There is a strong drive behind the quest for thin-film materials that are oxygen-free and polar. Oxygen hinders the integration of ferroelectric oxides with semiconductors, which affects efforts to develop nonvolatile memory—that is, a memory that can sustain its information without power. Ideally, one would use single-crystalline perovskite films to construct these devices so that the polarization can be maximized. However, when depositing crystalline polar perovskite oxides onto silicon or germanium, a nonpolar oxide buffer layer ( 1 ) or a native oxide layer ( 2 ) can be present at the interface, compromising device performance. A nitrogen-based perovskite may overcome this limitation ( 3 ). On page 1488 of this issue, Talley et al. ( 4 ) report the synthesis of lanthanum tungsten nitride (LaWN 3 ) thin films, which marks the first demonstration of polar nitride perovskite. This may lead to oxygen-free integration of functional perovskite on a semiconductor platform.
more »
« less
Synthesis of Lanthanum Tungsten Oxynitride Perovskite Thin Films
Ternary metal‐oxide material systems commonly crystallize in the perovskite crystal structure, which is utilized in numerous electronic applications. In contrast to oxides, there are no known nitride perovskites, likely due to the competition with oxidation, which makes the formation of pure nitride materials difficult and synthesis of oxynitride materials more common. While deposition of oxynitride perovskite thin films is important for many electronic applications, it is difficult to control oxygen and nitrogen stoichiometry. Lanthanum tungsten oxynitride (LaWN3−
- Award ID(s):
- 1534503
- NSF-PAR ID:
- 10460246
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Electronic Materials
- Volume:
- 5
- Issue:
- 7
- ISSN:
- 2199-160X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The chemical structures of Co oxynitrides – in particular, interactions among N and O atoms bonded to the same cobalt – are of great importance for an array of catalytic and materials applications. X-ray diffraction (XRD), core and valence band X-ray photoelectron spectroscopy (XPS) and plane wave density functional theory (DFT) calculations are used to probe chemical and electronic interactions of nitrogen-rich CoO1-xNx (x > 0.7) films deposited on Si(100) using NH3 or N2 plasma-based sputter deposition or surface nitridation. Total energy calculations indicate that the zincblende (ZB) structure is energetically favored over the rocksalt (RS) structure for x > ~ 0.2, with an energy minimum observed in the ZB structure for x ~ 0.8 - 0.9. This is in close agreement with XPS-derived film compositions when corrected for surface oxide/hydroxide layers. XRD data indicate that films deposited on Si (100) at room temperature display either a preferred (220) orientation or no diffraction pattern, and are consistent with either rocksalt (RS) or zincblende (ZB) structure. Comparison between experimental and calculated X-ray excited valence band densities of states – also similar for all films synthesized herein – demonstrates a close agreement with a ZB, but not an RS structure. Core level XPS spectra exhibit systematic differences between films deposited in NH3 vs N2 plasma environments. Films deposited by N2 plasma magnetron sputtering exhibit greater O content as evidenced by systematic shifts in N 1s binding energies. Excellent agreement with experiment for core level binding energies is obtained for DFT calculations based on the ZB structure, but not for the RS structure. The agreement between theory and experiment demonstrates that these N-rich Co oxynitride films exhibit the ZB structure, and forms the basis of a predictive model for understanding how N and O interactions impact the electronic, magnetic and catalytic properties of these materials.more » « less
-
more » « less
Abstract Chalcogenide perovskites have emerged as promising semiconductor materials due to their appealing properties, including tunable bandgaps, high absorption coefficients, reasonable carrier lifetimes and mobilities, excellent chemical stability, and environmentally benign nature. However, beyond the well‐studied BaZrS3, reports on chalcogenide perovskite thin films with diverse compositions are scarce. In this study, the realization of four different types of chalcogenide perovskite thin films with controlled phases, through CS2annealing of amorphous chalcogenide precursor films deposited by pulsed laser deposition (PLD), is reported. This achievement is guided by a thorough theoretical investigation of the phase stability of chalcogenide perovskites. Upon crystallization in the distorted perovskite phase, all materials exhibit photoluminescence (PL) with peak positions in the visible range, consistent with their expected bandgap values. However, the full‐width‐at‐half‐maximum (FWHM) of the PL spectra varies significantly across these materials, ranging from 99 meV for SrHfS3to 231 meV for BaHfS3. The difference is attributed to the difference in kinetic barriers between local structural motifs for the Sr and Ba compounds. The findings underscore the promise of chalcogenide perovskite thin films as an alternative to traditional halide perovskites for optoelectronic applications, while highlighting the challenges in optimizing their synthesis and performance.
-
more » « less
Abstract While hexagonal boron nitride (hBN) has been widely used as a buffer or encapsulation layer for emerging electronic devices, interest in utilizing it for large‐area chemical barrier coating has somewhat faded. A chemical vapor deposition process is reported here for the conformal growth of hBN on large surfaces of various alloys and steels, regardless of their complex shapes. In contrast to the previously reported very limited protection by hBN against corrosion and oxidation, protection of steels against 10% HCl and oxidation resistance at 850 °C in air is demonstrated. Furthermore, an order of magnitude reduction in the friction coefficient of the hBN coated steels is shown. The growth mechanism is revealed in experiments on thin metal films, where the tunable growth of single‐crystal hBN with a selected number of layers is demonstrated. The key distinction of the process is the use of N2gas, which gets activated exclusively on the catalyst's surface and eliminates adverse gas‐phase reactions. This rate‐limiting step allowed independent control of activated nitrogen along with boron coming from a solid source (like elemental boron). Using abundant and benign precursors, this approach can be readily adopted for large‐scale hBN synthesis in applications where cost, production volume, and process safety are essential.
-
The production of ammonia for agricultural and energy demands has accelerated research for more environmentally-friendly synthesis options, particularly the electrocatalytic reduction of molecular nitrogen (nitrogen reduction reaction, NRR). Catalyst activity for NRR, and selectivity for NRR over the competitive hydrogen evolution reaction (HER), are critical issues for which fundamental knowledge remains scarce. Herein, we present results regarding the NRR activity and selectivity of sputter-deposited titanium nitride and titanium oxynitride films for NRR and HER. Electrochemical, fluorescence and UV absorption measurements show that titanium oxynitride exhibits NRR activity under acidic conditions (pH 1.6, 3.2) but is inactive at pH 7. Ti oxynitride is HER inactive at all these pH values. In contrast, TiN – with no oxygen content upon deposition – is both NRR and HER inactive at all the above pH values. This difference in oxynitride/nitride reactivity is observed despite the fact that both films exhibit very similar surface chemical compositions – predominantly Ti IV oxide – upon exposure to ambient, as determined by ex situ X-ray photoelectron spectroscopy (XPS). XPS, with in situ transfer between electrochemical and UHV environments, however, demonstrates that this Ti IV oxide top layer is unstable under acidic conditions, but stable at pH 7, explaining the inactivity of titanium oxynitride at this pH. The inactivity of TiN at acidic and neutral pH is explained by DFT-based calculations showing that N 2 adsorption at N-ligated Ti centers is energetically significantly less favorable than at O-ligated centers. These calculations also predict that N 2 will not bind to Ti IV centers due to a lack of π-backbonding. Ex situ XPS measurements and electrochemical probe measurements at pH 3.2 demonstrate that Ti oxynitride films undergo gradual dissolution under NRR conditions. The present results demonstrate that the long-term catalyst stability and maintenance of metal cations in intermediate oxidation states for pi-backbonding are critical issues worthy of further examination.more » « less