Search for: All records

Group IVB transition metal dichalcogenides (TMDCs) have attracted significant attention due to their predicted high charge carrier mobility, large sheet current density, and enhanced thermoelectric power. Here, we investigate the electrical and optoelectronic properties of few-layer titanium diselenide (TiSe 2 )-metal junctions through spatial-, wavelength-, temperature-, power- and temporal-dependent scanning photocurrent measurements. Strong photocurrent responses have been detected at TiSe 2 -metal junctions, which is likely attributed to both photovoltaic and photothermoelectric effects. A fast response time of 31 μs has been achieved, which is two orders of magnitude better than HfSe 2 based devices. More importantly, our experimental results reveal a significant enhancement in the response speed upon cooling to the charge-density-wave (CDW) phase transition temperature ( T CDW = 206 K), which may result from dramatic reduction in carrier scattering that occurs as a result of the switching between the normal and CDW phases of TiSe 2 . Additionally, the photoresponsivity at 145 K is up to an order of magnitude higher than that obtained at room temperature. These fundamental studies not only offer insight for the photocurrent generation mechanisms of group IVB TMDC materials, but also provide a route to engineering future temperature-dependent, two-dimensional, fast electronic and optoelectronic devices. 

Understanding transport mechanisms of electrons and phonons, two major energy carriers in solids, are crucial for various engineering applications. It is widely believed that more free electrons in a material should correspond to a higher thermal conductivity; however, free electrons also scatter phonons to lower the lattice thermal conductivity. The net contribution of free electrons has been rarely studied because the effects of electron–phonon (e–ph) interactions on lattice thermal conductivity have not been well investigated. Here an experimental study of e–ph scattering in quasi-one-dimensional NbSe 3 nanowires is reported, taking advantage of the spontaneous free carrier concentration change during charge density wave (CDW) phase transition. Contrary to the common wisdom that more free electrons would lead to a higher thermal conductivity, results show that during the depinning process of the condensed electrons, while the released electrons enhance the electronic thermal conductivity, the overall thermal conductivity decreases due to the escalated e–ph scattering. This study discloses how competing effects of free electrons result in unexpected trends and provides solid experimental data to dissect the contribution of e–ph scattering on lattice thermal conductivity. Lastly, an active thermal switch design is demonstrated based on tuning electron concentration through electric field. 

We investigate electronic and optoelectronic properties of few-layer palladium diselenide (PdSe 2 ) phototransistors through spatially-resolved photocurrent measurements. A strong photocurrent resonance peak is observed at 1060 nm (1.17 eV), likely attributed to indirect optical transitions in few-layer PdSe 2 . More interestingly, when the thickness of PdSe 2 flakes increases, more and more photocurrent resonance peaks appear in the near-infrared region, suggesting strong interlayer interactions in few-layer PdSe 2 help open up more optical transitions between the conduction and valence bands of PdSe 2 . Moreover, gate-dependent measurements indicate that remarkable photocurrent responses at the junctions between PdSe 2 and metal electrodes primarily result from the photovoltaic effect when a PdSe 2 phototransistor is in the off-state and are partially attributed to the photothermoelectric effect when the device turns on. We also demonstrate PdSe 2 devices with a Seebeck coefficient as high as 74 μV K −1 at room temperature, which is comparable with recent theoretical predications. Additionally, we find that the rise and decay time constants of PdSe 2 phototransistors are ∼156 μs and ∼163 μs, respectively, which are more than three orders of magnitude faster than previous PdSe 2 work and two orders of magnitude over other noble metal dichalcogenide phototransistors, offering new avenues for engineering future optoelectronics. 

We report a reversible photo-induced doping effect in two-dimensional (2D) tungsten diselenide (WSe 2 ) field effect transistors on hexagonal boron nitride (h-BN) substrates under low-intensity visible light illumination (∼10 nW μm −2 ). Our experimental results have shown that this reversible doping process is mainly attributed to two types of defects in h-BN substrates. Moreover, the photo-doped WSe 2 transistors can be stable for more than one week in a dark environment and maintain the high on/off ratio (10 8 ) and carrier mobility, since there are no additional impurities involved during the photo-induced doping process to increase the columbic scattering in the conducting channel. These fundamental studies not only provide an accessible strategy to control the charge doping level and then to achieve a writing/erasing process in 2D transistors, but also shed light on the defect states and interfaces in 2D materials.