ABSTRACT High sulfur‐content materials (HSMs) prepared via inverse vulcanization are attractive for a range of sustainable material applications, particularly when synthesized from waste‐derived feedstocks such as brown grease (BG). Two BG‐based composites,SunBG90andaBG90, were prepared using elemental sulfur and either native or allylated brown grease, respectively. This study explores the effect of reinforcing these sulfur‐rich networks with low loadings (0.5–2 wt. %) of highcis‐1,4‐content liquid polybutadiene (PBD). Incorporation of PBD resulted in significant increases in storage modulus, with a near‐linear relationship between PBD content and stiffness enhancement for both material types. At −60°C, storage modulus increased more than fivefold foraBG90and more than tripled forSunBG90. In contrast, flexural strength and flexural modulus exhibited non‐linear responses, with diminishing or reversed gains at higher PBD loadings, suggesting limits to rubber domain compatibility and dispersion. Thermal analysis confirmed high decomposition temperatures (212°C–226°C) and stable glass transitions, indicating thermal robustness of the reinforced networks. Compared with previous studies requiring higher PBD loadings, these results demonstrate that BG‐based HSMs can be effectively reinforced at low additive levels, offering mechanically robust, low‐cost, and renewable alternatives for structural applications.
more »
« less
Brown Grease as a Precursor to Polyol Monomer for Polyurethane Synthesis
Abstract The valorization of waste‐derived feedstocks for polymer synthesis represents a sustainable alternative to petroleum‐based materials. In this study, brown grease, a low‐value waste lipid source, is utilized as a precursor for polyol monomer synthesis via a two‐step functionalization process. Transesterification of brown grease with allyl alcohol generates allyl esters, which are subsequently modified via thiol‐ene click chemistry with 2‐mercaptoethanol to yield hydroxyl‐functionalized polyols (BG‐diol). The thiol‐ene reaction proceeds under mild UV‐initiated conditions, achieving high conversion efficiency (>90%) while preserving the structural integrity of the derived polyol.BG‐diolis further polymerized with 4,4′‐methylene diphenyl diisocyanate (MDI) through step‐growth polymerization to form brown grease‐derived polyurethane (BG‐PU). Comparative analysis ofBG‐PUwith polyurethane (PU) synthesized from purified oleic acid (OLA‐PU) demonstrates comparable molecular weight distributions (Mn = 14.4 kDa,Mw = 20.4 kDa forBG‐PU) and thermal properties (Tg = 24 °C,Td,5%= 270 °C forBG‐PU). These results underscore the feasibility of brown grease as a cost‐effective and renewable alternative to plant oil‐based polyols, offering a pathway toward sustainable PU production while mitigating food security concerns. This approach exemplifies the potential of waste lipids in circular economy strategies for high‐performance polymer synthesis.
more »
« less
- Award ID(s):
- 2203669
- PAR ID:
- 10644359
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- ChemistrySelect
- Volume:
- 10
- Issue:
- 33
- ISSN:
- 2365-6549
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
ABSTRACT Brown grease (BG) is a high‐free fatty acid (FFA) waste coproduct from the food industry that remains largely unexploited. Herein, we describe a design strategy to upcycle BG into high sulfur‐content materials (HSMs) via inverse vulcanization, circumventing the need for costly transition metals or food‐grade compatibilizers. First, BG was esterified with methyl or allyl groups, yielding MeBG and aBG, respectively. This modification masked the polar carboxylic acids and enhanced miscibility with molten sulfur. Subsequent inverse vulcanization produced remeltable HSMs at 80 or 90 wt% sulfur with uniform elemental distributions by SEM–EDX. FT‐IR spectroscopy revealed the consumption of C=C moieties and the formation of C–S bonds, signifying robust cross‐linking. Thermal analysis (TGA, DSC) indicated good thermal stability (Td,5%up to 223°C) and glass transitions characteristic of polysulfide networks. Mechanical evaluations demonstrated compressive strengths up to 19.2 MPa, exceeding the minimum requirement for residential foundation‐grade cement (17 MPa) and rivaling previously reported HSMs containing similarly high sulfur content. Notably, MeBG and aBG incorporate organics comprising up to 97 wt% BG, significantly improving the upcycled mass efficiency relative to earlier BG‐based composites. This esterification‐driven approach thus offers a practical, scalable pathway to convert low‐value BG into advanced materials with tunable thermomechanical properties.more » « less
-
Abstract Lignocellulosic biomass remains underutilized despite its annual production in gigaton quantities. Sulfur is another vastly underutilized waste product of fossil fuel refining. New mechanistic insight into the reactions of sulfur unveiled since 2020 suggest a rich and hitherto unexplored chemistry between biomass‐derived olefins and elemental sulfur. In this study, four biomass‐derived olefins (eugenol (1), 4‐allyl‐2,6‐dimethoxyphenol (2),o‐eugenol (3), and 2‐allyl‐6‐methylphenol(4)) were reacted with elemental sulfur to elucidate the S−C bond‐forming and other reactivity of these compounds. Each of the compounds was reacted with elemental sulfur in three sulfur : organic reactant ratios (2 : 1, 4 : 1 and 9 : 1) and at two temperatures (180 °C or 230 °C). Product mixtures were characterized using1H NMR spectrometry and GC‐MS analysis. Products resulting from a range of mechanisms were unveiled, including inverse vulcanization, S−Callylic/benzylicbond formation, S−Carylbond formation, intramolecular cyclization, C−C σ‐bond scission, and C−O σ‐bond scission. It is anticipated that the insights from this study will support further synergy between the critical sustainability goals of biomass and sulfur utilization.more » « less
-
ABSTRACT: Covalent adaptive networks combine the advantages of cross-linked elastomers and dynamic bonding in a single system. In this work, we demonstrate a simple one-pot method to prepare thiol−ene elastomers that exhibit reversible photoinduced switching from an elastomeric gel to fluid state. This behavior can be generalized to thiol−ene cross-linked elastomers composed of different backbone chemistries (e.g., polydimethylsiloxane, polyethylene glycol, and polyurethane) and vinyl groups (e.g., allyl, vinyl ether, and acrylate). Photoswitching from the gel to fluid state occurs in seconds upon exposure to UV light and can be repeated over at least 180 cycles. These thiol−ene elastomers also exhibit the ability to heal, remold, and serve as reversible adhesives. KEYWORDS: covalent adaptive network, elastomer chemistry, click chemistry, self-healing, photoresponsive materials, adhesivesmore » « less
-
Rare earth elements (REEs) are crucial for clean energy technologies but are predominantly purified by solvent extraction using strong acids. This work explores two adsorbents with selective chemistry based on lanmodulin-derived peptides. Two membrane adsorber platforms were synthesized: (1) a poly(vinylbenzyl chloride) membrane with a grafted poly(allyl methacrylate) network and (2) a poly(arylene ether sulfone)membrane with allyl pendant groups. Both membrane adsorbers were functionalized with LanM1 peptides via a thiol−ene click reaction. The morphology, surface chemistry, and adsorption of select trivalent lanthanides (La, Ce, Pr, Nd) were characterized in pH 4−5 solutions, mimicking phosphogypsum waste streams. Results from the adsorption experiments indicate that the lanmodulin peptide sequence maintains its ability to bind when it is immobilized on the surface of polymer fibers for some ions. Despite the different adsorbent designs, the measured capacity of both adsorbents is on the same order of magnitude, which may be explained by differences in the surface area of the fibersmore » « less