Solar water splitting using photoelectrochemical cells (PEC's) is a promising pathway toward clean and sustainable storage of renewable energy. Practical realization of solar-driven synthesis of hydrogen and oxygen integrating light absorption and electrolysis of water has been challenging because of (1) the limited stability of good photovoltaic materials under the required electrochemical conditions, and (2) photovoltaic efficiency losses due to light absorption by catalysts, the electrolyte, and generated bubbles, or reflection at their various interfaces. Herein, we evaluate a novel integrated solar water splitting architecture using efficient silicon heterojunction photovoltaic cells that avoids such losses and exhibits a solar-to-hydrogen (STH) efficiency in excess of 10%. Series-connected silicon Heterojunction with Intrinsic Thin layer (HIT) cells generate sufficient photovoltage for unassisted water splitting, with one of the cells acting as the photocathode. Platinum is deposited on the back (dark) junction of this HIT cell as the catalyst for the hydrogen evolution reaction (HER). The photocathode is protected from corrosion by a TiO 2 layer deposited by atomic layer deposition (ALD) interposed between the HIT cell and the Pt, enabling stable operation for >120 hours. Combined with oxygen evolution reaction (OER) catalysts deposited on a porous metal dark anode, these PEC's achieve stable water splitting with a record high STH efficiency for an integrated silicon photosynthesis device.
more »
« less
Dual Protection Layer Strategy to Increase Photoelectrode–Catalyst Interfacial Stability: A Case Study on Black Silicon Photoelectrodes
Photoelectrode degradation under harsh solution conditions continues to be a major hurdle for long-term operation and large-scale implementation of solar fuel conversion. In this study, a dual-layer TiO2 protection strategy is presented to improve the interfacial durability between nanoporous black silicon and photocatalysts. Nanoporous silicon photocathodes decorated with catalysts are passivated twice, providing an intermediate TiO2 layer between the substrate and catalyst and an additional TiO2 layer on top of the catalysts. Atomic layer deposition of TiO2 ensures uniform coverage of both the nanoporous silicon substrate and the catalysts. After 24 h of electrolysis at pH = 0.3, unprotected photocathodes layered with platinum and molybdenum sulfide retain only 30% and 20% of their photocurrent, respectively. At the same pH, photocathodes layered with TiO2 experience an increase in photocurrent retention: 85% for platinum-coated photocathodes and 91% for molybdenum sulfide–coated photocathodes. Under alkaline conditions, unprotected photocathodes experience a 95% loss in photocurrent within the first 4 h of electrolysis. In contrast, TiO2-protected photocathodes maintain 70% of their photocurrent during 12 h of electrolysis. This approach is quite general and may be employed as a protection strategy for a variety of photoabsorber–catalyst interfaces under both acidic and basic electrolyte conditions
more »
« less
- Award ID(s):
- 1704992
- PAR ID:
- 10093794
- Date Published:
- Journal Name:
- Advanced materials interfaces
- Issue:
- 6
- ISSN:
- 2196-7350
- Page Range / eLocation ID:
- 1802085
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Selective removal of oxygen from biomass-derived polyols is critical toward bridging the gap between biomass feedstocks and the production of commodity chemicals. In this work, we show that earth-abundant molybdenum oxide based heterogeneous catalysts are active, selective, and stable for the cleavage of vicinal C–O bonds in biomass-derived polyols. Catalyst characterization (Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS)) shows that partially reduced MoOx centers are responsible for C–O bond cleavage and are generated in situ by hydrogen dissociated atoms over palladium (Pd) nanoparticles. We find that the support, TiO2, facilitates communication between the hydrogen dissociating metal and dispersed MoOx sites through hydrogen spillover. Reactivity studies using a biomass-derived model substrate (1,4-anhydroerythritol) show the effective removal of vicinal hydroxyls over MoOx-Pd/TiO2 producing tetrahydrofuran with >98% selectivity at 29% conversion. Catalyst stability is demonstrated upon cycling. These studies are critical toward the development of low-cost heterogeneous catalysts for sustainable hydrodeoxygenation of biobased polyols to platform chemicals.more » « less
-
