Title: An Experimental Investigation of Combined Symmetric-Asymmetric Composite Laminates
It has been found that certain asymmetric composite laminates exhibit bistability, where the composite laminate exhibits multiple stable static equilibrium states. If the bistable composite is actuated, it will snap to its secondary equilibrium state and then remain there without further actuation. This study investigates how the amount of symmetry in a combined symmetric asymmetric rectangular laminate under an imposed clamped edge boundary condition affects the bistability and the curvature of the laminate. Laminates with varying amounts of asymmetry were fabricated and then measured using a profilometer to capture the curvatures of the equilibrium shapes. The results showed that up to 20% symmetry can be introduced in the laminate without a substantial loss in snap through curvature, and that up to 83% symmetry can be introduced in the laminate before bistability is lost. Finite element simulations were conducted in Abaqus and showed good correlation with the experimental results.  more » « less
Award ID(s):
1760943
NSF-PAR ID:
10111245
Author(s) / Creator(s):
;
Date Published:
Journal Name:
Journal of Composites Science
Volume:
3
Issue:
3
ISSN:
2504-477X
Page Range / eLocation ID:
71
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ( , Journal of Composite Materials)
    null (Ed.)
    Bistability is exhibited by an object when it can be resting in two stable equilibrium states. Certain composite laminates exhibit bistability by having two stable curvatures of opposite sign with the two axes of curvature perpendicular to each other. These laminates can be actuated from one state to the other. The actuation from the original post-cure shape to the second shape is called as ‘snap-through’ and the reverse actuation is called as ‘snap-back’. This phenomenon can be used in applications for morphing structures, energy harvesting, and other applications where there is a conflicting requirement of a structure that is load-carrying, light, and shape-adaptable. MW Hyer first reported this phenomenon in his paper in 1981. He found that thin unsymmetric laminates do not behave according to the predictions of the Classical Lamination Theory (CLT). The CLT is a linear theory and predicts the post-cure shape of thin unsymmetric laminates to be a saddle. MW Hyer developed a non-linear method called the “Extended Classical Lamination Theory” which accurately predicted the laminate to have two cylindrical shapes. Since then, a number of researchers have tried to identify the key parameters affecting the behavior of such laminates. Geometric parameters such as stacking sequence, fibre orientation, cure cycle, boundary conditions, and force of actuation, have all been studied. The objective of this research is to define a relation between the length, width and thickness of square and rectangular laminates required to achieve bistability. Using these relations, a 36 in × 36 in bistable laminate is fabricated with a thickness of 30 CFRP layers. Also, it is proved that a laminate does not lose bistability with an increase in aspect ratio, as long as both sides of the rectangular laminate are above a certain ‘critical length’. A bistable laminate with dimensions of 2 in × 50 in is fabricated. Further, for laminates that are bistable, it is necessary to be able to predict the curvature and force required for actuation. Therefore, a method is developed which allows us to predict the curvature of both stable shapes, as well as the force of actuation of laminates for which the thickness and dimensions are known. Finite Element Analysis is used to carry out the numerical calculations, which are validated by fabricating laminates. The curvature of these laminates is measured using a profilometer and the force of actuation is recorded using a universal test set-up. 
    more » « less
  2. ; ; ( , Journal of Composite Materials)

    Bistable composite laminates have large-scale applications in morphing and energy-harvesting structures, but their fatigue performance remains largely unexplored. This study investigates the stiffness and damage progression and evaluates bistable performance to develop protocols for long-term applications. We analyze the effects of displacement-controlled fully reversible high cycle fatigue-loading on stiffness, damage, curvature, and snap-through load in the out-of-plane loading direction at eight different combinations of parameters with frequency from 1 to 10 Hz, two boundary conditions, and temperature from 22°C to 150°C up to 3 to 10 million cycles. Stiffness and damage evolution analysis demonstrate the first two stages in out-of-plane fatigue loading. The study proposes a damage definition in terms of load adapting with two fatigue damage models: (1) Shiri Model and (2) Wu Model, while both models exhibit reasonable accuracy in predicting damage for the first two stages despite deviating at the final cycle due to assuming this cycle as the final failure cycle. Of the two models, the Shiri model provided a smaller range of model parameter values, 0.22 and 0.43, for parameters p and q, respectively, which reflects adjustability to different test conditions by maintaining a moderate range. Specimens encountered no final failure by fiber breakage and did not lose bistability for any combination. Curvature and snap-through load measurements have not substantially changed due to fatigue loading. These findings confirm application protocols with a broad range of parameters for which the laminates can operate without significant fatigue damage and maintain their bistable performance for an infinite lifetime.

