film solid-state interfacial dealloying (thin-film SSID) is an emerging technique to design nanoarchitecture thin films. The resulting controllable 3D bicontinuous nanostructure is promising for a range of applications including catalysis, sensing, and energy storage. Using a multiscale microscopy approach, we combine X-ray and electron nano-tomography to demonstrate that besides dense bicontinuous nanocomposites, thin-film SSID can create a very fine (5–15 nm) nanoporous structure. Not only is such a fine feature among one of the finest fabrications by metal-agent dealloying, but a multilayer thin-film design enables creating nanoporous films on a wider range of substrates for functional applications. Through multimodal synchrotron diffraction and spectroscopy analysis with which the materials’ chemical and structural evolution in this novel approach is characterized in details, we further deduce that the contribution of change in entropy should be considered to explain the phase evolution in metal-agent dealloying, in addition to the commonly used enthalpy term in prior studies. The discussion is an important step leading towards better explaining the underlying design principles for controllable 3D nanoarchitecture, as well as exploring a wider range of elemental and substrate selections for new applications. 
    more » « less
  3. Nanostructured materials and nanolattices with high porosity can have novel optical and mechanical properties that are attractive for nanophotonic devices. One existing challenge is the integration of microstructures that can be used as waveguides or electrodes on such nanostructures without filling in the pores. This study investigates the fabrication of TiO2 microstructures on nanolattices using a stencil mask. In this approach, the nanostructures are planarized with a polymer film while the microstructures are patterned in a sequential shadow deposition step. Our results demonstrate the successful fabrication of a “dog-bone” microstructure with 400 μm length, 100 μm width, and 30–560 nm thicknesses on nanostructure with 390 and 500 nm period. The experimental results show that cracks can form in the microstructures, which can be attributed to residual stress and the thermal annealing cycle. A key finding is that the film cracks decrease as the TiO2 layer becomes thinner, highlighting an important relationship between grain size distribution and the film thickness. The mechanical stability of the underlying nanolattices also plays a key role, where interconnected architecture mitigated the crack formation when compared with isolated structures. The demonstrated fabrication process can lead to integrated waveguides and microelectrodes on nanolattices, which can find applications for next-generation photonic and electronic devices. 
    more » « less
  4. In this investigation, we explore the impact of the Nb–Al ratio on the microstructural and mechanical properties of high-entropy superalloys (HESAs), focusing on hierarchical microstructures. Utilizing a series of HESAs with varying Nb–Al ratios, our study employs advanced characterization techniques, including differential scanning calorimetry (DSC) for thermal analysis, electron probe micro-analyzer (EPMA) for compositional analysis for the design of a homogenization treatment at 1500 K/24 h. Transmission electron microscopy (TEM) reveals that the increasing Nb–Al ratio refines the γ' precipitates and influences the size and volume fraction of embedded hierarchical γ particles. ThermoCalc equilibrium phase analysis and Vegard's-law calculations reveal a minimal lattice misfit between these phases, highlighting the interplay between Nb–Al ratio and phase stability. The increasing Nb–Al ratio inhibits the formation of hierarchical γ particles. We observe an enhancement in hardness from 433 HV to 492 HV with an increasing Nb–Al ratio. This study provides valuable insights into the role of Nb and the Nb–Al ratio in HESAs with hierarchical microstructures, demonstrating its significant influence on γ particle formation within γ' precipitates and mechanical strength. The findings advance our understanding of alloy design and pave the way for developing advanced HESAs for high-temperature applications. 
    more » « less
  5. Abstract Quasi‐2D metal halide perovskites (MHPs) are an emerging material platform for sustainable functional optoelectronics, but the uncontrollable, broad phase distribution remains a critical challenge for applications. Nevertheless, the basic principles for controlling phases in quasi‐2D MHPs remain poorly understood, due to the rapid crystallization kinetics during the conventional thin‐film fabrication process. Herein, a high‐throughput automated synthesis‐characterization‐analysis workflow is implemented to accelerate material exploration in formamidinium (FA)‐based quasi‐2D MHP compositional space, revealing the early‐stage phase growth behaviors fundamentally determining the phase distributions. Upon comprehensive exploration with varying synthesis conditions including 2D:3D composition ratios, antisolvent injection rates, and temperatures in an automated synthesis‐characterization platform, it is observed that the prominentn= 2 2D phase restricts the growth kinetics of 3D‐like phases—α‐FAPbI3MHPs with spacer‐coordinated surface—across the MHP compositions. Thermal annealing is a critical step for proper phase growth, although it can lead to the emergence of unwanted local PbI2crystallites. Additionally, fundamental insights into the precursor chemistry associated with spacer‐solvent interaction determining the quasi‐2D MHP morphologies and microstructures are demonstrated. The high‐throughput study provides comprehensive insights into the fundamental principles in quasi‐2D MHP phase control, enabling new control of the functionalities in complex materials systems for sustainable device applications. 
    more » « less