skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


This content will become publicly available on July 3, 2026

Title: Sand Composites Prepared with a Tung Oil-Based, Crosslinked Resin and its Preliminary Trials in Binder Jetting
In this work, a tung oil-based thermosetting resin was synthesized via free radical polymerization and reinforced with thirteen different types of sand. The viability of this process inspired the adaptation of the resin for its use as a binder material in binder jetting, an additive manufacturing process. Firstly, it was shown that the resin could have its initial viscosity (~0.33 cP) increased upon heating to attain values compatible to existing printing systems. The curing kinetics of the resin was assessed via dielectric analysis (DEA), combining the utilization of heat and ultraviolet (UV) light, showing that a resin with a viscosity of 10 cP can be fully cured after 250 min at 90 ◦C, or 300 min at 75 ◦C, both under a 365 nm light exposure. Preliminary binder-jet tests successfully provided a solid object, which was post-cured, resulting in a hard specimen. The results presented herein suggest that the tung oil-based resin in question is a suitable bio-based binder for binder-jet 3D-printing applications. The novelty of the work reported lies in the conversion of an already established and effective bio-based thermosetting resin into a versatile photocurable binder that can be irrestrictively used with unsorted sands of different composition, making this technology broadly applicable to different isolated regions, using local resources available. The technology presented herein is potentially transformative and impactful, as binder jetting is typically associated to extremely well-sorted particles.  more » « less
Award ID(s):
2229267
PAR ID:
10639829
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ; ; ;
Publisher / Repository:
Elsevier
Date Published:
Journal Name:
Materials Today Communications
Volume:
47
ISSN:
2352-4928
Page Range / eLocation ID:
113243
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; (, Coatings)
    In this work, renewable composites were prepared by the association of a thermosetting resin synthesized via free-radical polymerization, using a mixture of tung oil, n-butyl methacrylate, and divinylbenzene, with silica-rich fillers, namely an algae biomass with high silica content, and a well-sorted sand. Furthermore, to investigate if the interaction between the non-polar resin and polar reinforcements could be improved, enhancing the materials’ mechanical properties, itaconic anhydride, a bio-derived molecule obtained from itaconic acid, was introduced to the resin composition. Thermogravimetric analysis (TGA) suggested that the thermal stability of the composites was overall not changed with the addition of itaconic anhydride. The mechanical properties of the sand composites, however, did improve, as the storage modulus at room temperature, measured by dynamic mechanical analysis (DMA), almost doubled in the presence of itaconic anhydride. The glass transition temperatures of the materials increased by approximately 30 °C when sand was used as a reinforcement. Water absorption experiments validated an increase in the polarity of the unreinforced resin by the addition of itaconic anhydride to its formulation. The composites, however, did not exhibit a significant difference in polarity in the presence of itaconic anhydride. Finally, scanning electron microscopy (SEM), equipped with energy dispersive spectroscopy (EDS), demonstrated better matrix–filler adhesion in the presence of itaconic anhydride for high-silica algae composites. 
    more » « less
  2. ; ; ; ; ; ; ; ; (, RSC Advances)
    Four different biorenewable methacrylated/acrylated monomers, namely, methacrylated fatty acid (MFA), methacrylated eugenol (ME), isobornyl methacrylate (IM), and isobornyl acrylate (IA) were employed as reactive diluents (RDs) to replace styrene (St) in a maleinated acrylated epoxidized soybean oil (MAESO) resin to produce bio-based thermosetting resins using free radical polymerization. The curing kinetics, gelation times, double bond conversions, thermal–mechanical properties, and thermal stabilities of MAESO-RD resin systems were characterized using DSC, rheometer, FT-IR, DMA, and TGA. The results indicate that all four RD monomers possess high bio-based carbon content (BBC) ranging from 63.2 to 76.9% and low volatilities (less than 7 wt% loss after being held isothermally at 30 °C for 5 h). Moreover, the viscosity of the MAESO-RD systems can be tailored to acceptable levels to fit the requirements for liquid molding techniques. Because of the introduction of RDs to the MAESO resin, the reaction mixtures showed an improved reactivity and an accelerated reaction rate. FT-IR results showed that almost all the CC double bonds within MAESO-RD systems were converted. The glass transition temperatures ( T g ) of the MAESO-RDs ranged from 44.8 to 100.8 °C, thus extending the range of application. More importantly, the T g of MAESO-ME resin (98.1 °C) was comparable to that of MAESO-St resin (100.8 °C). Overall, this work provided four potential RDs candidates to completely replace styrene in the MAESO resin, with the ME monomer being the most promising one. 
