A key component of cooling devices is the transfer of entropy from the cold load to heat sink. An electrocaloric (EC) polymer capable of generating both large electrocaloric effect (ECE) and substantial electroactuation can enable EC cooling devices to pump heat without external mechanisms, resulting in compact designs and enhanced efficiency. However, achieving both high ECE and significant electroactuation remains challenging. Herein, it is demonstrated that poly(vinylidene fluoride‐trifluoroethylene‐chlorofluoroethylene‐double bond) [P(VDF‐TrFE‐CFE‐DB)] tetrapolymers can simultaneously generate high electrocaloric effects and electroactuations under low fields. These P(VDF‐TrFE‐CFE‐DB) tetrapolymers are synthesized through the dehydrochlorination of P(VDF‐TrFE‐CFE) terpolymer. By facile tuning the composition of the initial terpolymer to avoid pure relaxor state, tetrapolymers with optimal DB compositions are achieved, near the critical endpoint of normal ferroelectric phase with diffused phase transition. The nearly vanishing energy barriers between the nonpolar to polar phases result in a strong electrocaloric response and significant electroactuation. Specifically, the P(VDF‐TrFE‐CFE‐DB) tetrapolymer exhibits an EC entropy change ΔSof 100 J kg−1 K−1under 100 MV m−1: comparable to state‐of‐the‐art (SOA) EC polymers, while delivering nearly twice the electroactuation of the SOA EC polymers. This work presents a general strategy for developing EC materials that combine large electrocaloric effect and electroactuation at low electric fields.
more »
« less
Operando Investigation of the Molecular Origins of Dipole Switching in P(VDF‐TrFE‐CFE) Terpolymer for Large Adiabatic Temperature Change
Abstract Relaxor ferroelectric polymers exhibiting a giant electrocaloric effect (ECE) can potentially be used to create next‐generation solid‐state coolers. Under an electric field, poly(vinylidene fluoride‐trifluoroethylene‐chlorofluoroethylene) terpolymer goes through a large dipolar entropy change producing a high adiabatic temperature change (ΔTECE). This work resolves the molecular origins of the large entropy change behind the electric field‐induced dipole switching. A Fourier transform infrared spectroscopy equipped with a high voltage source is used to operandoly observe the characteristic molecular vibrational modes. A short‐range trans (T) conformation of the CF2‐CH2dyads interrupted by a gauche (G) conformation, e.g., TTTG in the terpolymer chain, undergoes a dynamic transformation that leads to a corresponding ΔTECEwhenever an electric field is applied. The molecular dynamics simulation also proves that the energy barrier that the transformation from TTTGs into a long T sequence overcomes is smaller than that for all other conformations. A mixed solvent system is used to obtain T3G‐enriched terpolymer films exhibiting a 4.02 K ΔTECEat 60 MV m−1and these films are employed to manufacture a 2‐layer‐cascaded cooling device that achieves a 6.7 K temperature lift, the highest reported value for a 2‐layer cascaded device made of fluoropolymers.
