skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Comparison of Charge Storage Properties of Prussian Blue Analogues Containing Cobalt and Copper
Prussian blue analogues are of great interest as alternative battery materials because of their long life cycle and potential use of earth-abundant elements. In this work, thin film mixed-metal hexacyanoferrates (HCFs) based on NiCo and NiCu alloys were fabricated in an all electrochemical process. The structure and composition of the samples were characterized, along with the charge storage capacity and kinetics of the charge transfer reaction. For both NiCo-HCF and NiCu-HCF samples, the total charge capacity increased with the substitution of Ni with more Co or Cu, and the increase was larger for Cu samples than for Co samples. On the other hand, the charge storage kinetics had only a modest change with substituted metal, and these effects were independent of the amount of that substitution. Thus, the mixed-metal HCFs have promise for increasing overall storage capacity without negatively influencing the rate capability when used in battery applications.  more » « less
Award ID(s):
1608327
PAR ID:
10128107
Author(s) / Creator(s):
;
Date Published:
Journal Name:
Metals
Volume:
9
Issue:
12
ISSN:
2075-4701
Page Range / eLocation ID:
1343
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; (, Discover Materials)
    null (Ed.)
    Abstract Prussian Blue Analogues are of major interest for their use in alternative battery technologies due to their charge storing ability with a long life cycle. In this work the Prussian Blue Analogue nickel hexacyanoferrate (Ni-HCF) was produced using an all electrochemical method. Creating charge storing materials with electrochemical processes provides a new approach to the development of battery-like materials. These methods have not been commonly employed because the charge storing material yield is not directly known. The charge storage of the Ni-HCF was characterized with two different methods which provided a measure of the electrochemically active Fe present. These were then compared with the Particle Induced X-ray Emission (PIXE) method which measured the total amount of Fe present. By comparing the electrochemical measurement of active Fe to the total Fe as measured by PIXE, the percentage of material that is active in the charge storage was determined. This enables an independent calculation of the specific charge capacity of the material for comparison to other battery technologies. 
    more » « less
  2. ; ; ; ; ; ; ; ; (, Zenodo)
    The development of alternative energy sources is crucial for reducing reliance on fossil fuels, particularly for mobile applications such as personal electronics and transportation. This necessitates the advancement of battery materials based on abundant and inexpensive constituent elements. To achieve this requires investigating materials in a broader compositional and structural design space. Early transition metal oxides, including the intercalation electrode α–V2O5, however, the performance of V2O5 is hindered by phase transformations during battery cycling that lead to capacity fade and short device lifetimes. This study investigates the modification of V2O5 through Mo substitution in a series of the form V2−xMoxO5 for x = 0.05, 0.1, 0.2, 0.4, 0.6, and 0.8. X-ray diffraction data reveal progressive structural changes with increasing Mo content, which in turn change the progression of phase transformations during the first discharge. The different product also results in different cycling profile shapes that indicate differences in the charge storage mechanism as a function of Mo content. As a result, samples with higher Mo-substitution, especially V1.2Mo0.8O5, have narrower hysteresis, higher capacity, and improved capacity retention. While there is a limited solubility of Mo in the V2O5structure, with secondary phases and defects at many compositions, we show that Mo substitution alters the cycling behavior of V2O5 to deep discharge, which can inform the design of intercalation materials for energy storage applications. 
    more » « less
  3. ; ; ; ; ; ; ; ; ; (, Journal of Materials Chemistry A)
    Hydrated vanadium pentoxide (VOH) can deliver a gravimetric capacity as high as 400 mA h g −1 owing to the variable valence states of the V cation from 5+ to 3+ in an aqueous zinc ion battery. The incorporation of divalent transition metal cations has been demonstrated to overcome the structural instability, sluggish kinetics, fast capacity degradation, and serious polarization. The current study reveals that the catalytic effects of transition metal cations are probably the key to the significantly improved electrochemical properties and battery performance because of the higher covalent character of 55% in the Cu–O bond in comparison with 32% in the Mg–O bond in the respective samples. Cu( ii ) pre-inserted VOH (CuVOH) possesses a significantly enhanced intercalation storage capacity, an increased discharge voltage, great transport properties, and reduced polarization, while both VOH and Mg( ii ) pre-inserted VOH (MgVOH) demonstrate similar electrochemical properties and performances, indicating that the incorporation of Mg cations has little or no impact. For example, CuVOH has a redox voltage gap of 0.02 V, much smaller than 0.25 V for VOH and 0.27 V for MgVOH. CuVOH shows an enhanced exchange current density of 0.23 A g −1 , compared to 0.20 A g −1 for VOH and 0.19 A g −1 for MgVOH. CuVOH delivers a zinc ion storage capacity of 379 mA h g −1 , higher than 349 mA h g −1 for MgVOH and 337 mA h g −1 for VOH at 0.5 A g −1 . CuVOH shows an energy efficiency of 72%, superior to 53% for VOH and 55% for MgVOH. All of the results suggest that pre-inserted Cu( ii ) cations played a critical role in catalyzing the zinc ion intercalation reaction, while the Mg( ii ) cations did not exert a detectable catalytic effect. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; (, Advanced Energy Materials)
    Abstract The growing demand for bioelectronics has generated widespread interest in implantable energy storage. These implantable bioelectronic devices, powered by a complementary battery/capacitor system, have faced difficulty in miniaturization without compromising their functionality. This paper reports on the development of a promising high‐rate cathode material for implantable power sources based on Li‐exchanged Na1.5VOPO4F0.5anchored on reduced graphene oxide (LNVOPF‐rGO). LNVOPF is unique in that it offers dual charge storage mechanisms, which enable it to exhibit mixed battery/capacitor electrochemical behavior. In this work, electrochemical Li‐ion exchange of the LNVOPF structure is characterized by operando X‐ray diffraction. Through designed nanostructuring, the charge storage kinetics of LNVOPF are improved, as reflected in the stored capacity of 107 mAh g−1at 20C. A practical full cell device composed of LNVOPF and T‐Nb2O5, which serves as a pseudocapacitive anode, is fabricated to demonstrate not only high energy/power density storage (100 Wh kg−1at 4000 W kg−1) but also reliable pulse capability and biocompatibility, a desirable combination for applications in biostimulating devices. This work underscores the potential of miniaturizing biomedical devices by replacing a conventional battery/capacitor couple with a single power source. 
    more » « less
  5. ; ; ; ; ; ; ; ; (, Angewandte Chemie International Edition)
    Abstract Dual‐ion batteries that use anions and cations as charge carriers represent a promising energy‐storage technology. However, an uncharted area is to explore transition metals as electrodes to host carbonate in conversion reactions. Here we report the reversible conversion reaction from copper to Cu2CO3(OH)2, where the copper electrode comprising K2CO3and KOH solid is self‐sufficient with anion‐charge carriers. This electrode dissociates and associates K+ions during battery charge and discharge. The copper active mass and the anion‐bearing cathode exhibit a reversible capacity of 664 mAh g−1and 299 mAh g−1, respectively, and relatively stable cycling in a saturated mixture electrolyte of K2CO3and KOH. The results open an avenue to use carbonate as a charge carrier for batteries to serve for the consumption and storage of CO2. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email