    more » « less
  3. ; ; ; ; ; ; (, Molecules)
    We report a transformative epoxy system with a microalgae-derived bio-binder from hydrothermal liquefaction processing (HTL). The obtained bio-binder not only served as a curing agent for conventional epoxy resin (e.g., EPON 862), but also acted as a modifying agent to enhance the thermal and mechanical properties of the conventional epoxy resin. This game-changing epoxy/bio-binder system outperformed the conventional epoxy/hardener system in thermal stability and mechanical properties. Compared to the commercial EPON 862/EPIKURE W epoxy product, our epoxy/bio-binder system (35 wt.% bio-binder addition with respect to the epoxy) increased the temperature of 60% weight loss from 394 °C to 428 °C and the temperature of maximum decomposition rate from 382 °C to 413 °C, while the tensile, flexural, and impact performance of the cured epoxy improved in all cases by up to 64%. Our research could significantly impact the USD 38.2 billion global market of the epoxy-related industry by not only providing better thermal and mechanical performance of epoxy-based composite materials, but also simultaneously reducing the carbon footprint from the epoxy industry and relieving waste epoxy pollution. 
    more » « less
  4. ; ; ; ; (, Molecules)
    We report a transformative epoxy system with a microalgae-derived bio-binder from hydrothermal liquefaction processing (HTL). The obtained bio-binder not only served as a curing agent for conventional epoxy resin (e.g., EPON 862), but also acted as a modifying agent to enhance the thermal and mechanical properties of the conventional epoxy resin. This game-changing epoxy/bio-binder system outperformed the conventional epoxy/hardener system in thermal stability and mechanical properties. Compared to the commercial EPON 862/EPIKURE W epoxy product, our epoxy/bio-binder system (35 wt.% bio-binder addition with respect to the epoxy) increased the temperature of 60% weight loss from 394 °C to 428 °C and the temperature of maximum decomposition rate from 382 °C to 413 °C, while the tensile, flexural, and impact performance of the cured epoxy improved in all cases by up to 64%. Our research could significantly impact the USD 38.2 billion global market of the epoxy-related industry by not only providing better thermal and mechanical performance of epoxy-based composite materials, but also simultaneously reducing the carbon footprint from the epoxy industry and relieving waste epoxy pollution. 
    more » « less
  5. ; ; ; (, Journal of Composites Science)
    Epoxy is the most prevalent thermosetting resin in the field of polymer composite materials. There has been a growing interest in the development of bio-based epoxy resins as a sustainable alternative to conventional petrochemical epoxy resins. Advances in this field in recent years have included the use of various renewable resources, such as vegetable oils, lignin, and sugars, as direct precursors to produce bio-based epoxy resins. In the meantime, bio-oils have been produced via the decomposition of biomass through thermochemical conversion and mainly being used as renewable liquid fuels. It is noteworthy that bio-oils can be used as a sustainable resource to produce epoxy resins. This review addresses research progress in producing bio-oil-based epoxy resins from thermochemical processing techniques including organic solvent liquefaction, fast pyrolysis, and hydrothermal liquefaction. The production of bio-oil from thermochemical processing and its use to inject sustainability into epoxy resins are discussed. Herein, we intend to provide an overall picture of current attempts in the research area of bio-oil-based epoxy resins, reveal their potential for sustainable epoxy resins, and stimulate research interests in green/renewable materials. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email