Abstract An improved understanding of catalyst dynamics for the oxygen evolution reaction (OER) in acid is critical for informing the development of highly efficient, stable, and cost‐effective OER catalysts for proton exchange membrane water electrolysis applications. Herein highly tunable, active, and dynamic Ir 5+ materials are studied, Ln3IrO7(Ln = Pr, Nd, Sm, and Eu). Leveraging a combination of in situ and ex situ characterization, as well as an advanced mercury underpotential deposition technique for Ir surface site quantification, the dynamic nature of Ln3IrO7materials throughout electrochemical activation under OER conditions is characterized. The trends are elucidated between intrinsic OER activity, surface Ir site quantity, and metal site dissolution behavior as tuned by the Ln site's atomic number. A critical relationship is uncovered to show that maintenance of excellent OER activity throughout performance testing is correlated with a catalysts’ ability to preserve a high degree of Ir enrichment, where heightened stability of Ir sites interestingly parallels reduced stability of Ln sites throughout testing. It is found that as the Ln site's atomic number is decreased, the materials’ intrinsic OER performance improves, due to an increased thermodynamic driving force for Ln dissolution, which is hypothesized to enable the maintenance of highly active Ir‐based surface motifs.
more »
« less
This content will become publicly available on November 8, 2025
Quantification of electrochemically accessible iridium oxide surface area with mercury underpotential deposition
Research drives development of sustainable electrocatalytic technologies, but efforts are hindered by inconsistent reporting of advances in catalytic performance. Iridium-based oxide catalysts are widely studied for electrocatalytic technologies, particularly for the oxygen evolution reaction (OER) for proton exchange membrane water electrolysis, but insufficient techniques for quantifying electrochemically accessible iridium active sites impede accurate assessment of intrinsic activity improvements. We develop mercury underpotential deposition and stripping as a reversible electrochemical adsorption process to robustly quantify iridium sites and consistently normalize OER performance of benchmark IrOx electrodes to a single intrinsic activity curve, where other commonly used normalization methods cannot. Through rigorous deconvolution of mercury redox and reproportionation reactions, we extract net monolayer deposition and stripping of mercury on iridium sites throughout testing using a rotating ring disk electrode. This technique is a transformative method to standardize OER performance across a wide range of iridium-based materials and quantify electrochemical iridium active sites.
more »
« less
- Award ID(s):
- 2144365
- PAR ID:
- 10629434
- Publisher / Repository:
- American Association for the Advancement of Science (AAAS)
- Date Published:
- Journal Name:
- Science Advances
- Volume:
- 10
- Issue:
- 45
- ISSN:
- 2375-2548
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Acidic oxygen evolution reaction (OER) electrocatalysts that have high activity, extended durability, and lower costs are needed to further the development and wide-scale adoption of proton-exchange membrane electrolyzers. In this work, we report hydrous cobalt–iridium oxide two-dimensional (2D) nanoframes exhibit higher oxygen evolution activity and similar stability compared with commercial IrO 2 ; however, the bimetallic Co–Ir catalyst undergoes a significantly different degradation process compared with the monometallic IrO 2 catalyst. The bimetallic Co–Ir 2D nanoframes consist of interconnected Co–Ir alloy domains within an unsupported, carbon-free, porous nanostructure that allows three-dimensional molecular access to the catalytically active surface sites. After electrochemical conditioning within the OER potential range, the predominately bimetallic alloy surface transforms to an oxide/hydroxide surface. Oxygen evolution activities determined using a rotating disk electrode configuration show that the hydrous Co–Ir oxide nanoframes provide 17 times higher OER mass activity and 18 times higher specific activity compared to commercial IrO 2 . The higher OER activities of the hydrous Co–Ir nanoframes are attributed to the presence of highly active surface iridium hydroxide groups. The accelerated durability testing of IrO 2 resulted in lowering of the specific activity and partial dissolution of Ir. In contrast, the durability testing of hydrous Co–Ir oxide nanoframes resulted in the combination of a higher Ir dissolution rate, an increase in the relative contribution of surface iridium hydroxide groups and an increase in specific activity. The understanding of the differences in degradation processes between bimetallic and monometallic catalysts furthers our ability to design high activity and stability acidic OER electrocatalysts.more » « less