     
    more » « less
  3. ; ; ; ( , Proceedings of the ASME 2021 International Design Engineering Technical Conferences and Computers and Information in Engineering Conference)
    Thin bistable composite laminates can be used for shape morphing applications by virtue of their material properties and asymmetric ply layup. These laminates are called bistable because they can be snapped into two or more stable shapes. A single bistable patch can result in simple cylindrical shapes and when multiple such patches are assembled into a single multi-patch laminate they result in more complex shapes and multiple stable shapes that can find wide practical use in shape morphing applications. Analytical models exist that can approximate the stable shapes of the laminates from the input of material properties and laminate geometry. And these models correlate with FEA and experiment to a satisfactory degree and could be used for the design of multi patch laminates. In this research, we make use of these analytical models that solve for a four-patch grid laminate and create a design method based on optimization to solve the reverse problem to arrive at the laminate parameters given the target shape(s). Two approaches are presented wherein one targets a single stable shape and the other targets two stable shapes which are the shapes before and after snap through. This work would be useful to understand how multi-patch laminates could be designed using optimization. 
    more » « less
  4. ; ; ( , Proceeding of ASME 2022 Conference on Smart Materials, Adaptive Structures and Intelligent Systems)
    Abstract

    Bistable composite laminates have exhibited enormous potential in morphing and energy harvesting followed by a wide range of application in aerospace, power generation and automobile industries. This study presents the fatigue analysis of bistable laminates in terms of stiffness degradation and loss of bistability. Moisture saturation of the specimens are ensured by keeping them in a controlled laboratory environment for an extended period of time. Mass of the specimens have been measured to quantify the moisture saturation. Fatigue tests are performed at 1 Hz frequency, and R = −1 stress ratio which is the ratio of minimum stress to maximum stress. Specimens are tested for 3 million cycles in displacement control. Load-displacement plot from the test is divided into 5 stiffness regions. A piecewise study of each region has demonstrated good agreement with existing analytical model. Stiffness degradation in 4 regions corresponding to 2 stable configurations follows general trend for composites up to the second stage of damage in three stage damage progression model while the remaining region corresponding to unstable configuration is not considered in this analysis. Test results have been reproduced with minor discrepancy at the specified environmental and loading condition, ply configuration, and size of the laminate. Test protocols, results, and damage analysis presented in this study can be utilized to evaluate the fatigue performance of multistable CFRP structures subjected to higher amplitudes and frequencies.

     
    more » « less
  5. ; ; ; ( , CAMX 2023 Technical Proceedings)
    The matrix sensitive weaknesses of Carbon Fiber Reinforced Polymer (CFRP) laminates are usually magnified by mainstream additive manufacturing (AM) methods due to the AM-process-induced voids and defects. In this paper, a novel Magnetic Compaction Force Assisted-Additive Manufacturing (MCFA-AM) method is used to print Carbon Nanofibers (CNF) Z-threaded CFRP (i.e., ZT-CFRP) composite laminates. The MCFA-AM method utilizes a magnetic force to simultaneously support, deposit, and compact Continuous Carbon Fiber Reinforced Polymer (C-CFRP) composites in free space and quickly solidifies the CFRP part without any mold; it effectively reduces the voids. Past research proved that the zig-zag threading pattern of the CNF z-threads reinforces the interlaminar and intralaminar regions in the ZT-CFRP laminates manufactured by the traditional Out of Autoclave-Vacuum Bag Only (OOA-VBO) method, and enhances the matrix sensitive mechanical, thermal, and electrical properties. In this study, the longitudinal compressive test (ASTM D695, i.e., SACMA SRM 1R-94) was performed on the MCFA-AM printed ZT-CFRP laminate. The results were compared with unaligned CNF-modified CFRP (UA-CFRP), control CFRP, and no-pressure CFRP samples’ data to investigate the impact of the CNF z-threads and MCFA-AM process on the CFRP’s performance. The 0.5-bar MCFA-AM printed ZT-CFRP showed comparable longitudinal compressive strength with the 1-bar OOA-VBO cured CFRP. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email