Digital light processing (DLP) 3D printing has become a powerful manufacturing tool for the fast fabrication of complex functional structures. The rapid progress in DLP 3D printing has been linked to research on optical design factors and ink selection. This critical review highlights the main challenges in the DLP 3D printing of photopolymerizable inks. The kinetics equations of photopolymerization reaction in a DLP printer are solved, and the dependence of curing depth on the process optical parameters and ink chemical properties are explained. Developments in DLP platform design and ink selection are summarized, and the roles of monomer structure and molecular weight on printing resolution are shown by experimental data. A detailed guideline is presented to help engineers and scientists to select inks and optical parameters for fabricating functional structures for multi-material and 4D printing.
more »
« less
Fast and Efficient Fabrication of Functional Electronic Devices through Grayscale Digital Light Processing 3D Printing
Abstract Fabricating polymeric composites with desirable characteristics for electronic applications is a complex and costly process. Digital light processing (DLP) 3D printing emerges as a promising technique for manufacturing intricate structures. In this study, polymeric samples are fabricated with a conductivity difference exceeding three orders of magnitude in various portions of a part by employing grayscale DLP (g‐DLP) single‐vat single‐cure 3D printing deliberate resin design. This is realized through the manipulation of light intensity during the curing process. Specifically, the rational resin design with added lithium ions results in the polymer cured under the maximum UV‐light intensity exhibiting higher electrical resistance. Conversely, sections that are only partially cured retains uncured monomers, serving as a medium that facilitates ion mobility, consequently leading to higher conductivity. The versatility of g‐DLP allows precise control of light intensity in different regions during the printing process. This characteristic opens up possibilities for applications, notably the low‐cost, facile, and rapid production of complex electrical circuits and sensors. The utilization of this technique makes it feasible to fabricate materials with tailored conductivity and functionality, providing an innovative pathway to advance the accelerated and facile creation of sophisticated electronic devices.
more »
« less
- Award ID(s):
- 2323696
- PAR ID:
- 10641055
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials
- Volume:
- 36
- Issue:
- 46
- ISSN:
- 0935-9648
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract An acoustic liquefaction approach to enhance the flow of yield stress fluids during Digital Light Processing (DLP)‐based 3D printing is reported. This enhanced flow enables processing of ultrahigh‐viscosity resins (μapp > 3700 Pa s at shear rates = 0.01 s–1) based on silica particles in a silicone photopolymer. Numerical simulations of the acousto–mechanical coupling in the DLP resin feed system at different agitation frequencies predict local resin flow velocities exceeding 100 mm s–1at acoustic transduction frequencies of 110 s–1. Under these conditions, highly loaded particle suspensions (weight fractions, ϕ = 0.23) can be printed successfully in complex geometries. Such mechanically reinforced composites possess a tensile toughness 2000% greater than the neat photopolymer. Beyond an increase in processible viscosities, acoustophoretic liquefaction DLP (AL‐DLP) creates a transient reduction in apparent viscosity that promotes resin recirculation and decreases viscous adhesion. As a result, acoustophoretic liquefaction Digital Light Processing (AL‐DLP) improves the printed feature resolution by more than 25%, increases printable object sizes by over 50 times, and can build parts >3 × faster when compared to conventional methodologies.more » « less
-
In this work, a tung oil-based thermosetting resin was synthesized via free radical polymerization and reinforced with thirteen different types of sand. The viability of this process inspired the adaptation of the resin for its use as a binder material in binder jetting, an additive manufacturing process. Firstly, it was shown that the resin could have its initial viscosity (~0.33 cP) increased upon heating to attain values compatible to existing printing systems. The curing kinetics of the resin was assessed via dielectric analysis (DEA), combining the utilization of heat and ultraviolet (UV) light, showing that a resin with a viscosity of 10 cP can be fully cured after 250 min at 90 ◦C, or 300 min at 75 ◦C, both under a 365 nm light exposure. Preliminary binder-jet tests successfully provided a solid object, which was post-cured, resulting in a hard specimen. The results presented herein suggest that the tung oil-based resin in question is a suitable bio-based binder for binder-jet 3D-printing applications. The novelty of the work reported lies in the conversion of an already established and effective bio-based thermosetting resin into a versatile photocurable binder that can be irrestrictively used with unsorted sands of different composition, making this technology broadly applicable to different isolated regions, using local resources available. The technology presented herein is potentially transformative and impactful, as binder jetting is typically associated to extremely well-sorted particles.more » « less
-
Abstract The utility of visible light for 3D printing has increased in recent years owing to its accessibility and reduced materials interactions, such as scattering and absorption/degradation, relative to traditional UV light‐based processes. However, photosystems that react efficiently with visible light often require multiple molecular components and have strong and diverse absorption profiles, increasing the complexity of formulation and printing optimization. Herein, a streamlined method to select and optimize visible light 3D printing conditions is described. First, green light liquid crystal display (LCD) 3D printing using a novel resin is optimized through traditional empirical methods, which involves resin component selection, spectroscopic characterization, time‐intensive 3D printing under several different conditions, and measurements of dimensional accuracy for each printed object. Subsequent analytical quantification of dynamic photon absorption during green light polymerizations unveils relationships to cure depth that enables facile resin and 3D printing optimization using a model that is a modification to the Jacob's equation traditionally used for stereolithographic 3D printing. The approach and model are then validated using a distinct green light‐activated resin for two types of projection‐based 3D printing.more » « less
-
Abstract Liquid crystalline elastomers (LCEs) are anisotropic soft materials capable of large dimensional changes when subjected to a stimulus. The magnitude and directionality of the stimuli‐induced thermomechanical response is associated with the alignment of the LCE. Recent reports detail the preparation of LCEs by additive manufacturing (AM) techniques, predominately using direct ink write printing. Another AM technique, digital light process (DLP) 3D printing, has generated significant interest as it affords LCE free‐forms with high fidelity and resolution. However, one challenge of printing LCEs using vat polymerization methods such as DLP is enforcing alignment. Here, we document the preparation of aligned, main‐chain LCEs via DLP 3D printing using a 100 mT magnetic field. Systematic examination isolates the contribution of magnetic field strength, alignment time, and build layer thickness on the degree of orientation in 3D printed LCEs. Informed by this fundamental understanding, DLP is used to print complex LCE free‐forms with through‐thickness variation in both spatial orientations. The hierarchical variation in spatial orientation within LCE free‐forms is used to produce objects that exhibit mechanical instabilities upon heating. DLP printing of aligned LCEs opens new opportunities to fabricate stimuli‐responsive materials in form factors optimized for functional use in soft robotics and energy absorption.more » « less