-
Earth-abundant manganese-based oxides have emerged as promising alternatives to noble-metal-based catalysts for the oxygen evolution reaction (OER) in acidic conditions; however, their inferior activity and stability present critical challenges for the sustainable production of hydrogen via water electrolysis. Moving beyond oxides, heteroanionic materials, which incorporate anions with lower electronegativity than oxygen, have shown potential for improving the OER performance, but a detailed understanding of the underlying mechanisms is lacking. Here, we investigate manganese based oxychlorides (Mn8O10Cl3 and FeMn7O10Cl3) that exhibit excellent activity and stability for acidic OER to elucidate material property dynamics and correlate them with OER behaviors. Our rigorous electrochemical stability testing reveals that the high operating potential mitigates Mn dissolution over prolonged exposure to the OER conditions. Through a combination of ex situ and in situ surface and bulk-sensitive X-ray spectroscopy analyses, we observe a trade-off between increasing Mn valence and maintaining structural integrity, which results in dynamic bond length changes within the [MnCl6] octahedra during the activation and degradation processes of these oxychloride catalysts. This study provides insights into the fundamental relationships between the chemical, electronic, and geometric properties of the catalysts and their electrocatalytic outcomes.more » « less
-
The two polymorphs of lithium cobalt oxide, LiCoO 2 , present an opportunity to contrast the structural requirements for reversible charge storage (battery function) vs. catalysis of water oxidation/oxygen evolution (OER; 2H 2 O → O 2 + 4H + + 4e − ). Previously, we reported high OER electrocatalytic activity from nanocrystals of the cubic phase vs. poor activity from the layered phase – the archetypal lithium-ion battery cathode. Here we apply transmission electron microscopy, electron diffraction, voltammetry and elemental analysis under OER electrolysis conditions to show that labile Li + ions partially deintercalate from layered LiCoO 2 , initiating structural reorganization to the cubic spinel LiCo 2 O 4 , in parallel with formation of a more active catalytic phase. Comparison of cubic LiCoO 2 (50 nm) to iridium (5 nm) nanoparticles for OER catalysis (commercial benchmark for membrane-based systems) in basic and neutral electrolyte reveals excellent performance in terms of Tafel slope (48 mV dec −1 ), overpotential ( η = ∼420 mV@10 mA cm −2 at pH = 14), faradaic yield (100%) and OER stability (no loss in 14 hours). The inherent OER activity of cubic LiCoO 2 and spinel LiCo 2 O 4 is attributed to the presence of [Co 4 O 4 ] n+ cubane structural units, which provide lower oxidation potential to Co 4+ and lower inter-cubane hole mobility. By contrast, the layered phase, which lacks cubane units, exhibits extensive intra-planar hole delocalization which entropically hinders the four electron/hole concerted OER reaction. An essential distinguishing trait of a truly relevant catalyst is efficient continuous operation in a real electrolyzer stack. Initial trials of cubic LiCoO 2 in a solid electrolyte alkaline membrane electrolyzer indicate continuous operation for 1000 hours (without failure) at current densities up to 400 mA cm −2 and overpotential lower than proven PGM (platinum group metal) catalysts.more » « less
-
The interaction between catalyst surfaces and adsorbed oxygen intermediates is critical to catalytic performance for electrochemical water oxidation to oxygen. However, the relationship between adsorption energetics and electrocatalytic activity is primarily assessed for pristine catalyst materials, which leaves much unknown about the dynamics of these properties in relationship to catalyst performance during long-term operation. In this work, we experimentally assess OH and O adsorption on Ca2IrO4 nanoparticles and monitor their evolution during extensive chronoamperometry tests at highly oxidizing potentials in a range of low pH electrolytes. In situ x-ray absorption spectroscopy reveals changes for surface adsorbate energetics and local iridium structures with applied potentials. Increasingly unfavorable adsorption of OH and formation of O intermediates after long-term operation is correlated with severe metal dissolution, distorted [IrO6] octahedral linkages, and a decreased average Ir valence. This work establishes connections between surface adsorption energetics, Ir structure, OER kinetics, and material stability outcomes.more » « less