Thermomechanical loading paths involving a simultaneous increase of stress and decrease of temperature (i.e., out-of-phase paths) were investigated for a NiTiHf High-Temperature Shape Memory Alloy (HTSMA). Isothermal and isobaric loadings were first performed to characterize the fundamental shape memory properties and establish the stress-temperature phase diagram. Fully-transforming out-of-phase loadings were then performed for different maximum stress levels. The obtained mechanical responses exhibited significant recoverable strains, indicating reversible martensitic transformations, contrary to the mechanical responses under pure isothermal mechanical loading. The out-of-phase responses were compared to those under isobaric paths to analyze the phase-transformation characteristics and identify the role of loading paths on the transformation reversibility and the possible interactions between deformation modes. The out-of-phase paths produce strain responses similar to the ones obtained from isobaric actuation tests. However, the strain recovery can be observed from both strain-temperature and stress–strain perspectives. Since recovery can occur from a stress–strain perspective, it is denominated as ”non-isothermal superelasticity”. The transformation temperatures obtained for these paths showed similar values to the ones corresponding to isobaric loading. A general definition of the work output is proposed to capture it under varying stresses, as opposed to the classical definition under constant stress levels in isobaric actuation experiments. An analysis of the work inputs and outputs, using this new definition, revealed that out-of-phase loadings produce a lower but relatively constant work output as a function of the stress level for a significantly lower work input, enabling new possibilities for HTSMA actuators in environments with limited work input available.
more »
« less
This content will become publicly available on September 1, 2026
Full-field investigation of in-phase and out-of-phase thermomechanical loading paths in high-temperature shape memory alloys
This study investigated the evolution of strain and temperature fields of a NiTiHf High-Temperature Shape Memory Alloy (HTSMA) undergoing complex thermomechanical loads involving simultaneous stress and temperature changes. In situ Digital Image Correlation (DIC) was used to track strain due to combined phase transformation and plastic yielding. Two types of loadings were performed: out-of-phase (OP) involving a simultaneous increase of stress and decrease of temperature and in-phase (IP) involving a simultaneous increase of stress and temperature. Five cycles were performed for each path. Due to a temperature gradient in the samples during the experiments, transformation nucleated in regions with the adequate temperature at a given stress level. Results showed a smooth transformation behavior for out-of-phase loadings along with a concentration of residual strain where transformation fronts meet one another. Due to the simultaneous high stress and high temperature for in-phase paths, creep was identified as a significant deformation mechanism for those paths. Furthermore, DIC allowed us to identify twinning/detwinning regions within the samples. Partial phase diagrams of the alloy were generated using the test results. Those experiments demonstrated the feasibility of characterizing HTSMAs using thermo-mechanical cycling to gain insights into the couplings between thermally- and mechanically-induced solid-state phase transformations for combined loading paths.
more »
« less
- Award ID(s):
- 2331036
- PAR ID:
- 10635090
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Journal of Alloys and Compounds
- Volume:
- 1040
- ISSN:
- 0925-8388
- Page Range / eLocation ID:
- 183335
- Subject(s) / Keyword(s):
- Solid-state phase transformation Digital Image Correlation NiTiHf Thermo-mechanical testing Path dependency Phase diagram
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Scale-free phase-field approach and corresponding finite element method simulations for multivariant martensitic phase transformation from cubic Si I to tetragonal Si II in a polycrystalline aggregate are presented. Important features of the model are large and very anisotropic transformation strain tensor 𝜺𝑡 = {0.1753; 0.1753; −0.447} and stress-tensor dependent athermal dissipative threshold for transformation, which produce essential challenges for computations. 3D polycrystals with stochastically oriented grains are subjected to uniaxial strain- and stress-controlled loadings under periodic boundary conditions and zero averaged lateral strains. Coupled evolution of discrete martensitic microstructure, volume fractions of martensitic variants and Si II, stress and transformation strain tensors, and texture are presented and analyzed. Macroscopic variables effectively representing multivariant transformational behavior are introduced. Macroscopic stress–strain and transformational behavior for 55 and 910 grains are close. Large transformation strains and grain boundaries lead to huge internal stresses of tens GPa, which affect microstructure evolution and macroscopic behavior. In contrast to a single crystal, the local mechanical instabilities due to phase transformation and negative local tangent modulus are stabilized at the macroscale by arresting/slowing the growth of Si II regions by the grain boundaries. This leads to increasing stress during transformation. The developed methodology can be used for studying similar phase transformations with large transformation strains and for further development by including plastic strain and strain-induced transformations.more » « less