more »
« less
- Award ID(s):
- 2103196
- PAR ID:
- 10641050
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 34
- Issue:
- 26
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Boron (B) alloying transforms the magnetoelectric antiferromagnet Cr2O3into a multifunctional single‐phase material which enables electric field driven π/2 rotation of the Néel vector. Nonvolatile, voltage‐controlled Néel vector rotation is a much‐desired material property in the context of antiferromagnetic spintronics enabling ultralow power, ultrafast, nonvolatile memory, and logic device applications. Néel vector rotation is detected with the help of heavy metal (Pt) Hall‐bars in proximity of pulsed laser deposited B:Cr2O3films. To facilitate operation of B:Cr2O3‐based devices in CMOS (complementary metal‐oxide semiconductor) environments, the Néel temperature,TN, of the functional film must be tunable to values significantly above room temperature. Cold neutron depth profiling and X‐ray photoemission spectroscopy depth profiling reveal thermally activated B‐accumulation at the B:Cr2O3/ vacuum interface in thin films deposited on Al2O3substrates. The B‐enrichment is attributed to surface segregation. Magnetotransport data confirm B‐accumulation at the interface within a layer of ≈50 nm thick where the device properties reside. HereTNenhances from 334 K prior to annealing, to 477 K after annealing for several hours. Scaling analysis determinesTNas a function of the annealing temperature. Stability of post‐annealing device properties is evident from reproducible Néel vector rotation at 370 K performed over the course of weeks.more » « less
-
Abstract The availability of materials with high electrocaloric (EC) strengths is critical to enabling EC refrigeration in practical applications. Although large EC entropy changes, ΔSEC, and temperature changes, ΔTEC, have been achieved in traditional thin‐film ceramics and polymer ferroelectrics, they require the application of very high electric fields and thus their EC strengths ΔSEC/ΔEand ΔTEC/ΔEare too low for practical applications. Here, a fundamental thermodynamic description is developed, and extraordinarily large EC strengths of a metal‐free perovskite ferroelectric [MDABCO](NH4)I3(MDABCO) are predicted. The predicted EC strengths: isothermal ΔSEC/ΔEand adiabatic ΔTEC/ΔEfor MDABCO are 18 J m kg−1K−1MV−1and 8.06 K m MV−1, respectively, more than three times the largest reported values in BaTiO3single crystals. These predictions strongly suggest the metal‐free ferroelectric family of materials as the best candidates among existing materials for EC applications. The present work not only presents a general approach to developing thermodynamic potential energy functions for ferroelectric materials but also suggests a family of candidate materials with potentially extremely high EC performance.more » « less
-
Abstract The structure of liquid lithium pyroborate, Li4B2O5(J= Li/B = 2), has been measured over a wide temperature range by high‐energy X‐ray diffraction, and compared to that of its glass and borate liquids of other compositions. The results indicate a gradual increase in tetrahedral boron fraction from 3(1)% to 6(1)% during cooling fromT= 1271(15) to 721(8) K, consistent with the largerN4 = 10(1)% found for the glass, and literature11B nuclear magnetic resonance measurements. van't Hoff analysis based on a simple boron isomerization reaction BØ3O2–⇌ BØO22–yields ΔH= 13(1) kJ mol–1and ΔS= 40(1) J mol–1 K–1for the boron coordination change from 4 to 3, which are, respectively, smaller and larger than found for singly charged isomers forJ ≤ 1. With these, we extend our model forN4(J,T), nonbridging oxygen fractionfnbr(J,T), configurational heat capacity , and entropySconf(J,T) contributions up toJ= 3. A maximum is revealed in atJ= 1, and shown semi‐quantitatively to lead to a corresponding maximum in fragility contribution, akin to that observed in the total fragilities by temperature‐modulated differential scanning calorimetry. Lithium is bound to 4.6(2) oxygen in the pyroborate liquid, with 2.7(1) bonds centered around 1.946(8) Å and 1.9(1) around 2.42(1) Å. In the glass,nLiO= 5.4(4), the increase being due to an increase in the number of short Li–O bonds.more » « less
-
Abstract Kagome materials are of topical interest for their diverse quantum properties linked with correlated magnetism and topology. Here, we report anomalous hydrostatic pressure (p) effect on ErMn6Sn6through isobaric and isothermal-isobaric magnetization measurements. Magnetic field (H) suppresses antiferromagneticTNwhile simultaneously enhancing the ferrimagneticTCby exhibiting dual metamagnetic transitions, arising from the triple-spiral-nature of Er and Mn spins. Counter-intuitively, pressure enhances bothTCandTNwith a growth rate of 74.4 K GPa−1and 14.4 K GPa−1respectively. Pressure unifies the dual metamagnetic transitions as illustrated throughp-Hphase diagrams at 140 and 200 K. Temperature-field-pressure (T-H,T-p) phase diagrams illustrate distinct field- and pressure-induced critical points at (Tcr= 246 K,Hcr= 23.3 kOe) and (Tcr= 435.8 K,pcr= 4.74 GPa) respectively. An unusual increase of magnetic entropy by pressure aroundTcrand a putative pressure-induced tricritical point pave a unique way of tuning the magnetic properties of kagome magnets through simultaneous application ofHandp.more » « less