Modification of ethyleneechlorotrifluoroethylene (ECTFE) membranes by simple surface oxidation was reported in the present investigation in order to induce thin hydrophilic layer on hydrophobic membrane surface for the treatment of real produced water (PW). FTIR spectra indicates the appearance of hydrophilic functional groups (–OH and –COOH) on the membrane surface due to modification, while water contact angle, zeta potential measurement, EDX, XPS analysis confirmed the presence of O functionalized hydrophilic groups on the surface. The effect of modification temperature and the time of surface oxidation on the performance of the resulting membranes were studied systematically, which revealed that induction of optimized hydrophilicity can successfully reduce the organic fouling. However, too much hydrophilic surface induces polar/electrostatic interaction resulting salt deposition on membrane surface. A simple on site cleaning procedure was demonstrated to be successful for the treatment PW for at least three consecutive cycles of membrane distillation (MD).
more »
« less
Surface Modification of PVDF Membranes for Treating Produced Waters by Direct Contact Membrane Distillation
Direct contact membrane distillation (DCMD) has been conducted to treat hydraulic fracturing-produced water using polyvinylidenedifluoride (PVDF) membranes. Tailoring the surface properties of the membrane is critical in order to reduce the rate of adsorption of dissolved organic species as well as mineral salts. The PVDF membranes have been modified by grafting zwitterion and polyionic liquid-based polymer chains. In addition, surface oxidation of the PVDF membrane has been conducted using KMnO4 and NaOH. Surface modification conditions were chosen in order to minimize the decrease in contact angle. Thus, the membranes remain hydrophobic, essential for suppression of wetting. DCMD was conducted using the base PVDF membrane as well as modified membranes. In addition, DCMD was conducted on the base membrane using produced water (PW) that was pretreated by electrocoagulation to remove dissolved organic compounds. After DCMD all membranes were analyzed by scanning electron microscopy imaging as well as Energy-Dispersive X-Ray spectroscopy. Surface modification led to a greater volume of PW being treated by the membrane prior to drastic flux decline. The results indicate that tailoring the surface properties of the membrane enhances fouling resistance and could reduce pretreatment requirements.
more »
« less
- Award ID(s):
- 1822101
- PAR ID:
- 10105567
- Date Published:
- Journal Name:
- International Journal of Environmental Research and Public Health
- Volume:
- 16
- Issue:
- 5
- ISSN:
- 1660-4601
- Page Range / eLocation ID:
- 685
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Simultaneous fouling and pore wetting of the membrane during membrane distillation (MD) is a major concern. In this work, an electrospun bilayer membrane for enhancing fouling and wetting resistance has been developed for treating hydraulic fracture-produced water (PW) by MD. These PWs can contain over 200,000 ppm total dissolved solids, organic compounds and surfactants. The membrane consists of an omniphobic surface that faces the permeate stream and a hydrophilic surface that faces the feed stream. The omniphobic surface was decorated by growing nanoparticles, followed by silanization to lower the surface energy. An epoxied zwitterionic polymer was grafted onto the membrane surface that faces the feed stream to form a tight antifouling hydration layer. The membrane was challenged with an aqueous NaCl solution containing sodium dodecyl sulfate (SDS), an ampholyte and crude oil. In the presence of SDS and crude oil, the membrane was stable and displayed salt rejection (>99.9%). Further, the decrease was much less than the base polyvinylidene difluoride (PVDF) electrospun membrane. The membranes were also challenged with actual PW. Our results highlight the importance of tuning the properties of the membrane surface that faces the feed and permeate streams in order to maximize membrane stability, flux and salt rejection.more » « less
-
Direct contact membrane distillation (DCMD) for desalination is attractive for high salt concentrations if low cost steam/waste heat is available and waste brine disposal cost for inland desalination is factored in. A number of innovations have taken place in DCMD in terms of the structure of the porous hydrophobic membrane. Composite membranes are of increasing interest. Composite membrane structures of great interest include a thin hydrophobic porous layer over a porous hydrophilic layer of polyvinylidene fluoride (PVDF) or a thin porous hydrophobic layer over a more conventional hydrophobic porous membrane. These membranes can be in the form of an integral composite or a stacked composite or a laminated composite. A facile method of fabricating such integral composite membranes is plasma polymerization under vacuum. A class of such membranes yielding quite high water vapor fluxes have been characterized using a variety of characterization techniques: Contact angle, liquid entry pressure (LEP), bubble-point pressure, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), atomic force microscopy (AFM). Stacked composites of a hydrophobic ePTFE membrane over a hydrophilic PVDF membrane or a hydrophobic PVDF membrane over another hydrophobic PVDF membrane were also studied. Novel conditions created lead to very high water vapor fluxes compared to those from conventional hydrophobic membranes supported on a mesh support.more » « less
-
Increasing water demand coupled with projected climate change puts the Southwestern United States at the highest risk of water sustainability by 2050. Membrane distillation offers a unique opportunity to utilize the substantial, but largely untapped geothermal brackish groundwater for desalination to lessen the stress. Two types of hydrophobic, microporous hollow fiber membranes (HFMs), including polytetrafluoroethylene (PTFE) and polyvinylidene fluoride (PVDF), were evaluated for their effectiveness in direct contact membrane distillation (DCMD). Water flux and salt rejection were measured as a function of module packing density and length in lab-scale systems. The PVDF HFMs generally exhibited higher water flux than the PTFE HFMs possibly due to thinner membrane wall and higher porosity. As the packing density or module length increased, water flux declined. The water production rate per module, however, increased due to the larger membrane surface area. A pilot-scale DCMD system was deployed to the 2nd largest geothermally-heated greenhouse in the United States for field testing over a duration of about 22 days. The results demonstrated the robustness of the DCMD system in the face of environmental fluctuation at the facility.more » « less
-
In this study, hydrophilic silica nanoparticles (Si NPs) were used to modify α-alumina tubular membranes to improve their performance in terms of flux, oil rejection, and anti-fouling properties. Our work focuses on enhancing membrane performance, particularly for difficult applications such as produced water treatment. The prepared membranes were applied for oil-in-water emulsion treatment. After coating hydrophilic Si NPs, the oil contact angle improved from 133.8° to 171.4°. To prevent Si NPs from leaching off the surface of α-alumina tubular membranes, polyvinyl alcohol was used to coat the membranes as a pre-treatment step before Si NP modification. After coating the membrane with Si NPs, the roughness of the membrane surface decreased, likely leading to less fouling. After coating Si NPs, Total Organic Carbon rejection increased from 93.1% for pristine α-alumina tubular membranes to 97.7% for silica-modified membranes because of hydrophilic improvements of the modified membranes. The Si NP coating improved the anti-fouling property of membranes with the flux recovery ratio increasing from 71.3% for pristine α-alumina tubular membranes to 85.9% for silica-modified membranes. Scanning Electron Microscopy, Energy- dispersive X-ray spectroscopy, oil contact angle, and Atomic Force Microscopy characterization tests were done. The tests showed successful Si NPs impregnation and altered wettability.more » « less