To produce efficient ORR catalysts with low Pt content, PtNi porous films (PFs) with sufficiently exposed Pt active sites were designed by an approach combining electrochemical bottom‐up (electrodeposition) and top‐down (anodization) processes. The dynamic oxygen‐bubble template (DOBT) programmably controlled by a square‐wave potential was used to tune the catalyst morphology and expose Pt active facets in PtNi PFs. Surface‐bounded species, such as hydroxyl (OH*, *=surface site) on the exposed PtNi PFs surfaces were adjusted by the applied anodic voltage, further affecting the dynamic oxygen (O2) bubbles adsorption on Pt. As a result, PtNi PF with enriched Pt(111) facets (denoted as Pt3.5 %Ni PF) was obtained, showing prominent ORR activity with an onset potential of 0.92 V (vs. RHE) at an ultra‐low Pt loading (0.015 mg cm−2).
To produce efficient ORR catalysts with low Pt content, PtNi porous films (PFs) with sufficiently exposed Pt active sites were designed by an approach combining electrochemical bottom‐up (electrodeposition) and top‐down (anodization) processes. The dynamic oxygen‐bubble template (DOBT) programmably controlled by a square‐wave potential was used to tune the catalyst morphology and expose Pt active facets in PtNi PFs. Surface‐bounded species, such as hydroxyl (OH*, *=surface site) on the exposed PtNi PFs surfaces were adjusted by the applied anodic voltage, further affecting the dynamic oxygen (O2) bubbles adsorption on Pt. As a result, PtNi PF with enriched Pt(111) facets (denoted as Pt3.5 %Ni PF) was obtained, showing prominent ORR activity with an onset potential of 0.92 V (vs. RHE) at an ultra‐low Pt loading (0.015 mg cm−2).
more » « less- Award ID(s):
- 1851674
- NSF-PAR ID:
- 10115274
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Angewandte Chemie International Edition
- Volume:
- 58
- Issue:
- 44
- ISSN:
- 1433-7851
- Page Range / eLocation ID:
- p. 15848-15854
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Bifunctional oxygen catalysts for oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) with high activities and low‐cost are of prime importance and challenging in the development of fuel cells and rechargeable metal–air batteries. This study reports a porous carbon nanomaterial loaded with cobalt nanoparticles (Co@NC‐
x /y ) derived from pyrolysis of a Co/Zn bimetallic zeolitic imidazolite framework, which exhibits incredibly high activity as bifunctional oxygen catalysts. For instance, the optimal catalyst of Co@NC‐3/1 has the interconnected framework structure between porous carbon and embedded carbon nanotubes, which shows the superb ORR activity with onset potential of ≈1.15 V and half‐wave potential of ≈0.93 V. Moreover, it presents high OER activity that can be further enhanced to over commercial RuO2by P‐doped with overpotentials of 1.57 V versus reversible hydrogen electrode at 10 mA cm−2and long‐term stability for 2000 circles and a Tafel slope of 85 mV dec−1. Significantly, the nanomaterial demonstrates better catalytic performance and durability than Pt/C for ORR and commercial RuO2and IrO2for OER. These findings suggest the importance of a synergistic effect of graphitic carbon, nanotubes, exposed Co–Nx active sites, and interconnected framework structure of various carbons for bifunctional oxygen electrocatalysts. -
more » « less
Abstract The development of dual catalysts with high efficiency toward oxygen reduction and evolution reactions (ORR and OER) in acidic media is a significant challenge. Here an active and durable dual catalyst based upon cubic Pt39Ir10Pd11nanocages with an average edge length of 12.3 nm, porous walls as thin as 1.0 nm, and well‐defined {100} facets is reported. The trimetallic nanocages perform better than all the reported dual catalysts in acidic media, with a low ORR‐OER overpotential gap of only 704 mV at a Pt‐Ir‐Pd loading of 16.8 µgPt+Ir+Pdcm−2geo. For ORR at 0.9 V, when benchmarked against the commercial Pt/C and Pt‐Pd nanocages, the trimetallic nanocages exhibit an enhanced mass activity of 0.52 A mg−1Pt+Ir+Pd(about four and two times as high as those of the Pt/C and Pt‐Pd nanocages) and much improved durability. For OER, the trimetallic nanocages show a remarkable mass activity of 0.20 A mg−1Pt+Irat 1.53 V, which is 16.7 and 4.3 fold relative to those of the Pt/C and Pt‐Pd nanocages, respectively. These improvements can be ascribed to the highly open structure of the nanocages, and the possible electronic coupling between Ir and Pt atoms in the lattice.