The two polymorphs of lithium cobalt oxide, LiCoO 2 , present an opportunity to contrast the structural requirements for reversible charge storage (battery function) vs. catalysis of water oxidation/oxygen evolution (OER; 2H 2 O → O 2 + 4H + + 4e − ). Previously, we reported high OER electrocatalytic activity from nanocrystals of the cubic phase vs. poor activity from the layered phase – the archetypal lithium-ion battery cathode. Here we apply transmission electron microscopy, electron diffraction, voltammetry and elemental analysis under OER electrolysis conditions to show that labile Li + ions partially deintercalate from layered LiCoO 2 , initiating structural reorganization to the cubic spinel LiCo 2 O 4 , in parallel with formation of a more active catalytic phase. Comparison of cubic LiCoO 2 (50 nm) to iridium (5 nm) nanoparticles for OER catalysis (commercial benchmark for membrane-based systems) in basic and neutral electrolyte reveals excellent performance in terms of Tafel slope (48 mV dec −1 ), overpotential ( η = ∼420 mV@10 mA cm −2 at pH = 14), faradaic yield (100%) and OER stability (no loss in 14 hours). The inherent OER activity of cubic LiCoO 2 and spinel LiCo 2 O 4 is attributed to the presence of [Co 4 O 4 ] n+ cubane structural units, which provide lower oxidation potential to Co 4+ and lower inter-cubane hole mobility. By contrast, the layered phase, which lacks cubane units, exhibits extensive intra-planar hole delocalization which entropically hinders the four electron/hole concerted OER reaction. An essential distinguishing trait of a truly relevant catalyst is efficient continuous operation in a real electrolyzer stack. Initial trials of cubic LiCoO 2 in a solid electrolyte alkaline membrane electrolyzer indicate continuous operation for 1000 hours (without failure) at current densities up to 400 mA cm −2 and overpotential lower than proven PGM (platinum group metal) catalysts.more » « less
-
null (Ed.)Organic electrosynthesis is emerging as a cost-effective and environmental-friendly chemical production strategy by utilizing renewable electricity. Paired electrolysis cogenerates valuable chemicals at both electrodes can optimize the energy efficiency and economic feasibility. We report pairing hydrogenation and oxidation of 5-(hydroxymethyl)furfural (HMF) or furfural to desired chemicals at a single electrolysis cell. Electrocatalytic hydrogenation of HMF to 2,5-bis(hydroxymethyl)furan (BHMF) and furfural to furfural alcohol (FA) with high selectivity of >90% can be operated at near-neutral pH on Ag-based and Pb-based catalysts, respectively. In addition, oxidizing HMF to 2,5-furandicarboxylic acid (FDCA) and furfural to furoic acid can both be realized at TEMPO mediated process by using carbon-based catalysts or at Ni-based catalyst in an alkaline medium. Taken together, HMF or furfural can be performed in a single electrolysis cell with a minimized cell voltage only around 1.6 V. Products selectivity and faradaic efficiency are highly related to the reaction conditions, including potential or current density, architectures of the reactor, type of catalysts. By optimizing the single flow reactor, a three-electrode system, two-electrode membrane assembly architecture, and pH-symmetric and pH-asymmetric structure can be designed to reduce the capital expense, minimize required energy, and simplify processing steps. Finally, a complete electrons economy can be achieved by pairing two electrochemical reactions, and the overall charge efficiency can attain over 170% without any crossover issue detected. As a result, the continuous cogeneration of high value-added BHMF or FA and FDCA or furoic acid can be performed in a single electrolyzer.more » « less
-
Nanostructured molybdenum disulfide (MoS2) thin films were grown on a nanohole-patterned silicon substrate using plasma-enhanced atomic layer deposition. A nanoscale hole-patterned silicon substrate was fabricated for the growth of MoS2 film using the self-assembly-based nanofabrication method. The nanoscale holes can significantly increase the surface area of the substrate while the formation and growth of nanostructures normally start at the surface of the substrate. Hydrogen sulfide (H2S) gas was used as the S source in the growth of molybdenum disulfide (MoS2) while molybdenum (V) chloride (MoCl5) powder was used as the Mo source. The MoS2 film had a stoichiometric ratio of 1 (Mo) to 2 (S), and had peaks of E12g and A1g, which represent the in-plane and out-plane vibration modes of the Mo–S bond, respectively. It was found that the MoS2 film grown in the nanoscale hole, especially at the wall of the hole, has more hexagonal-like structures due to the effects of nanoscale space confinement and the nanoscale interface although the film shows an amorphous structure. Post-growth high-temperature annealing ranging from 800 to 900 °C produced local crystalline structures in the film, which are compatible with those reported by other researchers.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- The DOI is not currently available.