Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Elastic Modulus Measurement at High Temperatures for Miniature Ceramic Samples Using Laser Micro-Machining and Thermal Mechanical Analyzer
Title: Elastic Modulus Measurement at High Temperatures for Miniature Ceramic Samples Using Laser Micro-Machining and Thermal Mechanical Analyzer
In this paper, we demonstrate a method of measuring the flexural elastic modulus of ceramics at an intermediate (~millimeter) scale at high temperatures. We used a picosecond laser to precisely cut microbeams from the location of interest in a bulk ceramic. They had a cross-section of approximately 100 μm × 300 μm and a length of ~1 cm. They were then tested in a thermal mechanical analyzer at room temperature, 500 °C, 800 °C, and 1100 °C using the four-point flexural testing method. We compared the elastic moduli of high-purity Al2O3 and AlN measured by our method with the reported values in the literature and found that the difference was less than 5% for both materials. This paper provides a new and accurate method of characterizing the high-temperature elastic modulus of miniature samples extracted from representative/selected areas of bulk materials.  more » « less
Award ID(s):
2119833
PAR ID:
10637303
Author(s) / Creator(s):
; ; ;
Publisher / Repository:
MDPI
Date Published:
Journal Name:
Materials
Volume:
17
Issue:
18
ISSN:
1996-1944
Page Range / eLocation ID:
4636
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; (, Metals)
    Ni–Mn–Ga Heusler alloys are multifunctional materials that demonstrate macroscopic strain under an externally applied magnetic field through the motion of martensite twin boundaries within the microstructure. This study sought to comprehensively characterize the microstructural, mechanical, thermal, and magnetic properties near the solidus in binder-jet 3D printed 14M Ni50Mn30Ga20. Neutron diffraction data were analyzed to identify the martensite modulation and observe the grain size evolution in samples sintered at temperatures of 1080 °C and 1090 °C. Large clusters of high neutron-count pixels in samples sintered at 1090 °C were identified, suggesting Bragg diffraction of large grains (near doubling in size) compared to 1080 °C sintered samples. The grain size was confirmed through quantitative stereology of polished surfaces for differently sintered and heat-treated samples. Nanoindentation testing revealed a greater resistance to plasticity and a larger elastic modulus in 1090 °C sintered samples (relative density ~95%) compared to the samples sintered at 1080 °C (relative density ~80%). Martensitic transformation temperatures were lower for samples sintered at 1090 °C than 1080 °C, though a further heat treatment step could be added to tailor the transformation temperature. Microstructurally, twin variants ≤10 μm in width were observed and the presence of magnetic anisotropy was confirmed through magnetic force microscopy. This study indicates that a 10 °C sintering temperature difference can largely affect the microstructure and mechanical properties (including elastic modulus and hardness) while still allowing for the presence of magnetic twin variants in the resulting modulated martensite. 
    more » « less
  2. ; ; (, Journal of the American Ceramic Society)
    Abstract Zirconium carbide (ZrC) powder, batched to a ratio of 0.98 C/Zr, was prepared by carbothermal reduction of ZrO2with carbon black. Nominally phase‐pure ZrC powder had a mean particle size of 2.4 μm. The synthesized powder was hot‐pressed at 2150°C to a relative density of > 95%. The mean grain size was 2.7 ± 1.4 μm with a maximum observed grain size of 17.5 μm. The final hot‐pressed billets had a C/Zr ratio of 0.92, and oxygen content of 0.5 wt%, as determined by gas fusion analysis. The mechanical properties of ZrC0.92O0.03were measured at room temperature. Vickers’ hardness decreased from 19.5 GPa at a load of 0.5 kgf to 17.0 GPa at a load of 1 kgf. Flexural strength was 362.3 ± 46 MPa, Young's modulus was 397 ± 13 MPa, and fracture toughness was 2.9 ± 0.1 MPa•m1/2. Analysis of mechanical behavior revealed that the largest ZrC grains were the strength‐limiting flaw in these ceramics. 
    more » « less
  3. ; ; ; ; ; (, Polymers)
    null (Ed.)