-
The effect of initial microstructure and its evolution across the α→ω phase transformation in commercially pure Zr under hydrostatic compression has been studied using in situ x-ray diffraction measurements. Two samples were studied: one is plastically pre-deformed Zr with saturated hardness and the other is annealed. Phase transformation α→ω initiates at lower pressure for pre-deformed sample, suggesting pre-straining promotes nucleation by producing more defects with stronger stress concentrators. With transformation progress, the promoting effect on nucleation reduces while that on growth is suppressed by producing more obstacles for interface propagation. The crystal domain size reduces and microstrain and dislocation density increase during loading for both α and ω phases in their single-phase regions. For α phase, domain sizes are much smaller for prestrained Zr, while microstrain and dislocation densities are much higher. On the other hand, they do not differ much in ω Zr for both prestrained and annealed samples, implying that microstructure is not inherited during phase transformation. The significant effect of pressure on the microstructural parameters (domain size, microstrain, and dislocation density) demonstrates that their postmortem evaluation does not represent the true conditions during loading. A simple model for the initiation of the phase transformation involving microstrain is suggested, and a possible model for the growth is outlined. The obtained results suggest an extended experimental basis is required for better predictive models for the pressure-induced and combined pressure- and strain-induced phase transformations.more » « less
-
Strain-transformable Ti-based alloys are known to display a superior combination of strength, ductility and strain-hardening and attracted considerable interest on recent years. They generally still display, however, a limited yield strength that can be possibly overcome by further precipitation strengthening of the developed systems. In that work, we developed a design strategy to reach a forged dual-phase (α+β) microstructure with TRIP/TWIP properties in a Ti–10V–2Fe–3Al alloy. The results showed an excellent combination of mechanical properties due to the strain-transformable deformed β-matrix. The investigation on the deformation mechanisms in the Ti–10V–2Fe–3Al alloy was accurately performed by means of both in-situ synchrotron XRD, mechanical testing followed by SEM/EBSD mapping and “post mortem” TEM microstructural analyses. Combined Twinning Induced Plasticity (TWIP) and Transformation Induced Plasticity (TRIP) effects were shown to be intensively activated in the alloy. The particular role of stain-induced martensite α″, acting as a relaxation mechanism at the α∕β interfaces, as well as the strong interactions between mechanical twins and primary α nodules were particularly highlighted.more » « less
-
This study addresses the limitations of cross weld tensile testing (CWTT) in quantifying local mechanical properties across microstructural and compositional gradients in dissimilar– and matching–filler metal welds. A digital image correlation (DIC) methodology was validated for application in CWTT by direct comparison of stress-strain curves generated using conventional and virtual DIC extensometers in tensile testing of homogeneous steel samples. DIC-instrumented CWTT of dissimilar weld metal Alloy 625 filler metal on F65 steel demonstrated capability in quantifying the local yield strength, strain-hardening kinetics, and strain at failure in the base metal, heat-affected zone (HAZ), fusion boundary (FB) region, and weld metal in dissimilar and matching filler metal welds. It was shown that the high strain-hardening capacity in Alloy 625 weld metal led to base metal failure in CWTT despite the lower Alloy 625 weld metal yield strength. It was also shown that DIC-instrumented CWTT can be used for determining weld metal undermatching and overmatching conditions in compositionally matching- and dissimilar-metal welds. Furthermore, by quantifying local strain distribution (both elastic and plastic) in the HAZ, FB region, and weld metal, DIC-instrumented CWTT provides an additional method for evaluating hydrogen-assisted cracking susceptibility in dissimilar-metal welds.more » « less