-
more » « less
Abstract Using molten‐salt synthetic techniques, NaNbO3(Space group
Pbcm ; No. 57) was prepared in high purity at a reaction time of 12 hours and a temperature of 900°C. All NaNbO3products were prepared from stoichiometric ratios of Nb2O5and Na2CO3together with the addition of a salt flux introduced at a 10:1 molar ratio of salt to NaNbO3, that is, using the Na2SO4, NaF, NaCl, and NaBr salts. A solid‐state synthesis was performed in the absence of a molten salt to serve as a control. The reaction products were all found to be phase pure through powder X‐ray diffraction, for example, with refined lattice constants ofa = 5.512(5) Å,b = 5.567(3) Å, andc = 15.516(8) Å from the Na2SO4salt reaction. The products were characterized using UV‐Vis diffuse reflectance spectroscopy to have a bandgap size of ~3.5 eV. The particles sizes were analyzed by scanning electron microscopy (SEM) and found to be dependent upon the flux type used, from ~<1 μm to >10 μm in length, with overall surface areas that could be varied from 0.66 m2/g (for NaF) to 1.55 m2/g (for NaBr). Cubic‐shaped particle morphologies were observed for the metal halide salts with the set of exposed (100)/(010)/(001) crystal facets, while a truncated octahedral morphology formed in the sodium sulfate salt reaction with predominantly the set of (110)/(101)/(011) crystal facets. The products were found to be photocatalytically active for hydrogen production under UV‐Vis irradiation, with the aid of a 1 wt% Pt surface cocatalyst. The platinized NaNbO3particles were suspended in an aqueous 20% methanol solution and irradiated by UV‐Vis light (λ > 230 nm). After 6 hours of irradiation, the average total hydrogen production varied with the particle morphologies and sizes, with 753 µmol for Na2SO4, 334 µmol for NaF, 290 µmol for NaCl, 81 µmol for NaBr, and 249 µmol for the solid‐state synthesized NaNbO3. These trends show a clear relationship to particle sizes, with smaller particles showing higher photocatalytic activity in the order of NaF > NaCl > NaBr. Furthermore, the particle morphologies obtained from the Na2SO4flux showed even higher photocatalytic activity, though having a relatively similar overall surface area, owing to the higher activity of the (110) crystal facets. The apparent quantum yield (100 mW/cm2,λ = 230 to 350 nm, pH = 7) was measured to be 3.7% for NaNbO3prepared using the NaF flux, but this was doubled to 6.8% when prepared using the Na2SO4flux. Thus, these results demonstrate the powerful utility of flux synthetic techniques to control particle sizes and to expose higher‐activity crystal facets to boost their photocatalytic activities for molecular hydrogen production. -
more » « less
Abstract Highly efficient and stable electrocatalysts, particularly those that are capable of multifunctionality in the same electrolyte, are in high demand for the hydrogen evolution reaction (HER), oxygen evolution reaction (OER), and oxygen reduction reaction (ORR). In this work, highly monodisperse CoP and Co2P nanocrystals (NCs) are synthesized using a robust solution‐phase method. The highly exposed (211) crystal plane and abundant surface phosphide atoms make the CoP NCs efficient catalysts toward ORR and HER, while metal‐rich Co2P NCs show higher OER performance owing to easier formation of plentiful Co2P@COOH heterojunctions. Density functional theory calculation results indicate that the desorption of OH* from cobalt sites is the rate‐limiting step for both CoP and Co2P in ORR and that the high content of phosphide can lower the reaction barrier. A water electrolyzer constructed with a CoP NC cathode and a Co2P NC anode can achieve a current density of 10 mA cm−2at 1.56 V, comparable even to the noble metal‐based Pt/C and RuO2/C pair. Furthermore, the CoP NCs are employed as an air cathode in a primary zinc–air battery, exhibiting a high power density of 62 mW cm−2and good stability.