    The temperature dependence of the mechanical properties of polyvinyl alcohol-based poly n-isopropyl acrylamide (PVA-PNIPAm) hydrogel was studied from the static and dynamic bulk modulus of the material. The effect of the temperature-induced volumetric phase transition on Young’s Modulus, Poisson’s ratio, and the density of PVA-PNIPAm was experimentally measured and compared with a non-thermo-responsive Alginate hydrogel as a reference. An increase in the temperature from 27.5 to 32 °C results in the conventional temperature-dependent de-swelling of the PVA-PNIPAm hydrogel volume of up to 70% at the lower critical solution temperature (LCST). However, with the increase in temperature, the PVA-PNIPAm hydrogel showed a drastic increase in Young’s Modulus and density of PVA-PNIPAm and a corresponding decrease in the Poisson’s ratio and the static bulk modulus around the LCST temperature. The dynamic bulk modulus of the PVA-PNIPAm hydrogel is highly frequency-dependent before the LCST and highly temperature-sensitive after the LCST. The dynamic elastic properties of the thermo-responsive PVA-PNIPAm hydrogel were compared and observed to be significantly different from the thermally insensitive Alginate hydrogel. 
    more » « less
  4. ; ; ; ; (, Journal of the American Ceramic Society)
    Abstract Ultrahigh temperature ceramics (UHTCs) have melting points above 3000°C and outstanding strength at high temperatures, thus making them apposite structural materials for high‐temperature applications. Di‐borides, nitride, and carbide compounds—processed via various techniques—have been extensively studied and used in the manufacture of UHTCs. Current analytical models, based on our current but incomplete understanding of the theory, are unable to produce a priori predictions of mechanical properties of UHTCs based on their mixture designs and processing parameters. As a result, researchers have to rely on experiments—which are often costly and time‐consuming—to understand composition–structure–performance links in UHTCs. This study employs machine learning (ML) models (i.e., random forest and artificial neural network models) to predict Young's modulus, flexural strength, and fracture toughness of UHTCs in relation to a wide range of mixture designs, processing parameters, and testing conditions. Outcomes demonstrate that adequately trained ML models can yield reliable predictions, a priori, of the three aforesaid mechanical properties. The prediction performance on Young's modulus is superior to flexural strength and fracture toughness. Next, the ML model with the best prediction performance is utilized to evaluate and rank the impacts of input variables on Young's modulus. Finally, on the basis of such classification of consequential and inconsequential input variables, this study develops an easy‐to‐use, closed‐form analytical model to predict Young's modulus of UHTCs. Overall, this study highlights the ability of data‐driven numerical models to complement, or even replace, time‐consuming experiments, thereby accelerating the development of UHTCs. 
    more » « less
  5. ; ; ; (, Journal of Polymer Science)
    ABSTRACT High sulfur‐content materials (HSMs) prepared via inverse vulcanization are attractive for a range of sustainable material applications, particularly when synthesized from waste‐derived feedstocks such as brown grease (BG). Two BG‐based composites,SunBG90andaBG90, were prepared using elemental sulfur and either native or allylated brown grease, respectively. This study explores the effect of reinforcing these sulfur‐rich networks with low loadings (0.5–2 wt. %) of highcis‐1,4‐content liquid polybutadiene (PBD). Incorporation of PBD resulted in significant increases in storage modulus, with a near‐linear relationship between PBD content and stiffness enhancement for both material types. At −60°C, storage modulus increased more than fivefold foraBG90and more than tripled forSunBG90. In contrast, flexural strength and flexural modulus exhibited non‐linear responses, with diminishing or reversed gains at higher PBD loadings, suggesting limits to rubber domain compatibility and dispersion. Thermal analysis confirmed high decomposition temperatures (212°C–226°C) and stable glass transitions, indicating thermal robustness of the reinforced networks. Compared with previous studies requiring higher PBD loadings, these results demonstrate that BG‐based HSMs can be effectively reinforced at low additive levels, offering mechanically robust, low‐cost, and renewable alternatives for structural applications. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email