Abstract Due to their low damage tolerance, engineering ceramic foams are often limited to non-structural usages. In this work, we report that stereom, a bioceramic cellular solid (relative density, 0.2–0.4) commonly found in the mineralized skeletal elements of echinoderms (e.g., sea urchin spines), achieves simultaneous high relative strength which approaches the Suquet bound and remarkable energy absorption capability (ca. 17.7 kJ kg−1) through its unique bicontinuous open-cell foam-like microstructure. The high strength is due to the ultra-low stress concentrations within the stereom during loading, resulted from their defect-free cellular morphologies with near-constant surface mean curvatures and negative Gaussian curvatures. Furthermore, the combination of bending-induced microfracture of branches and subsequent local jamming of fractured fragments facilitated by small throat openings in stereom leads to the progressive formation and growth of damage bands with significant microscopic densification of fragments, and consequently, contributes to stereom’s exceptionally high damage tolerance.
more »
« less
Geometrically Templated, Ultra‐Lightweight and High Strength Soap Films from Lyotropic Liquid Crystalline Graphene Oxide/Polymer Composites
Abstract Cellular solids composed of a network of interconnected pores offer low‐density and high strength‐to‐weight ratio as exemplified by wood, bones, corks, and shells. However, the slender edges and low connectivity of the structs in cellular lattices make them vulnerable to buckle, fracture, or collapse. Here, by taking advantage of the continuity of a thin film that can follow curvatures and dissipate energy, shellular materials are created by dip coating a wireframe of the primitive triply periodic minimal surface (TPMS) with an aqueous solution of lyotropic liquid crystalline graphene oxide (GO)/polymer composites. Regulated by surface tension, GO nanosheets align on the polymer soap film as the stress builds up during drying. When the wireframe mesh density is low, the shellular material is film‐dominated, demonstrating superior mechanical strength (384.30 Nm kg−1) and high specific energy absorption (1.59 kJ kg−1) yet lightweight (equivalent density, 0.063 g cm−3), with an energy absorption rate comparable to that of carbon nanotube‐based lattices but a lower equivalent density. The study offers insights into designing lightweight yet high‐strength structural materials that also function as impact energy absorbers.
more »
« less
- Award ID(s):
- 2037097
- PAR ID:
- 10628997
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Solar steam generation technologies have gained increasing attention due to their great potential for clean water generation with low energy consumption. The rational design of a light absorber that can maximize solar energy utilization is therefore of great importance. Here, the synthesis of Ni@C@SiO2core–shell nanoparticles as promising light absorbers for steam generation by taking advantage of the plasmonic excitation of Ni nanoparticles, the broadband absorption of carbon, and the protective function and hydrophilic property of silica is reported. The nanoparticle‐based evaporator shows an excellent photothermal efficiency of 91.2%, with an evaporation rate of 1.67 kg m−2 h−1. The performance can be further enhanced by incorporating the nanoparticles into a polyvinyl alcohol hydrogel to make a composite film. In addition, utilizing the magnetic property of the core–shell particles allows the creation of surface texture in the film by applying an external magnetic field, which helps increase surface roughness and further boost the evaporation rate to as high as 2.25 kg m−2 h−1.more » « less
-
Abstract Manufacturing of low‐density‐high‐strength carbon foams can benefit the construction, transportation, and packaging industries. One successful route to lightweight and mechanically strong carbon foams involves pyrolysis of polymeric architectures, which is inevitably accompanied by drastic volumetric shrinkage (usually >98%). As such, a challenge of these materials lies in maintaining bulk dimensions of building struts that span orders of magnitude difference in length scale from centimeters to nanometers. This work demonstrates fabrication of macroscale low‐density‐high‐strength carbon foams that feature exceptional dimensional stability through pyrolysis of robust template‐coating pairs. The template serves as the architectural blueprint and contains strength‐imparting properties (e.g., high node density and small strut dimensions); it is composed of a low char‐yielding porous polystyrene backbone with a high carbonization‐onset temperature. The coating serves to imprint and transcribe the template architecture into pyrolytic carbon; it is composed of a high char‐yielding conjugated polymer with a relatively low carbonization‐onset temperature. The designed carbonization mismatch enables structural inheritance, while the decomposition mismatch affords hollow struts, minimizing density. The carbons synthesized through this new framework exhibit remarkable dimensional stability (≈80% dimension retention; ≈50% volume retention) and some of the highest specific strengths (≈0.13 GPa g−1cm3) among reported carbon foams derived from porous polymer templates.more » « less
-
Supercapacitors and batteries are essential for sustainable energy development. However, the bottleneck is the associated high cost, which limits bulk use of batteries and supercapacitors. In this context, realizing that the cost of energy‐storage device mainly depends on materials, synthesis processes/procedures, and device fabrication, an effort is made to rationally design and develop novel low‐cost electrode materials with enhanced electrochemical performance in asymmetric supercapacitors. Herein, surface functionalization approach is adopted to design low‐cost 3D mesoporous and nanostructured nickel–nickel oxide electrode materials using facile synthesis for application in supercapacitors. It is demonstrated that the 3D mesoporous Ni provides the high surface area and enhanced ionic conductivity, while germanium functionalization improves the electrical conductivity and reduces the charge‐transfer resistance of NiO. Surface functionalization with Ge demonstrates the significant improvement in specific capacitance of NiO. The asymmetric supercapacitor using these Ge‐functionalized NiO–Ni electrodes provides a specific capacitance of 304 Fg−1(94 mF cm−2), energy density of 23.8 Wh kg−1(7.35 μWh cm−2), and power density of 6.8 kW kg−1(2.1 mW cm−2) with excellent cyclic stability of 92% after 10 000 cycles. To validate their practical applications, powering the digital watch using the asymmetric supercapacitors in laboratory conditions is demonstrated.more » « less
-
Lightweight cement-based composites with high specific strength and low thermal conductivity are highly sought in the energy and construction industries. These characteristics are important in designing cement liners for high-temperature, high-pressure (HTHP) wells, in addition to those operating in permafrost. Similar attributes are also desirable in designing cementitious composites for energy efficient building envelopes. This work reports the results of an experimental campaign focused on engineering lightweight cementitious composites with hollow glass microspheres. It is demonstrated that the chemical stability of microspheres at HTHP conditions can be directly controlled by modulating the specific surface area and dissolution rate constant of supplementary siliceous additives. In addition to the stabilizing effect, such additives lead to the pore structure refinement and the enhancement of interfacial transition zone (ITZ). Introduced lightweight composites are capable of delivering significant load bearing capacity when normally cured, which is greatly increased by hydrothermal curing. Such high specific strength composites possess thermal conductivity below 0.3 W/mK at the oven dry density <1000 kg/m3 and cement dosage <400 kg/m3. This class of cementitious composites bears potential to enhance zonal insulation and well integrity, as well as increasing energy efficiency of building envelopes.more » « less