The inclusion-based boundary element method (iBEM) is developed to calculate the elastic fields of a bi-layered composite with inhomogeneities in one layer. The bi-material Green’s function has been applied to obtain the elastic field caused by the domain integral of the source fields on inclusions and the boundary integral of the applied loads on the surface. Using Eshelby’s equivalent inclusion method (EIM), the material mismatch between the particle and matrix phases is simulated with a continuously distributed source field, namely eigenstrain, on inhomogeneities so that the iBEM can calculate the local field. The stress singularity along the interface leads to the delamination of the bimaterials under a certain load. The crack’s energy release rate ( J) is obtained through the J-integral, which predicts the stability of the delamination. When the stiffness of one layer increases, the J-integral increases with a higher gradient, leading to lower stability. Particularly, the effect of the boundary and inhomogeneity on the J-integral is illustrated by changing the crack length and inhomogeneity configuration, which shows the crack is stable at the beginning stage and becomes unstable when the crack tip approaches the boundary; a stiffer inhomogeneity in the neighborhood of a crack tip decreasesJand improves the fracture resistance. For the stable cracking phase, the J-integral increases with the volume fraction of inhomogeneity are evaluated. The model is applied to a dual-glass solar module with air bubbles in the encapsulant layer. The stress distribution is evaluated with the iBEM, and the J-integral is evaluated to predict the delamination process with the energy release rate, which shows that the bubbles significantly increase the J-integral. The effect of the bubble size, location, and number on the J-integral is also investigated. The present method provides a powerful tool for the design and analysis of layered materials and structures.
more »
« less
Tuning crack-inclusion interaction with an applied T-stress
The interaction between cracks and inclusions plays an important role in the fracture behavior of particulate composites. It is commonly recognized that an inclusion stiffer than the matrix tends to deflect an approaching crack away while a softer inclusion attracts the crack. Here, we demonstrate by analytical modeling and numerical simulations that the crack-inclusion interaction can be tuned by an applied T-stress. Under a sufficiently large compressive applied T-stress, cracks can be attracted to stiffer inclusions while repelled by softer ones, thus reversing the conventional trend. Potential applications of this work include composite electrodes in lithium-ion batteries and hydraulic fracturing.
more »
« less
- Award ID(s):
- 1634492
- PAR ID:
- 10142493
- Date Published:
- Journal Name:
- International journal of fracture
- Volume:
- 222
- ISSN:
- 0376-9429
- Page Range / eLocation ID:
- 13-23
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Summary The dependence of rock behavior on the deformation rate is still not well understood. In salt rock, the fundamental mechanisms that drive the accumulation of irreversible deformation, the reduction of stiffness, and the development of hysteresis during cyclic loading are usually attributed to intracrystalline plasticity and diffusion. We hypothesize that at low pressure and low temperature, the rate‐dependent behavior of salt rock is governed by water‐assisted diffusion along grain boundaries. Accordingly, a chemo‐mechanical homogenization framework is proposed in which the representative elementary volume (REV) is viewed as a homogeneous polycrystalline matrix that contains sliding grain‐boundary cracks. The slip is related to the mass of salt ions that diffuse along the crack surface. The relationship between fluid inclusion‐scale and REV‐scale stresses and strains is established by using the Mori–Tanaka homogenization scheme. It is noted from the model that a lower strain rate and a larger number of sliding cracks enhance stiffness reduction and hysteresis. Thinner sliding cracks (i.e., thinner brine films) promote stiffness reduction and accelerate stress redistributions. The larger the volume fraction of the crack inclusions, the larger the REV deformation and the larger the hysteresis. Results presented in this study shed light on the mechanical behavior of salt rock that is pertinent to the design of geological storage facilities that undergo cyclic unloading, which could help optimize the energy production cycle with low carbon emissions.more » « less
-
In situ crack tip pH measurements for corrosion fatigue (CF) cracks in sensitized AA5456-H116 loaded under low loading frequencies show that cathodic polarization can arrest actively growing stress corrosion cracking (SCC) and CF cracks and produce a local alkaline crack tip pH. A method for measuring crack tip pH in situ was developed. For AA5456-H116 under a single level of high sensitization, CF experiments while loading in the Paris regime at a loading frequency of 0.1 Hz were conducted under freely corroding conditions and a cathodic polarization of −1.3 VSCE. Results show that under freely corroding conditions the crack actively grows, and the crack tip pH is slightly acidic, while at −1.3 VSCE an alkaline crack tip develops with a pH of 10 to 12. The findings of this study support the earlier published hypothesis that crack arrest of SCC and low loading frequency CF cracks is due to corrosion-induced blunting after the development of highly alkaline conditions that cause corrosion of the crack tip region blunting and halting the crack.more » « less
-
The Pure Shear (PS) crack specimen is widely employed to assess the fracture toughness of soft elastic materials. It serves as a valuable tool for investigating the behavior of crack growth in a steady-state manner following crack initiation. One of its advantages lies in the fact that the energy release rate (J) remains approximately constant for sufficiently long cracks, independent of crack length. Additionally, the PS specimen facilitates the easy evaluation of J for long cracks by means of a tension test conducted on an uncracked sample. However, the lack of a published expression for short cracks currently restricts the usefulness of this specimen. To overcome this limitation, we conducted a series of finite element (FE) simulations utilizing three different constitutive models, namely the neo-Hookean (NH), Arruda-Boyce (AB), and Mooney-Rivlin (MR) models. Our finite element analysis (FEA) encompassed practical crack lengths and strain levels. The results revealed that under a fixed applied displacement, the energy release rate (J) monotonically increases with the crack length for short cracks, reaches a steady-state value when the crack length exceeds the height of the specimen, and subsequently decreases as the crack approaches the end of the specimen. Drawing from these findings, we propose a simple closed-form expression for J that can be applied to most hyper-elastic models and is suitable for all practical crack lengths, particularly short cracks.more » « less
-
null (Ed.)Understanding the failure mechanisms of piezoelectric thin films is critical for the commercialization of piezoelectric microelectromechanical systems. This paper describes the failure of 0.6 mu m lead zirconate titanate (PZT) thin films on Si wafers with different in-plane stresses under large electric fields. The films failed by a combination of cracking and thermal breakdown events. It was found that the crack initiation and propagation behavior varied with the stress state of the films. The total stress required for crack initiation was estimated to be near 500 MPa. As expected, cracks propagated perpendicular to the maximum tensile stress direction. Thermal breakdown events and cracks were correlated, suggesting coupling between electrical and mechanical failure. It was also found that films that were released from the underlying substrates were less susceptible to failure by cracking. It was proposed that during electric field loading the released film stacks were able to bow and alleviate some of the stress. Released films may also experience enhanced domain wall motion that increases their fracture toughness. The results indicate that both applied stress and clamping conditions play important roles in the electromechancial failure of piezoelectric thin films.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1007/s10704-020-00423-9